X-ray Diffraction Study of Pine Wood Treated with NaOH

• Autorzy: Borysiak S. , Doczekalska B.

Warianty tytułu

PL

Badania rentgenowskie drewna sosnowego aktywowanego wodorotlenkiem sodu

• Konferencja: International Conference on X-ray Investigations of Polymer Structures (6 ; 2004 ; Bielsko-Biała, Poland)
• Języki publikacji: EN

Abstrakty

EN

The supermolecular structure of pine wood after mercerisation by sodium hydroxide was investigated by means of wide-angle x-ray scattering (WAXS). The relationship between the condition of mercerised pine wood (Pinus silvestris L.) and the degree of transformation from cellulose I to cellulose II were analysed. It was found that the amount of cellulose II depends on the concentration of NaOH solution as well as on the time of chemical activation. The greatest efficiency of polymorphic transition of cellulose was noted in the highest concentration of sodium hydroxide solution (20 and 25%). Moreover, the rate of polymorphic conversion of cellulose by the decrease in the crystallinity of wood was estimated.

PL

W pracy badano strukturę nadcząsteczkową drewna sosnowego poddanego procesowi merceryzacji wodorotlenkiem sodu za pomocą szerokokątowej dyfrakcji promieni rentgenowskich (WAXS). Przeprowadzono analizę wpływu stosowanych warunków procesu merceryzacji na stopień transformacji fazowej celulozy I do celulozy II. Stwierdzono, że ilość celulozy II, indukowanej w procesie alkalizacji, silnie zależy od stężenia roztworu wodorotlenku sodu oraz od czasu chemicznej aktywacji drewna sosnowego. Największą efektywność transformacji fazowej w celulozie zanotowano przy stosowaniu najwyższych stężeń roztworów NaOH, tj. 20 % i 25 %. Ponadto, proces merceryzacji drewna sosnowego spowodował spadek stopnia krystaliczności celulozy.

Słowa kluczowe

EN

X-ray diffraction; supermolecular structure; pinewood; cellulose; mercerisation; sodium hydroxide

PL

dyfrakcja rentgenowska; struktura nadcząsteczkowa; drewno sosnowe; celuloza; merceryzacja; wodorotlenek sodowy

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2005
• Tom: Vol. 13, no. 5 (53)
• Strony: 87--89
• Opis fizyczny: Bibliogr. 18 poz., rys.

Twórcy

autor

Borysiak S.

• Institute of Chemical Technology and Engineering, Poznan University of Technology, pl. M. Skłodowskiej-Curie 2, 60-965 Poznań, Poland

autor

Doczekalska B.

• Institute of Chemical Wood Technology, August Cieszkowski Agricultural University of Poznan, ul. Wojska Polskiego 38/42, 60-637 Poznań, Poland.

Bibliografia

• 1. Mwaikambo, L. Y.; Ansell, M. P.; Die Angewandte Makromolekulare Chemie 1999, 212, 108.
• 2. Kim, N.-H.; Sugiyama, J.; Okano, T.; Mokuzai Gokkaishi 1991, 37, 637. Young, R. A.; Rowell Y.; Cellulose - Structure, Modification and Hydrolysis; A Wiley-Interscience Publication: New York, 1986.
• 4. Garbarczyk, J., Borysiak, S., Fibres & Textiles in East. Eur. 2003, 11, 104.
• 5. Fengel D., Wegener G.; Wood - Chemistry, Ultrastructure, Reactions; Walter de Gruyter: Berlin, New York, 1989.
• 6. Fengel D.; Papier 1980, 34, 428.
• 7. Sarko A.; Tappi 1978, 61, 59.
• 8. Blackwell J.; Kolpak F.J.; Gardner K.; Tappi 1978, 61, 71.
• 9. Sarko A.; Appl. Polym. Symp. 1976, 28, 729.
• 10. Kim, N.-H.; Sugiyama, J.; Okano, T.; Mokuzai Gokkaishi 1991, 37, 637.
• 11. Young, R. A.; Rowell Y.; Cellulose - Structure, Modification and Hydrolysis; A Wiley-Interscience Publication: New York, 1986.
• 12. Hindeleh A.M.; Johnson, D.J.; Polymer 1974, 15, 697.
• 13. Rabiej, S.; Eur. Polym. 1991, 27, 947.
• 16. Okano T.; Sarko A.; J. Appl. Polym, Sci. 1985, 30, 325.
• 17. Murase H.; Sugiyama J.; Saiki H.; Harada H.; Mokuzai Gakkaishi 1988, 34, 956.
• 18. Rovol J.F.; Goring D.A.; J. Appl. Polym. Sci. 1981, 26, 1275.