Effect of 2% at. of alloying elements: Si, V, Nb, Mo, Ti, Zr or Cu on the corrosion behavior of sintered Nd-Fe-B under conditions of prolonged atmospheric exposure

• Autorzy: Bala H. , Szymura S. , Dymek M. , Rabinovich Y. M. , Kucharska B.

Warianty tytułu

PL

Wpływ 2% at. dodatków stopowych: Si, V, Nb, Mo, Ti, Zr lub Cu na korozyjne zachowanie spieków Nd-Fe-B w warunkach długotrwałej ekspozycji atmosferycznej

• Konferencja: Ogólnopolska Konferencja Naukowo-Techniczna "Antykorozja : Systemy - Materiały - Powłoki" (22 ; 09-11.04.2014 ; Ustroń-Jaszowiec, Polska)
• Języki publikacji: EN

Abstrakty

EN

The Nd-Fe-B type sinters were exposed to long-term (10 years) atmospheric corrosion which brought about their partial pulverization. The destruction process is markedly inhibited by partial (2 at.%) substitution of Si for Fe but it is strongly accelerated by Ti, Zr or Cu substitutions. A galvanic nature of the sinter damage is postulated. Due to contact with humidity the sinters absorb reversibly hydrogen and there is evident correlation between hydrogen uptake ability and pulverization susceptibility of the Nd-Fe-B based sinters.

PL

Długotrwała (10-letnia) ekspozycja atmosferyczna spiekanych materiałów na bazie Nd-Fe-B prowadzi do częściowej pulweryzacji spieków. Podstawienie żelaza niewielką (2% at.) ilością Si wyraźnie hamuje zaś podstawienie za pomocą Ti, Zr lub Cu – znacznie przyśpiesza degradację. Powstałe zniszczenia korozyjne sugerują ich galwaniczny charakter. W wyniku oddziaływania z wilgocią spieki na bazie Nd-Fe-B odwracalnie pochłaniają wodór, przy czym widoczna jest korelacja pomiędzy zdolnością do absorpcji wodoru a podatnością spieków na pulweryzację.

Słowa kluczowe

EN

Nd-Fe-B sinters; alloying additions; atmospheric degradation; hydrogen uptake

PL

spieki Nd-Fe-B; dodatki stopowe; degradacja atmosferyczna; pochłanianie wodoru

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Ochrona przed Korozją
• Rocznik: 2014
• Tom: nr 4
• Strony: 111--115
• Opis fizyczny: Bibliogr. 19 poz., rys., tab., wykr.

Twórcy

autor

Bala H.

• Division of Chemistry, Czestochowa Univ. of Technology, Czestochowa

autor

Szymura S.

• PWSZ State Highschool, Nysa

autor

Dymek M.

• Division of Chemistry, Czestochowa Univ. of Technology, Czestochowa

autor

Rabinovich Y. M.

• Applied Magnet Technology Company, Portage, USA

autor

Kucharska B.

• Inst. of Materials Engineering, Czestochowa Univ. of Technology, Czestochowa

Bibliografia

• 1. M. Pourbaix, Atlas of electrochemical equilibria in aqueous solutions. 2d English ed. 1974, Houston, Texas.: NACE
• 2. H. Bala, S. Szymura, J.J. Wysłocki; Electrochemical corrosion resistance of NdFeB permanent magnets, J. Mater. Sci., 25 (1990) 571-574
• 3. H. Bala, G. Pawłowska, S. Szymura, V.V. Sergeev, Yu.M. Rabinovich; Corrosion characteristics of Nd-Fe-B sintered magnets containing various alloying elements, J. Magn. Magn. Mater., 87 (1990) L255-L259
• 4. S. Szymura, H. Bala, M. Malik, Yu.M. Rabinovich, V.V. Sergeev, D.V. Pokrovskii; Microstructure, magnetic properties and corrosion behavior of sintered (Nd,Dy)-(Fe,Co)-B magnets with minor Re, W and Zr additions; Mater. Chem. and Physics, 30 (1991) 93
• 5. H. Bala, J. Gęga, S. Szymura, V.V. Sergeev, V.V. Vetrov; Badanie odporności korozyjnej powłok ochronnych wytworzonych na materiałach magnetycznych typu Nd-Fe-B, Powłoki Ochronne, 121-122 (1993) 32
• 6. H. Bala, N.M. Trepak, S. Szymura, A.A. Lukin, V.A. Gaudyn, L.A. Isaicheva, G. Pawlowska, L.A. Ilina, Corrosion protection of Nd-Fe-B type permanent magnets by zinc phosphate surface conversion coatings, Intermetallics, 9/6 (2001) 515-519
• 7. A.A. Lukin, S. Szymura, Yu.M. Rabinovich, H. Bala, A.A. Zhuravlyev, Hydrogen embrittlement of (Sm,Dy,Gd)Co5 permanent magnets, Eng. Failure Analysis, 5 (1998) 317-321
• 8. S. Szymura, Yu.M. Rabinovich, H. Bala, T.K. Sergeyeva, A.A. Lukin; Peculiarities in electrochemical hydrogenation of Nd-Fe-B type permanent magnets, Metallic Materials, 39 (No. 1), (2001) 55-64
• 9. H. Bala, S. Szymura; Electrochemical investigation of dissolution of Nd-Fe-B magnets under cathodic polarization, Corros. Sci., 32 (1991) 953-963
• 10. B. Staliński, J. Terpiłowski, Wodór i wodorki, WNT, Warszawa 1989, s.75
• 11. H. Bala, G. Pawłowska, S. Szymura, Yu.M. Rabinovich; The electrochemical corrosion characterization of the intermetallic phases occurring in Nd-Fe-B type magnets, British Corros. J., 33 (1998) 37-41
• 12. E. Claude, S. Ram, I. Gimenez, P. Chaudouet, D. Boursier, J.C. Joubert, Evidence of quantitative relationship between the degree of hydrogen intercalation and the coercivity of the two permanent magnet alloys Nd2Fe14B and Nd2Fe11Co3B, Trans.Magn., 29 (1993) 2767-2769
• 13. C.N. Christodoulou, T. Takeshita, Sm2Fe17-nitrite based permanent magnets produced by the HDDR process, J. Alloys Comp., 196 (1993) 155-159
• 14. A. Kim, F. Camp, T. Lizzi, Hydrogen induced corrosion mechanism in NdFeB magnets, J. Appl. Phys., 79 (1996) 4840-4845
• 15. I. Kukuła, H. Bala, Ocena stopnia degradacji korozyjnej ujemnej elektrody ogniwa NiMH w oparciu o galwanostatyczne krzywe ładowania/ rozładowania. Ochr. przed Korozją, 54 (2011) 494-496
• 16. M. Dymek, H. Bala, Progress in evaluation of metal hydride electrode charge time and time of oxide phases reduction. Ochr. przed Korozją, 56 (2013) 115-118
• 17. H. Bala, M. Dymek, L. Adamczyk, K. Giza, H. Drulis, Hydrogen diffusivity, kinetics of H2O/H2 charge transfer and corrosion properties of LaNi5 powder, composite electrodes in 6M KOH solution, J. Solid State Electrochem. DOI: 10.1007/s10008-013-2322-x (on line, 19 Nov. 2013)
• 18. H. Bala, K. Giza, I. Kukula, Determination of hydrogenation ability and exchange current of H2O/H2 system on hydrogen absorbing metal alloys, J. Appl. Electrochem., 40 (2010) 791-797
• 19. H. Bala, M. Dymek, H. Drulis, Development of metal hydride material effi cient surface in conditions of galvanostatic charge/discharge cycling, in preparation