DSC Analysis of Order–Disorder Transition in Ni3Al Based Alloys From Ni-Al-Cr System

• Autorzy: Maciąg T. , Rzyman K. , Przeliorz R.

Identyfikatory

DOI

10.1515/amm-2015-0319

Warianty tytułu

PL

Analiza DSC przemian typu porządek-nieporządek w stopach na osnowie Ni3Al z układu Ni-Al-Cr

• Języki publikacji: EN

Abstrakty

EN

Ni-Al-Cr system is significant for industrial alloys based on intermetallic phase Ni3Al, that crystallizes in crystal lattice L12. It is indicated as γ′, contrary to disordered phase γ which occurs with addition of chromium. DSC analysis was performed on alloys of chemical composition from Ni75Al25÷Ni75Cr25 range of Ni-rich part of Ni-Al-Cr system. In addition, few measurements were conducted using DTA method. Based on curves registered, it was possible to identify characteristic temperature during heating and cooling of the sample. It corresponds to existence of phase boundary γ′+γ / γ in examined alloys. Results of thermal analysis were compared with results obtained with other method performed by authors which is solution calorimetric method.

PL

Układ Ni-Al-Cr jest ważnym układem dla przemysłowych stopów na osnowie fazy międzymetalicznej Ni3Al, która krystalizuje w uporządkowanej sieci L12. Oznacza się ją jako γ′ w odróżnieniu od fazy nieuporządkowanej γ, która pojawia się wraz z dodatkiem stopowym chromu. Wykonano serię stopów, których skład chemiczny leży na linii Ni75Al25÷Ni75Cr25 w bogatej w nikiel części układu Ni-Al-Cr i poddano je analizie DSC. Dodatkowo wykonano kilka pomiarów metodą DTA. Na podstawie zarejestrowanych krzywych udało się zidentyfikować charakterystyczne temperatury podczas nagrzewania i studzenia próbki. Odpowiadają one miejscom występowania granicy międzyfazowej γ′+γ / γ w stopach. Wyniki analiz termicznych zestawiono z wynikami innej metody zastosowanej przez autorów tj. kalorymetrycznej metody typu rozpuszczania.

Słowa kluczowe

EN

Ni-Al-Cr system; intermetallic phase Ni3Al; order-disorder; DSC analysis

PL

system Ni-Al-Cr; faza międzymetaliczna Ni3Al; faza nieuporządkowana; analiza DSC

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2015
• Tom: Vol. 60, iss. 3A
• Strony: 1871--1876
• Opis fizyczny: Bibliogr. 19 poz., rys., tab., wykr. wzory

Twórcy

autor

Maciąg T.

• Silesian University of Technology, Faculty of Materials Engineering and Metallurgy, 8 Krasinskiego Str., 40-019 Katowice, Poland

autor

Rzyman K.

• Silesian University of Technology, Faculty of Materials Engineering and Metallurgy, 8 Krasinskiego Str., 40-019 Katowice, Poland

autor

Przeliorz R.

• Silesian University of Technology, Faculty of Materials Engineering and Metallurgy, 8 Krasinskiego Str., 40-019 Katowice, Poland

Bibliografia

• [1] R. C. Reed, The Superalloys Fundamentals and applications; Cambridge 2006.
• [2] H. Q. Y e, Intemetallics 8, 503÷509 (2000).
• [3] N. S. Stoloff, C. T. Liu, S. C. Deevi, Intermetallics 8, 1313÷1320 (2000).
• [4] V. K. Sikka, S. C. Deevi, S. Viswanathan, R.W. Swindeman, M.L. Santella, Intermetallics 8, 1329÷1337 (2000).
• [5] Chromium Applications for ORNL′s Nickel Aluminides, Oak Ridge Laboratory Review 35, 3 (2002).
• [6] W. Malec, K. Rzyman, M. Czepelak, A. Wala, Archives of Metallurgy and Materials 56, 1007÷1014 (2011).
• [7] A. Taylor, R.W. Floyd, J. Inst. Met. 81, 451 (1952).
• [8] V. A. Chernenko, E. Cesari, J. Pons, C. Segu i, Journal of Materials Research 15, 1496÷1504 (2000).
• [9] T. Anraku, I. Sakaihara, T. Hoshikawa, M. Taniwaki, Materials Transactions 50, 683÷688 (2009).
• [10] A. Szczotok, R. Przeliorz, IOP Conf. Ser.: Mater. Sci. Eng. 35 (2012) DOI: 10.1088/1757-899X/35/1/01 (2005).
• [11] M. Jabłońska, A. Jasik, A. Hanc, Archives of Materials Science and Engineering 29, 16÷19 (2008).
• [12] T. Maciag, K. Rzyman, Journal of Thermal Analysis and Calorimetry 113, 189÷197 (2013).
• [13] W. Huang, Y. A. Chang, Intermetallics 7, 863÷874 (1999).
• [14] N. Dupin, L. Ansara, B. Sundman, Calphad 25, 279÷298 (2001).
• [15] R. Kainuma, I. Ohnuma, K. Ishida, Determination of phase diagrams involving order-disorder transitions, in: J.-C. Zhao (Ed.), Methods for Phase Diagram Determination 2007, Elsevier Ltd. (2007).
• [16] K. Kobayashi, R. Kainuma, K. Fukamichi, K. Ishida, J. Alloy. Compd. 403, 161 (2005).
• [17] Y. M. Hong, Y. Mishima, T. Suzuki, MRS Symp. Proc. 133, 429÷440 (1989).
• [18] Y. M. Hong, H. Nakajima, Y. Mishima, T. Suzuki, Iron Steel Inst. Jpan. Int. 29, 78 (1989).
• [19] Y. Mishima, Y. M. Hong, T. Suzuki, Materials Science and Engineering A 146, 123÷130 (1991).

Uwagi

EN

These studies were supported by the National Science Centre (Project 3217/B/T02/2011/40)