Susceptibility of Alloy IN617 to Hot Cracking

• Autorzy: Konieczna N. , Adamiec J.

Identyfikatory

DOI

10.17729/ebis.2018.4/5

Warianty tytułu

PL

Skłonność do pękania gorącego stopu IN617

• Języki publikacji: EN

Abstrakty

EN

The article presents results of tests concerning the susceptibility of alloy IN617 to hot cracking. The research-related tests required the inert gas-shielded melting of test alloy sheets using a tungsten electrode in forced strain conditions. The process of melting involved 3 mm and 5 mm thick test sheets. The tests of the welded joints included the macro and microstructural analysis of the molten area, base material and heat affected zone. Results obtained in the DTA differential analysis were used to perform tests using a Gleeble 3800 simulator. In the above-presented manner it was possible to determine the high-temperature brittleness range (HTBR) of alloy IN617 as well as to identify the effect of strains on the development of hot cracks in the Transvarestraint test. The tests were supplemented with the fractographic analysis of the crack area. It was revealed that the hot cracking phenomenon occurred within the high-temperature brittleness range of the alloy and depended on the size of strain as well as on the presence of eutectics formed in the solid-liquid state.

PL

Przedstawiono wyniki badań skłonności stopu IN617 do pękania gorącego. W tym celu wykonano próby przetopienia płyt z badanego stopu elektrodą wolframową w osłonie gazu obojętnego w warunkach wymuszonych odkształceń. Proces przetapiania prowadzony był na płytach próbnych o grubości 3 i 5 mm. Badania złączy spawanych obejmowały analizę makro- i mikrostruktury przetopienia, materiału rodzimego i strefy wpływu ciepła. Na podstawie uzyskanych wyników z analizy różnicowej DTA przeprowadzono badania na symulatorze Gleeble 3800. W ten sposób wyznaczono zakres kruchości wysokotemperaturowej (ZKW) stopu IN617, a także określono wpływ odkształceń na rozwój pęknięć gorących w próbie Transvarestraint. Uzupełnieniem badań była wykonana analiza fraktograficzna obszaru pęknięcia. Wykazano, że zjawisko pękania gorącego zachodzi w zakresie kruchości wysokotemperaturowej stopu i zależy od wielkości odkształcenia oraz obecności eutektyk tworzących się w stanie stało-ciekłym.

Słowa kluczowe

EN

metallography; Gleeble; DTA; hot cracking; Inconel 617

PL

metalografia; Gleeble; DTA; gorące pęknięcia; Inconel 617

• Wydawca: Sieć Badawcza Łukasiewicz - Górnośląski Instytut Technologiczny
• Czasopismo: Biuletyn Instytutu Spawalnictwa w Gliwicach
• Rocznik: 2018
• Tom: Vol. 62, No. 4
• Strony: 45--51
• Opis fizyczny: Bibliogr. 11 poz., rys., wykr., tab.

Twórcy

autor

Konieczna N.

• Silesian University of Technology, Institute of Materials Engineering, Katowice

autor

Adamiec J.

• Silesian University of Technology, Institute of Materials Engineering, Katowice

Bibliografia

• [1] Maile M.: Qualification of Ni-Based Alloys for Advanced Ultra Supercritical Plants. Procedia Engineering. 2013, 55, pp. 214–220. https://doi.org/10.1016/j.proeng.2013.03.245
• [2] Klöwer J., Husemann R. U., Bader M.: Development of Nickel Alloys Based on Alloy 617 for Components in 700°C Power Plants. Procedia Engineering. 2013, 55, pp. 226–331. https://doi.org/10.1016/j.proeng.2013.03.247
• [3] Bollinghaus T., Herold H., Cross C. E., Lippold J. C: Hot Cracking Phenomena in Welds II. Berlin 2008, Springer. http://dx.doi.org/10.1007/978-3-540-78628-3
• [4] Tasak E.: Metalurgia spawania. Kraków 2008, Wydawnictwo JAK.
• [5] Ma L.: Identifying and Understanding Environment-Induced Crack Propagation Behavior in Solid Strengthened Ni-Based Superalloys. 2012, Project No. 09-803. University of Nevada.
• [6] DuPont J., Lippold J., Kiser S.: Welding metallurgy and weldability of nickel-base alloys. 2009, New York, John Wiley & Sons. http://dx.doi.org/10.1002/9780470500262
• [7] Turowska A., Adamiec J.: Evaluation of high temperature corrosion resistance of finned tubes made of austenitic steel and nickel alloys. Archives of Metallurgy and Materials, 2016, no. 61 (2), pp. 1089-1093. http://dx.doi.org/10.1515/amm-2016-0183
• [8] Prokhorov N.N.: Russian Castings Production. 1962, 2, p. 172.
• [9] Lancaster J.F.: The metallurgy of welding, brazing and soldering. George Allen& Unwin Ltd, London, 1965. http://dx.doi.org/10.1017/s0368393100081864
• [10] ASME SB-168:2013: Specification for nickel-chromium-iron alloys (UNS N06600, N06601, N06603, N06690, N06693, N06025, and N06045) and nickel- chromium-cobalt-molybdenum alloy (UNS N06617) plate, sheet and strip.
• [11] Adamiec J.: 2010. Spawalność odlewniczych stopów magnezu. Gliwice, Wydawnictwo Politechniki Śląskiej.

Uwagi

PL

Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).

PL

Wersja polska artykułu w wydaniu papierowym s. 55-58.