Case studies of steel and their welded joint failures caused by liquid metal embrittlement LME

• Autorzy: Bernasovský P. , Brziak P.

Warianty tytułu

PL

Analiza przypadków pęknięć stalowych złączy spawanych wywołanych obecnością cieczy metalicznej

• Języki publikacji: EN

Abstrakty

EN

Liquid metal embrittlement (LME) is a phenomenon, where liquid (molten) metal is mostly intergranulary (but not only) penetrated into solid metal and causes its brit- tle fracture. The LME is usually related to low melting metals (zink, tin, cadmium), which are in the contact with higher molten ones (steels, Ni alloys). Cases of LME as a Cu penetration into pipeline welded joint of 15G2S steel, a hot temperature corrosion in the cement works shell plate made of AISI 310 stainless steel attacted by Ni3S2 (Ts = 644 °C) and a vanadium corrosion in the boiler vessel (10CrMo9-10 steel) due to V2O5 + Na2SO4 eutecticum (~600 °C) are concerned.

PL

Kruchość stali wywołana obecnością cieczy metalicznej (ang. LME – liquid metal embrittlement) zachodzi podczas oddziaływania i w konsekwencji penetrowania granic ziaren (stali oraz stopów Ni) niskotopliwych metalami (cu, Zn, Col Sn), w warunkach działania naprężeń rozciągających. W artykule przeanalizowano przypadki LME wynikające z penetrowania Cu złączy spawanych rurociągów ze stali 15G29 oraz wysokotemperaturowej erozji płyt ze stali 310 wg ALSI wywołanej działaniem Ni3S2 (Ts-644 °C) oraz erozji kotła ze stali 10CrMo9-10 wywołanym oddziaływaniem w wysokiej temperaturze V2O5 + Na2SO4.

Słowa kluczowe

EN

hot crack; embrittlement; liquid metal

PL

pęknięcie gorące; kruchość; ciecz metaliczna

• Wydawca: Stowarzyszenie Inżynierów i Techników Mechaników Polskich
• Czasopismo: Przegląd Spawalnictwa
• Rocznik: 2015
• Tom: R. 87, nr 2
• Strony: 37--40
• Opis fizyczny: Bibliogr. 8 poz., il., tab.

Twórcy

autor

Bernasovský P.

• Welding Research Institute - Industrial Institute of Slovak Republik, Bratislava, Slovakia

autor

Brziak P.

• Welding Research Institute - Industrial Institute of Slovak Republik, Bratislava, Slovakia

Bibliografia

• [1] D.G. Kolman.: Environmentally Induced Cracking, Liquid Metal Embrittlement, ASM Handbook, Volume 13A, Corrosion: Fundamentals, testing and Protection, ASM International, Materials Park, OH pp. 381-392 (2003).
• [2] Liquid metal embrittlement, Metallurgical minutes, MAI, Summer 2004.
• [3] TWI Technical knowledge, Great Abington, UK, 2000.
• [4] D.G. Kolman.: Environmentally Induced Cracking, Solid Metal Embrittlement, ASM. Handbook, Volume 13A, Corrosion: Fundamentals, testing and Protection, ASM International, Materials Park, OH pp. 393 - 397 (2003).
• [5] Bernasovský,P. Brziak,P.: Case study of 15G2S grade gas pipeline. Technical. report, VÚZ-PI SR, ME 103, Bratislava, June 2003.
• [6] Bernasovský, P.- Brziak, P.: Analysis of AISI 310 steel plate. Technical report, VÚZ-PI. SR, ME 148, Bratislava, 31.5.2007.
• [7] Mráz, Ľ. et al.: Analysis of 33,7x5 mm pipe made of 10VrMo 9-10 steel in boiler K3. Technical report , VÚZ - PI SR, ME 068, Bratislava, 13.4.2012.
• [8] Andijani, J.-Malik, A.U.: Sulfur and vanadium induced hot corrosion of boiler tubes. Chemistry & Industry Conference, Riyadh, Dec. 11-15, 2004.