Process of Preparing a Nonwoven/Filament/Woven - Fabric Sandwich Structure with Cushioning Effect of Ballistic Resistance

• Autorzy: Lin J. H. , Hsu C. H. , Meng H. H.

Warianty tytułu

PL

Konstrukcja wielowarstwowego kompozytu tekstylnego z włókien ciągłych i włókniny o efekcie „poduszkowym” dla zastosowań balistycznych

• Języki publikacji: EN

Abstrakty

EN

Non-penetrated damage is a main index that expresses the safety of bulletproof cloth in use. The kinetic energy of the bullet needs to be dissipated and dispersed by the bulletproof cloth after shooting to prevent excessive impact indentation. The nonwoven cushion structure is useful for improving the non-penetrating damage of the bulletproof cloth after a bullet is shot into it. In this work, the novel cushion material of the sandwich structure, made of the filament-laying layer and nonwoven fabric, is used to improve the properties of ballistic resistance. The design of the nonwoven cushion structure is expected to be suitable for reducing the impact indentation of the bulletproof cloth after a bullet is shot; it must be able to replace the original cushion material. The impact indentation of the bullet-shooting test can express the ability of the ballistic resistance or the resistance of the non-penetrating damage. The analytical results show that the design of the nonwoven cushion structure is effective in improving the non-penetrating damage of the bulletproof cloth after the bullet has been shot.

PL

Stopień zniszczenia struktury chronionej, bez jej penetracji, jest podstawowym wskaźnikiem, wyrażającym bezpieczeństwo przy stosowaniu tekstyliów dla odzieży kuloodpornej. Po strzale, energia kinetyczna pocisku musi zostać rozproszona przez tekstylną warstwę ochronną, dla umknięcia nadmiernie dużego odcisku udarowego. Struktury włókniste z efektem „poduszkowym " są użyteczne dla zmniejszenia strefy zniszczeń (bez wystąpienia penetracji) obiektu chronionego. W przedstawionej pracy omówiono nowy materiał z efektem „poduszkowym ", o strukturze warstwowej, z zastosowaniem warstwy syntetycznych włókien ciągłych i włókniny. Wyniki badań potwierdzają sprawność zaprojektowanej konstrukcji, która jest lepsza od dotychczas stosowanych.

Słowa kluczowe

EN

non-penetrated damage; bulletproof cloth; nonwoven cushion structure; impact indentation

PL

zniszczenie bez penetracji; tkanina kuloodporna; włóknina z efektem „poduszkowym "; ucisk udarowy

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2005
• Tom: Vol. 13, no. 4 (52)
• Strony: 43--47
• Opis fizyczny: Bibliogr. 10 poz., rys., tab.

Twórcy

autor

Lin J. H.

• Laboratory of Fiber Application and Manufacturing, Graduated Institute of Textile Engineering, Feng Chia University, Taichung, Taiwan, R.O.C.

autor

Hsu C. H.

• Laboratory of Fiber Application and Manufacturing, Graduated Institute of Textile Engineering, Feng Chia University, Taichung, Taiwan, R.O.C.

autor

Meng H. H.

• Department of Forensic Science, Central Police University, Taiwan, R.O.C.

Bibliografia

• 1. B. A. Cheeseman, T. A. Bogetti: Ballistic impact into fabric and compliant composite laminates. Composite Structures, 61, 2003, p. 161-173.
• 2. L. R. Xu, A. J. Rosakis: Impact failure characteristics in sandwich structures; Part I: Basic failure mode selection. International Journal of Solids and Structures, 39, 2002, p. 4215-4235.
• 3. V. Koissin, V. Skvortsov, S. Krahmalev, A. Shilpsha: The elastic response of sandwich structures to local loading. Composite Structure, 63, 2004, p. 375-385.
• 4. S.R. Swanson, J. Kim: Design of sandwich structures under contact loading. Composite Structures, 59, 2003, p. 403-413.
• 5. L. R. Xu, A. J. Rosakis: Impact failure characteristics in sandwich structures; Part II: Effects of impact speed and interfacial strength. International Journal of Solids and Structures, 39, 2002, p. 4237-4248.
• 6. R. A. Prosser, S. H. Cohen, R. A. Segars: Heat as a factor in the penetration of cloth ballistic panels by 0.22 caliber projectiles, Textile Research Journal, 70 (8), 2000, p. 709–722.
• 7. H. H. Billon, D. J. Robinson: Model for the ballistic impact of fabric armour. International Journal of Impact Engineering, 25, 2001, p. 411-422.
• 8. M. O. W. Richardson, M. J. Wisheart: Review of low-velocity impact properties of composite materials. Composites Part A, 27A, 1996, p. 1123-1131.
• 9. V. P. W. Shim, V. B. C. Tan, T. E. Tay: Modelling deformation and damage characteristics of woven fabric under small projectile impact. Int. J. Impact Eng., 16 (4), 1995, p. 585-605.
• 10. B. Wang, S. M. Chou: The behaviour of laminated composite plates as armour, Journal of Materials Processing Technology, 68, 1997, 279-287.