Wpływ rodzaju rozpuszczalnika na mechaniczne właściwości włókien z dibutyrylochityny
Języki publikacji
Abstrakty
This paper concerns the manufacture of fibres from dibutyrylchitin (DBC) using the wet spinning method. Special attention was paid to exploring the effect of solvent type on the mechanical properties of DBC fibres. Dimethyl formamide (DMF), dimethyl sulphoxide (DMSO), n-methyl-2-pyrrolidone (MP) and ethyl alcohol (EtOH) were used for preparing the DBC spinning solutions. Additionally, more detailed investigations were carried out on the DMF spinning dope, such as the effect of polymer content in the solution, as well as that of the spinning conditions (temperature of coagulation bath, fibre take-up speed and stretching ratio) on the mechanical properties of DBC fibres. The conditions of DBC fibre spinning on a semi-technical scale were defined for the DMSO and DMF spinning dopes. DBC fibres from DMSO and DMF solutions were characterised by a tenacity of 10.5 to 14.6 cN/tex and elongation at break from 10% to 22%. Batches of DBC fibres (from DMF and DMSO solutions) were prepared for further processing into nonwovens for medical use.
W artykule opisano metodę mokrą wytwarzania włókien z dibutyrylochityny (DBC). Zbadano wpływ rodzaju rozpuszczalnika DBC na mechaniczne właściwości włókien DBC. Do badań zastosowano następujące rozpuszczalniki DBC: dimetyloformamid (DMF), dimetylosulfotlenek (DMSO), N-Metylo-2-pirolidon (MP) i alkohol etylowy (EtOH). Dla roztworów przędzalniczych dibutyrylochityny w DMF zbadano wpływ stężenia polimeru w roztworze a także warunków formowania włókien tj: temperatury kąpieli koagulacyjnej, rozciągu włókien oraz prędkości formowania na właściwości mechaniczne włókien DBC. Warunki formowania włókien DBC w skali 1⁄2-technicznej określone zostały dla roztworów przędzalniczych DMSO i DMF. Włókna DBC formowane z roztworów DMSO i DMF charakteryzowały się wytrzymałością w zakresie od 10,5 do 14,6cN/tex i wydłużeniem w zakresie od 10 do 22%. Partie włókien DBC wytworzone z roztworów DMSO i DMF przygotowane były do wyrobu włóknin do zastosowań medycznych.
Czasopismo
Rocznik
Strony
14--18
Opis fizyczny
Bibliogr. 10 poz., rys., tab.
Twórcy
autor
- Institute of Biopolymers and Chemical Fibresul. M. Sklodowskiej-Curie 19/27 90-570 Łódź, Poland
autor
- Institute of Biopolymers and Chemical Fibresul. M. Sklodowskiej-Curie 19/27 90-570 Łódź, Poland
autor
- Institute of Biopolymers and Chemical Fibresul. M. Sklodowskiej-Curie 19/27 90-570 Łódź, Poland
autor
- Department of Fibre Physics and Textile Metrology Faculty of Textile Engineering and Marketing Technical University of Łódź ul. Żeromskiego 116, 90-543 Łódź, Poland
autor
- Institute of Biopolymers and Chemical Fibresul. M. Sklodowskiej-Curie 19/27 90-570 Łódź, Poland
Bibliografia
- 1. Szosland L., Janowska G.,: ‘The method of preparation of dibutyrylchitin’, 1996, PL 169077 (B1).
- 2. Szosland L., Stęplewski W.: ‘Rheological characteristic of dibutyrylchitin semi-con-centrated solutions and wet spinning of dibutyrylchitin fibres’, in ‘Advances in Chitin Science’, volume II, 7th ICCC (Proceeding of 7th International Conference on Chitin and Chitosan, Lyon, 3 – 5 Sept. 1997), 531-536, 1997, ed. A. Domard, G.A.F. Roberts, K.M. Varum, Jacques Andre Pub. Lyon 1997.
- 3. Szosland L., East G.C.: ‘The dry spinning of dibutyrylchitin fibres’, J. Appl. Polym. Sci. 58, 2459-2466, 1995.
- 4. Biniaś W., Włochowicz A., Biniaś D., Boryniec S.: Polish Patent Application, No. P 359883.
- 5. Biniaś D., Boryniec S., Biniaś W., Włochowicz A.: ‘Alkaline Treatment of Dibutyrylchitin Fibres Spun from Polymer Solution in Ethyl Alcohol’, Fibres & Textiles in Eastern Europe July / September 2006, Vol. 14, No. 3 (57).
- 6. Szosland L., Stęplewski W.: “Method of obtaining fibre from chitin esters’, 2004, PL 187224 (B1).
- 7. Błasińska A., Mikołajczyk T., Krucińska I., Komisarczyk A.: ‘Investigations on ma-nufacturing of porous fibres made from dibutyrylchitin; Rheological properties of spinning solutions in ethanol and N-me-thylpyrrolidone’ Book of Proceedings of the 2nd International Textile, Clothing & Design Conference, Dubrovnik, Croatia, 3-6 October, 2004 (ISBN 953-7105-05-9).
- 8. Błasińska A., Mikołajczyk T.: “Wet Spinning of Dibutyrylchitin Fibres from Ethanol Solution’, Fibres & Textiles in Eastern Europe January / December 2005, Vol. 13, No. 6 (54).
- 9. Struszczyk H., Ciechańska D., Wawro D., Stęplewski W., Krucińska I., Szosland L., Van de Velde K., Kiekens P., ‘Some properties of dibutyrylchitin fibres’ w H. Struszczyk, A. Domard, M.G. Peter, H. Pospieszny, ed., ‘Advances in Chitin Science’ vol. VIII, EUCHIS'04, Institute of Plant Protection, Poznań, p. 279-283, 2005.
- 10. Gillet D., Contandriopoulos Y., Kopczacki P., Rutkowska-Olma E., Szuster L., Muszynski M., Krucinska I., Szosland L., Szumilewicz J., Kornobis E., Kiekens P., van de Velde K., Schoukens G., Wawro D., Stęplewski W.; ‘Dibutyrylchitin as a raw material for new bioactive textile dressing materials’: Results of the CHITOMED European Project’, World Textile Conference, 4th AUTEX Conference, Roubaix, France, 22-24 June 20, 2004.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-478b5d4a-5db1-4144-92db-6f0dfa25f758