Ability of the CuSn10 and CuSn5Zn5Pb5 brasses fulfillment of plaster mould cavity during underpressure casting

• Autorzy: Pawlak M.
• Języki publikacji: EN

Abstrakty

EN

Results of research on ability of a plaster mould cavity to be filled up on casting with alloy CuSn10 and CuSn5Zn5Pb5 are presented in this paper. The cylindrical plaster mould ø110x290 was casting using underpressure in the Vacuum Pressure Casting Machine VC500D of Indutherm. The size of mould cavity was ø15x200 mm and gauge: 2,0; 1,0; 0,8 and 0,6 mm, the temperature of pouring alloy was 1120, 1140, 1160, 1180 and 1200°C, temperature of plaster mould in the casting moment was 400, 500 and 600°C. The effectiveness of a mould cavity to be filled up on the difference distance from the centre of the mould was assesmented too used to mould cavity 10x200 mm and gauge: 2,0; 1,0; 0,8 and 0,6 mm. On the base of the results of the investigation its possible to reach a conclusion, that the best temperature of casting and temperature of the plaster mould t_f=500÷600°C. The distance of mould cavity from the mould centre doesn’t have a practical meaning for its ability to be filled up.

Słowa kluczowe

EN

innovative foundry technology; innovative foundry materials; precision casting; plaster mould; underpressure casting

PL

nowoczesne technologie w odlewnictwie; innowacyjne materiały w odlewnictwie; odlewnictwo precyzyjne; forma odlewnicza; odlewnictwo podciśnieniowe

• Wydawca: Komisja Odlewnictwa Polskiej Akademii Nauk Oddział w Katowicach
• Czasopismo: Archives of Foundry Engineering
• Rocznik: 2010
• Tom: Vol. 10, iss. 4
• Strony: 163--168
• Opis fizyczny: Bibliogr. 14 poz., fot., rys., tab., wykr.

Twórcy

autor

Pawlak M.

• Technical University of Lodz, Department of Materials Technologies and Production Systems, 1/15 Stefanowskiego Street, 90-924 Lodz, Poland

Bibliografia

• [1] Lewandowski L.: Materiały formierskie (Moulding materials), AKAPIT, Warszawa 1997.
• [2] Pawlak M., Niedźwiedzki Z.: Computer aided process of dimensional distortion determination of bounded plaster sandmix, Part II (Komputerowe wspomaganie procesu określania zmiany wymiarowej związanej gipsowej masy formierskiej, cz. II). Archives of Foundry Enginerring, Vol. 10, Issue 1, January – March 2010, p. 105÷108.
• [3] Pisarek B., Pawlak M.: The thermal analysis and derivate bronzes cast to plaster mould (Analiza termiczna i derywacyjna brązów odlewanych do form gipsowych). Archives of Foundry Engineering, Vol. 9, issue 3, July - September 2009.
• [4] Pawlak M., Niedźwiedzki Z.: Computer aided process of dimensional distortion determination of bounded plaster sandmix, (Komputerowe wspomaganie procesu określania zmiany wymiarowej związanej gipsowej masy formierskiej) Archives of Foundry Engineering, Vol. 9, Issue 3, July – September 2009, p. 261÷266.
• [5] Pisarek B., Pawlak M.: Selection of the temperature of casting the bronzes to plaster moulds (Dobór temperatury odlewania brązów do form gipsowych). Archives of Foundry Engineering, Vol. 9, issue 4, October – December 2009.
• [6] Pawlak M., Niedźwiedzki Z.: Dilatometric studies of plaster sandmix in raw and heat treated state (Badania dylatometryczne mas gipsowych w stanie surowym i po obróbce cieplnej). Archives of Foundry Engineering, Vol. 8, issue 3, July – September 2008, p. 145÷148.
• [7] Pawlak M.: Badanie właściwości firmowych mieszanek gipsowych dla technologii odlewania precyzyjnego z zastosowaniem podciśnienia. Praca niepublikowana, Archiw. K-17, Łódź 2009.
• [8] Pawlak M.: Wpływ temperatury i czasu wygrzewania na właściwości związanej masy formierskiej (Influence of temperature and time of firing on the properties of gypsum). Polska Metalurgia w latach 2002-2006, Komitet Metalurgii Polskiej Akademii Nauk, Kraków 2006.
• [9] Pawlak M.: Proces wysokotemperaturowego wygrzewania form gipsowych dla odlewnictwa artystycznego (The firing gypsum mould for artistic casting). Archiwum Odlewnictwa, PAN, 2006, Nr 19, s. 213÷220.
• [10] Pawlak M.: Proces wygrzewania wstępnego form gipsowych dla odlewnictwa artystycznego (The preliminary baking gypsum moulds for artistic casting). Archiwum Odlewnictwa, PAN, 2005, Nr 17, s. 225÷232.
• [11] Wiktorski M., Pawlak M., Niedźwiedzki Z.: Wpływ składu masy gipsowej na termiczne zmiany wymiarowe formy stosowanej w odlewnictwie precyzyjnym, Archiwum Odlewnictwa, PAN, 2005, nr 17, s. 365÷374.
• [12] Wiktorski M., Pawlak M., Niedźwiedzki Z.: Stanowisko do badania współczynnika przewodzenia ciepła materiałów stosowanych na formy gipsowe w odlewnictwie precyzyjnym (A stand to serach coefficient of thermal conductivity for materials applied on plaster moulds in precision casting), Archiwum Odlewnictwa, PAN, 2004, Nr 13, s. 232÷240.
• [13] Akerman K.: Gips i anhydryt (Gypsum and anhydrite), PWN, Warszawa 1964.
• [14] PN-86/B-04360 Spoiwa gipsowe. Metody badań. Oznaczanie cech fizycznych (Binders based on calcium sulfate. Method of tests for physical properties).