Dynamic Mechanical Analysis of Nylon 66 Cord Yarns

• Autorzy: Demšar A. , Bukošek V. , Kljun A.

Warianty tytułu

PL

Dynamiczna analiza parametrów mechanicznych przędz wykonanych z poliamidu 66

• Języki publikacji: EN

Abstrakty

EN

The viscoelastic properties of three different nylon cord yarns were analysed, and the dependence on the temperature of the annealing process was examined with the use of dynamic mechanical analysis (DMA). The research showed that the initial moduli of temperature-treated nylon cord yarns in a clamped state decrease after temperature treatment. The results also demonstrated that it is recommended to perform the vulcanisation of rubber composites at temperatures between 160 °C and 180 °C, where segmental motion is at minima. Likewise, it is not recommended to mechanically load cord yarns between 90 °C to 130 °C. This study demonstrated that DMA can be used to analyse the viscoelastic properties of cord yarns, which enables us to detect subtle differences between different materials and to interpret changes in the material at a supermolecular level. DMA can aid in determining optimal process conditions and materials.

PL

Przeprowadzono analizę właściwości lepko-sprężystych trzech różnych rodzajów przędz nylonowych oraz zbadano zależności temperaturowe procesu wygrzewania stosując dynamiczną analizę parametrów mechanicznych. Na podstawie uzyskanych Wyników można zasugerować, że proces wulkanizacji kompozytów kauczukowych należy przeprowadzać w temperaturze 160 °C – 180 °C. Jednocześnie nie powinno się obciążać kordów poliamidowych w temperaturach 90 °C – 130 °C. Badania wykazały, że metoda ta może być stosowana do analizy lepko-sprężystych właściwości przędz kordowych i pozwala na wykrywanie nieznacznych różnic pomiędzy materiałami.

Słowa kluczowe

EN

nylon; cord yarns; dynamic mechanical analysis; viscoelastic properties

PL

nylon; przędze sznurowe; dynamiczna analiza mechaniczna; właściwości lepkosprężyste

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2010
• Tom: Vol. 18, no. 4 (81)
• Strony: 29--34
• Opis fizyczny: Bibliogr. 22 poz., tab., rys.

Twórcy

autor

Demšar A.

• University of Ljubljana, Faculty of Natural Sciences and Engineering, Department of Textiles, Snezniska 5, 1000 Ljubljana, Slovenia

autor

Bukošek V.

• University of Ljubljana, Faculty of Natural Sciences and Engineering, Department of Textiles, Snezniska 5, 1000 Ljubljana, Slovenia

autor

Kljun A.

• University of Ljubljana, Faculty of Natural Sciences and Engineering, Department of Textiles, Snezniska 5, 1000 Ljubljana, Slovenia

Bibliografia

• 1. Wootton D. B.; The application of textiles in rubber. Shawbury, Shrewsbury, Shropshire [Great Britain]: Rapra Technology, 2001.
• 2. Prevoršek D. C.; Visokozmogljiva vlakna iz gibkih polimerov :teorija in tehnologija. Naravoslovnotehniška fakulteta, Oddelek za tekstilstvo, Ljubljana, 1998 (in Slovenian).
• 3. Lewin M., Pearce E. M.; Handbook of Fiber Science and Technology; Volume IV.: Fiber Chemistry, Marcel Dekker, Inc., New York and Basel, 1985.
• 4. Starkweather H. W., Jones G. A. J.; Polym. Sci. Polym. Phis. Ed., 19, 1981, pp. 467-477.
• 5. Prevoršek D. C., Oswald H. J.; Melt Spinning of PET and Nylon Fibers. In the book Solid State Behaviour of linear Polyesters and Polyamides, Prentice Hall, New Jersey (1990), pp. 131-208.
• 6. Dreyfuss P., Keller A. J.; Macromol. Sci.-Phys.: B4, 4, 1970, 811-836.
• 7. Dreyfuss P., Keller A., Willmouth F. M.; J. Polym. Sci.: A2, 10, 1972, pp. 857-861.
• 8. Atkins E. D. T., Keller A., Sadler D. M.; J. Polym. Sci.: A2, 10, 1972, pp. 863-875.
• 9. Dreyfuss P., Keller A. J.; Polym. Sci. Polym. Phis. Ed., 11, 1973, pp. 193-200.
• 10. Dreyfuss P.; J. Polym. Sci. Polym. Phis. Ed., 11, 1973, pp. 201-216.
• 11. Colclough M. L., Baker R. J.; Materials Sci., 13, 1978, pp. 2351-2540.
• 12. Magill J. H., Girolamao M., Keller A.; Polymer, 22, 1981, pp. 43-55.
• 13. Bukošek, V. Ph.D. thesis; Ljubljana, 1997 (in Slovenian).
• 14. Bukošek V., Prevoršek D. C.; Int J Polym Mater, 47 (4), 2000, pp. 569-592.
• 15. Murthy N. S.; et al. Polymer, 36 (20), 1995, pp. 3863-3873.
• 16. Peterlin A.; Textile Research Journal, 42 (1), 1972, pp. 20-30.
• 17. Peterlin A. J.; Journal of Applied Physics, 48 (10), 1977, pp. 4099-4107.
• 18. Prevoršek D. C., et al.; Ruber Chem Tech, 60, 1987, p. 59.
• 19. Kevin P. Menard; Dynamic Mechanical Analysis: A Practical Introduction, Second Edition; CRC Press: Boca Raton, 2008.
• 20. http://www.tainstruments.com/product.aspx?id=12&n=1&siteid=11.
• 21. Gupta V. B., In Textile Fibers: developments and innovations, Volume 2, Kothari, V.K., Ed.; IAFL Publications: New Delhi, 2000, pp. 11-118.
• 22. Elyashevich G. K., Baranov V. G., Frenkel S. Y.; J Macromol Sci – Physics, B13 (2), 1977, pp. 255-289.