Diagnostic methods of detecting defects within the material with the use of active infrared thermovision

• Autorzy: Grochalski K. , Peta K.

Identyfikatory

DOI

10.1515/amtm-2017-0006

• Języki publikacji: EN

Abstrakty

EN

Article presents the methods of detecting defects within material with the use of active infrared thermovision. During the study ABS and PVC samples were used inside which internal structure defects and defects of glue conjunction between components were modeled. During combining composite materials with the use of glue joints, there is a problem with homogenous distribution of the glue layer on the surface of an element, which results in the creation of defects in joint structure and the decline of active surface of adhesion forces on the combined materials. It is then necessary to control the quality of the conjunction between the glued surfaces. The use of non-contact diagnostic methods allows to analyze a larger surface which conditions in more efficient quality control process. In the study, external heat excitation was used - optical excitation with periodic variable signal (LockIn method) and unit step excitation (Pulse method). The methods of analysis of the obtained thermograms are presented.

Słowa kluczowe

EN

active thermovision; thermal images analysis; diagnostic; external forcing heat; defect detection

PL

termowizja aktywna; analiza obrazów termowizyjnych; diagnostyka; zewnętrzne wymuszanie ciepła; wykrywanie usterek

• Wydawca: Wydawnictwo Politechniki Poznańskiej
• Czasopismo: Archives of Mechanical Technology and Materials
• Rocznik: 2017
• Tom: Vol. 37
• Strony: 41--44
• Opis fizyczny: Bibliogr. 7 poz., fig.

Twórcy

autor

Grochalski K.

• Institute of Mechanical Technology, Poznan University of Technology, Piotrowo 3 Street, 60-965 Poznan, Poland

autor

Peta K.

• Institute of Mechanical Technology, Poznan University of Technology, Piotrowo 3 Street, 60-965 Poznan, Poland

Bibliografia

• [1] Więcek B., De Mey G.; „Termowizja w podczerwieni. Podstawy i zastosowania”, Wydawnictwo PAK, 2011.
• [2] Kostowski E.; Przepływ ciepła, Wydawnictwo Politechniki Śląskiej, 2006.
• [3] Liu J., Gong J., Qin L., Wang Y.Y.; „Study on lock-in thermography defect detectability for carbon-fiber reinforced polymer (CFRP) sheet with subsurface defects”, Int J Thermophys, Vol. 36(5-6), 1259-65, 2015.
• [4] Liang T., Ren W., Tian G.Y., Elradi M., Gao Y.; Low energy impact damage detection in CFRP using eddy current pulsed thermography, Composite Structures, Vol. 143, 352-61, 2016.
• [5] http://www.visiooimage.com (18.03.2017).
• [6] Szczepanik M., Stabik J., Wróbel G., Wierzbicki Ł.; Wykorzystanie systemów termowizyjnych do badań materiałów polimerowych, Modelowanie Inżynierskie, T. 5, nr 36, s. 279-286, 2008.
• [7] Szczygieł I.; Konwekcyjny przepływ ciepła, Wydawnictwo Politechniki Śląskiej.

Uwagi

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę (zadania 2017).