Composite Nickel Coatings Produced on 6XXX Series Aluminium Alloys with the Addition of Vanadium

• Autorzy: Nowak M. , Lech-Grega M. , Kozik A. , Mitka M. , Gawlik M. , Kłyszewski A.

Identyfikatory

DOI

10.1515/amm-2015-0487

Warianty tytułu

PL

Kompozytowe powłoki niklowe wytwarzane na stopach aluminum serii 6XXX z dodatkiem wanadu

• Języki publikacji: EN

Abstrakty

EN

Studies of composite nickel coatings electrolytically deposited on aluminium alloys with different content of vanadium were described. Composite coatings were deposited from a Watts bath containing fine-dispersed SiC powder particles in an amount of 20 g/l and organic matters such as saccharin and sodium laurate. The morphology, structure and thickness of the obtained composite coatings were presented. The corrosion resistance of produced coatings was examined by electrochemical method. Basing on the results of studies it was found that coatings obtained with the sole addition of saccharin were characterized by numerous surface defects. The addition of sodium laurate eliminated the occurrence of defects caused by hydrogen evolution and the resulting coatings were continuous with good adhesion to the substrate. The distribution of the ceramic SiC phase in coatings was fairly uniform for all the examined variants of aluminium alloys. SEM examinations did not reveal the phenomenon of the ceramic particles agglomeration.

PL

W pracy przedstawiono badania charakteryzujące kompozytowe powłoki niklowe osadzane elektrolitycznie na stopach aluminium z różną zawartością wanadu. Powłoki kompozytowe wytwarzano w kąpieli Wattsa z dodatkiem drobnodyspersyjnych cząstek proszku SiC w ilości 20 g/l oraz substancji organicznych takich jak sacharyna i laurynian sodu. Przedstawiono morfologię, strukturę, grubość uzyskanych powłok kompozytowych. Odporność korozyjną wytworzonych powłok badano metodą elektrochemiczną. Na podstawie przeprowadzonych badań stwierdzono, iż w przypadku powłok uzyskanych wyłącznie z dodatkiem sacharyny powłoki charakteryzują się licznymi wadami powierzchniowymi. Dodatek laurynianu sodu eliminuje występowanie wad spowodowanych wydzielaniem wodoru, a uzyskane powłoki są ciągłe oraz dobrze przyczepne do podłoża. Rozkład fazy ceramicznej SiC w powłoce jest w miarę równomierny dla wszystkich analizowanych wariantów stopów aluminium. Na podstawie obserwacji wykonanych za pomocą skaningowego mikroskopu elektronowego nie stwierdzono zjawiska aglomeracji cząstek ceramicznych.

Słowa kluczowe

EN

electrodeposition; composite coatings; vanadium; SiC

PL

elektroosadzanie; powłoki kompozytowe; wanad; SiC

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2015
• Tom: Vol. 60, iss. 4
• Strony: 3051--3056
• Opis fizyczny: Bibliogr. 10 poz., rys., tab.

Twórcy

autor

Nowak M.

• Institute of Non-Ferrous Metals in Gliwice, Light Metals Division in Skawina 19 Pilsudskiego Str., 32-050 Skawina, Poland

autor

Lech-Grega M.

• Institute of Non-Ferrous Metals in Gliwice, Light Metals Division in Skawina 19 Pilsudskiego Str., 32-050 Skawina, Poland

autor

Kozik A.

• Institute of Non-Ferrous Metals in Gliwice, Light Metals Division in Skawina 19 Pilsudskiego Str., 32-050 Skawina, Poland

autor

Mitka M.

• Institute of Non-Ferrous Metals in Gliwice, Light Metals Division in Skawina 19 Pilsudskiego Str., 32-050 Skawina, Poland

autor

Gawlik M.

• Institute of Non-Ferrous Metals in Gliwice, Light Metals Division in Skawina 19 Pilsudskiego Str., 32-050 Skawina, Poland

autor

Kłyszewski A.

• Institute of Non-Ferrous Metals in Gliwice, Light Metals Division in Skawina 19 Pilsudskiego Str., 32-050 Skawina, Poland

Bibliografia

• [1] Ch. Leppin/ AluForm Congres, Aluminium Crash Management and simulation, 20-21 (2004).
• [2] S. Zhu, J. Yao, L. Sweet, M. Easton, J. Taylot, P. Robinson, Nick Parson; JOM 65, 5, 584-592, (2013).
• [3] S. Camero, E. S.Puchi, G. Gonzales; J. Mater. Sci. 41, 7361-7373 (2006).
• [4] P. Wang, Y. Cheng, Z. Zhang, J. Coat. Technol. Res. 8, 3 409-417 (2011).
• [5] C. Zanella, M. Lekka, P.L. Bonora, J. Apll. Electrochem. 39, 31-38 (2009).
• [6] I. Garcia, J. Fransem, J.P. Celis, Surf. Coat. Tech. 148, 171-178 (2001).
• [7] L. Du, B. Xu,S. Dong, H. Yang, Y. Wu, Surf. Coat. Tech. 192, 311-316 (2005).
• [8] M. Srivastava, V. K. William Grips, K. S. Rajam, Materials Letters 62, 3487-3489 (2008).
• [9] S. T. Aruna, V. Ezhil Selvil, V. K. William Grips, K. S. Rajam, J. Apll. Electrochem. 41, 461-468 (2011).
• [10] M. Karaś, M. Nowak, M. Opyrchał, M. Bigaj, A. Najder, Arch. Metall. Mater. 59, 355-358 (2014).

Uwagi

PL

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.