Properties and Structure of Laser Beam Welded Joints of S700MC Thermomechanically Treated Steel

• Autorzy: Górka J , Stano S.

Warianty tytułu

PL

Własności i struktura złączy spawanych wiązką laserową stali obrabianej termomechanicznie S700MC

• Konferencja: 56. Konferencja Spawalnicza "Spawalnictwo - zawsze można więcej", Sosnowiec, 14-15.10.2014
• Języki publikacji: EN

Abstrakty

EN

The article presents the structure and properties of joints welded using a laser beam without a filler metal, made of 10 mm thick thermomechanically treated high yield point S700MC steel. The related non-destructive tests have classified the joints described above as representing the quality level B in accordance with standard 13919-1. The destructive tests have revealed the joint characterised by the tensile strength approximately 5% higher than that of the parent metal. Laser welding without the filler metal increases the content of chemical elements responsible for steel hardening (Ti, Nb), which leads to a weld toughness decrease below the acceptable value of 27 J/cm2.

PL

W artykule przedstawiono strukturę i własności złączy spawanych wiązką laserową bez materiału dodatkowego stali obrabianej termomechanicznie o wysokiej granicy plastyczności S700MC o grubości 10 mm. Przeprowadzone badania nieniszczące pozwoliły sklasyfikować złącza w poziomie jakości B zgodnie z norma ISO 13919-1. Badania niszczące wykazały, że złącze charakteryzuje się wytrzymałością na rozciąganie około 5% niższą niż wytrzymałość materiału rodzimego. Proces spawania laserowego bez dodatku spoiwa, powoduje w spoinie wzrost zawartości pierwiastków odpowiadających za umocnienie stali (Ti, Nb), co przyczynia się do obniżenia udarności spoiny. Udarność w spoinie spada poniżej dopuszczalnej wartości 27 J/cm2.

Słowa kluczowe

EN

laser beam welding; S700MC steel; welding joints; destructive tests

PL

spawanie laserowe; stal S700MC; połączenie spawane; badania niszczące

• Wydawca: Sieć Badawcza Łukasiewicz - Górnośląski Instytut Technologiczny
• Czasopismo: Biuletyn Instytutu Spawalnictwa w Gliwicach
• Rocznik: 2014
• Tom: Vol. 58, No. 5
• Strony: 35--40
• Opis fizyczny: Bibliogr. 15 poz., rys., tabl.

Twórcy

autor

Górka J

• Silesian University of Technology, Gliwice, Welding Department; dr inż.

autor

Stano S.

• Instytut Spawalnictwa in Gliwice, Welding Technologies Department

Bibliografia

• 1. Banasik M., Dworak J, Pilarczyk J., Stano S.: Various laser welding techniques – test results and possible applications. Welding International, 2010, nr. 11
• 2. Grajcar A., Różański M., Stano S., Kowalski A., Grzegorczyk B.: Effect of Heat Input on Microstructure and Hardness Distribution of Laser Welded Si-Al TRIP-Type Steel. Advances in Materials Science and Engineering, 2014, Article ID: 658947
• 3. Banasik M., Stano S.: Lasery dyskowe – nowoczesne, uniwersalne źródło ciepła dla procesów spawalniczych, Przegląd Spawalnictwa, 2011, nr 7
• 4. Thomy C., Seefeld T., Vollertsen F.: Laser and laser-GMA welding applications using High Power Fiber Laser, 1st international Fraunhofer workshop on fiber lasers. Fraunhofer IWS, Dresden, 22 November 2005
• 5. Brockmann R., Mann K.: Disk Lasers Enable Industrial Manufacturing - What Was Achieved and What Are the Limits? Laser Technik Journal, 2007, nr 3, s.50-53
• 6. Adamczyk J., Grajcar A.: Structure and mechanical properties of DP-type and TRIP-type sheets obtained after the thermomechanical processing. Journal of Materials Processing Technology, 2005, s. 23-27
• 7. Nishioka K., Ichikawa K.: Progress in termomechanical control of steel plates and their commercialization. Science and Technology of Advanced Materials, 2012, nr 2, s. 1-20
• 8. Ehrhardt B., Gerber T.: Property related design of advanced cold rolled steels with induced plasticity. Steel Grips, 2004, nr 4, s. 247-255
• 9. Dimatteo A., Lovicu G., Desanctis M., Valentini R., Solina A.: Correlations between microstructures and properties of transformation induced plasticity steels. Steel Grips, 2006, s. 143-147
• 10. Chen B., Yu H.: Hot ductility behaviour of V-N and V-Nb microalloyed steels. International Journal of Minerals, Metallurgy and Materials, 2012, nr 6, s. 525
• 11. Misra R.D.K.: Influence of vanadium on grain boundary segregation of phosphorus in iron and iron-carbon alloys. Bulletin Material Science, 1991, nr 6, s. 1309-1322
• 12. Portera, D., Laukkanenb A., Nevasmaab P., Rahkab K., Wallin K.: Performance of TMCP steel with respect to mechanical properties after cold forming and post-forming heat treatment. International Journal of Pressure Vessels and Piping, 2004, s. 867-877
• 13. Adamczyk J., Opiela M.: Influence of the thermo-mechanical treatment parameters on the inhomogeneity of the austenite structure and mechanical properties of the Cr-Mo steel with Nb, Ti and B microadditions. Journal of Materials Processing Technology, 2004, s. 456-461
• 14. Brózda J.: Nowoczesne stale konstrukcyjne i ich spawalność. Wydawnictwo Instytutu Spawalnictwa, Gliwice 2009
• 15. Górka J.: Własności i struktura złączy spawanych stali obrabianej termomechanicznie o wysokiej granicy plastyczności. Wydawnictwo Politechniki Śląskiej, Gliwice 2013

Uwagi

EN

The research work has been partly financed from the research grant: Controlling the Properties and Structure of Thermomechanically Treated High Yield Point Steels, no. N N507 321040, Silesian University of Technology in Gliwice

PL

Wersja polska artykułu w wydaniu papierowym s. 39--43