Analysis of the Possibility to Assess the Occurrence of Hidden Corrosion in Lap Joints Using Active Thermography

• Autorzy: Kornas Ł. , Dragan K.

Identyfikatory

DOI

10.2478/v10164-010-0037-3

• Języki publikacji: EN

Abstrakty

EN

The article details the NDT technique of pulse thermography used for objective diagnosis of riveted lap joints construction. The degradation of materials manifesting in corrosion is inherent in the process of aircraft operation. One type of corrosion is galvanic corrosion occurring in the overlap joints (known as hidden corrosion). As a result of the potential difference between the two layers of the aluminum alloy skin, there occurs the phenomenon of oxidation of the material, producing corrosion products in the form of oxide compounds characterized by heat properties different than those of the base material. Active thermography techniques allow observing infrared energy, which changes due to the difference of thermal properties of the tested materials.

• Wydawca: Wydawnictwa Naukowe Sieci Badawczej Łukasiewicz - Instytutu Lotnictwa
• Czasopismo: Fatigue of Aircraft Structures
• Rocznik: 2011
• Tom: Iss. 3
• Strony: 53--56
• Opis fizyczny: Bibliogr. 7 poz., rys., tab., wykr.

Twórcy

autor

Kornas Ł.

• Air Force Institute of Technology, Warsaw, Poland

autor

Dragan K.

• Air Force Institute of Technology, Warsaw, Poland

Bibliografia

• [1] Dragan, K. & Klimaszewski, S. (2003). Rozpoznanie i klasyfikacja korozji ukrytej w konstrukcji statków powietrznych za pomocą systemu DAIS. 32 Krajowa Konferencja Badań Niszczących, 27-30.10.2003 Międzyzdroje.
• [2] Oliferuk, W. (2008). Termografia podczerwieni w nieniszczących badaniach materiałów i urządzeń. Warszawa: Biuro Gamma.
• [3] Świderski, W. (2010). Metody termograficzne w nieniszczących badaniach materiałów kompozytowych do zastosowania specjalnych. Wojskowy Instytut Techniczny Uzbrojenia, Zielonka.
• [4] Matzkanin, G.A. & Yolken, H.T. (2007). Nondestructive Evaluation Techniques for Detecting Hidden Corrosion, The AMMTIAC Quarterly. 2(2), 3-6.
• [5] Vavilov, V.R. (2003). Non-contact one-sided evaluation of hidden corrosion in metallic constructions by using transient infrared thermography. Revista de Metalurgia. (2003), 235-242.
• [6] Perez, I. & Kulowitch, P. Thermography for characteriziation of corrosion damage. Naval Air Warfare Center, Aircraft Division Patuxent River MD 20670.
• [7] Shepard, S.M. (2001). Thermographic Detection of Front and Back Surface Corrosion. Thermal Wave Imaging, Inc. Ferndale, MI 48220.