Microstructure and Mechanical Properties of Dual-Phase Steel

• Autorzy: Miernik K. , Pytel S.

Identyfikatory

DOI

10.2478/amm-2014-0215

Warianty tytułu

PL

Mikrostruktura i własności mechaniczne stali dwufazowej

• Języki publikacji: EN

Abstrakty

EN

The paper presents results of microstructure and mechanical properties of the dual phase (DP) steel plate with 12 mm thickness produced by intercritical annealing at a two-phase region of ferrite and austenite (α + γ) and direct quenching in water. In addition the tempering treatment at temperature of 650°C was applied to investigate effect of martensite softening on mechanical properties of the tested steel. The parameters of heat treatment were designed to achieve the high strength while retaining optimum impact strength of the DP steel.

PL

W pracy przedstawiono wyniki badań własności mechanicznych i mikrostruktury stali dwufazowej (Dual-Phase Steel) w postaci blachy stalowej o grubości 12 mm otrzymanej w wyniku międzykrytycznego wyżarzania w obszarze występowania ferrytu i austenitu (α + γ) z następującym hartowaniem w wodzie. Dodatkowo przeprowadzono obróbkę cieplną uzyskanej stali dwufazowej na drodze odpuszczania w temperaturze 650°C w celu określenia wpływu zastosowanej obróbki na zmianę własności mechanicznych. Parametry obróbek cieplnych były ukierunkowane na osiągnięcie wysokiej wytrzymałości przy jednoczesnym zachowaniu optymalnej udarności badanej stali dwufazowej.

Słowa kluczowe

EN

dual-phase steel; DP; intercritical annealing; quenching; mechanical properties

PL

stal dwufazowa; wyżarzanie międzykrytyczne; gaszenie; właściwości mechaniczne

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2014
• Tom: Vol. 59, iss. 4
• Strony: 1257--1261
• Opis fizyczny: Bibliogr. 10 poz., rys., tab.

Twórcy

autor

Miernik K.

• Institute of Materials Engineering, Cracow University of Technology, 37 Jana Pawla II Av., 31-864 Kraków, Poland

autor

Pytel S.

• Institute of Materials Engineering, Cracow University of Technology, 37 Jana Pawla II Av., 31-864 Kraków, Poland

Bibliografia

• [1] M. Blicharski, Inzynieria Materiałowa - Stal, Wydawnictwo Naukowo Techniczne, 2009.
• [2] R. C. Hudd, Sheet Steel: Low Carbon, Encyclopedia of Materials: Science and Technology, 2008.
• [3] Y. Sakuma, M. Matsumura, H. Takechi, Mechanical-properties and retained austenite in intercritically heat-treated bainite-transformed steel and their variation with Si and Mn additions, Metallurgical Transactions a-Physical Metallurgy and Materials Science, 1991.
• [4] R. Bogucki, S. M. Pytel, The forming of high mechanical properties of low carbon copper bearing structural steel, Arch. Metal. Mater. 55, 239-246 (2010).
• [5] D. T. Llewellyn, R. C. Hudd, Steels Metallurgy @ Aplications Third Edition, 1988.
• [6] Web site://www.worldautosteel.org/projects/ulsab-avc-2/.
• [7] J. Adamczyk, A. Grajcar, Haeat treatment and mechanical properties of low-carbon steel with dual-phase microstructure, Journal of Achievements in Materials and Manufacturing Engineering 22, 2007.
• [8] V. H. Baltazar Hernandez, S. S. Nayak, Y. Zhou, Tempering of Martensite in Dual -Pahse Steels and Its Effects on Softening Behaviour, Mettallurgical and Materials Transactions A, 2011.
• [9] B. Krebs, A. Hazotte, L. Germain, M. Goune, Quantitative analysis of banded structures in dual-phase steels, Image Analysis and Stereology 2010.
• [10] Web site: http://rsbweb.nih.gov/ij/.