Wear resistance of graphitized steels

• Autorzy: Byelikov S , Volchok I. , Akimov I

Warianty tytułu

PL

Odporność grafityzowanej stali na zużycie ścierne

• Konferencja: International Conference Development Trends in Mechanization of Foundry Process (6 ; 5-7.09.2013 ; Inwałd, Poland)
• Języki publikacji: EN

Abstrakty

EN

Heat-treated graphitized steels with different carbon, silicon and copper contents have been the object of study. The influence of the composition on the structure and wear resistance (weight loss of the specimen) of graphitized steels (after hardening and tempering) under the conditions of metal to metal dry sliding friction with the use of Amsler-type friction machines, has been investigated in this work. Research results have shown that the main factors affecting wear resistance of graphitized steels have been not only their metal base hardness, but the quantity, shape and distribution of graphite inclusions uniformity in the structure of such steels as well. A regression dependence of the quantity of specimen’s weight loss on carbon, silicon and copper content has been obtained in the work. The highest wear resistance was pertained by the steel having the following content: 1.60. . . 1.70%C; 2.20. . . 2.30%Si; 0.80. . . 0.90%Cu; 0.60. . . 0.70%Mn; 0.15. . . 0.18%Cr; 0.22. . . 0.25%Al; up to 0.015%S and 0.024%P.

PL

Przedmiotem badań była grafityzowana stal (po obróbce cieplnej) o zróżnicowanej zawartości węgla, krzemu oraz miedzi. W pracy przedstawiono wyniki badań wpływu składu chemicznego grafityzowanej stali, po hartowaniu i odpuszczaniu, na jej strukturę i zużycie ścierne (zmniejszenie masy próbki) w warunkach suchego tarcia ”metal-metal” na maszynie typu Amslera. Wyniki badań świadczą o tym, że odporność na zużycie ścierne zależy nie tylko od twardości osnowy metalowej, lecz także od ilości, kształtu i jednorodności wydzieleń grafitu oraz rozkładu przestrzennego wtrąceń w strukturze stali tego typu. Otrzymano zależności regresyjne wartości ubytku masy próbek w funkcji zawartości węgla, krzemu i miedzi. Największą odpornością na zużycie ścierne wyróżniają się stale o następującym składzie chemicznym: 1,60. . .1,70% C, 2,20. . . 2,30% Si, 0,80. . . 0,90% Cu, 0,60. . . 0,70% Mn, 0,15 . .. 0,18% Cr, 0,22. . . 0,25% Al, do 0,015% S i 0,024% P.

Słowa kluczowe

EN

graphitized steel; graphite inclusions; wear resistance

PL

stal grafityzowana; wydzielenia grafitu; zużycie ścierne

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2013
• Tom: Vol. 58, iss. 3
• Strony: 813--816
• Opis fizyczny: Bibliogr. 11 poz., rys., tab.

Twórcy

autor

Byelikov S

• Metal Technology Department, Zaporizhzhya National Technical University, 64 Zhukovskogo St., 69063, Zaporizhzhya, Ukraine

autor

Volchok I.

• Metal Technology Department, Zaporizhzhya National Technical University, 64 Zhukovskogo St., 69063, Zaporizhzhya, Ukraine

autor

Akimov I

• Metal Technology Department, Zaporizhzhya National Technical University, 64 Zhukovskogo St., 69063, Zaporizhzhya, Ukraine

Bibliografia

• [1] G. V. Korovina, Cast graphitized steel - Sverdlovsk: Mahgiz, 1959, 39 p. (in Russian).
• [2] Forming of the optimal structure of graphitized steel / V. M. Zhurakovskij, B. V. Samelik, V. Y. Sadchikov [and oth.] // Technologiya i standartizatsiya proizvosdtva 4, 35-36 (1986) (in Russian).
• [3] I. O. Semenova, Research of the tempered graphite form in nickel steels // Teoriyaipraktika metallurgii 1/2, 110-112 (2011) (in Russian).
• [4] A. A. Zhukov, M. I. Zhurakovskij, Cast graphitized steel // Litejnoe proizvodstvo 10, 30-34 (1993) (in Russian).
• [5] P. Y Gruzdov, Graphitized steel. - M.: Standartizdat 84, (1950) (in Russian).
• [6] R. P. Todorov, M. V. Nikolov, Structure and properties of castings from graphitized steel. - M.: Metallurgiya, 168 (1976) (in Russian).
• [7] A. A. Zhukov, V. P. Polovinchuk, V. S. Churkin, Wear resistant anti-friction chromium-copper cast irons // Izvestiya vysshih uchebnyh zavedenij. Chernaya metalurgiya 4, 30-31 (1993) (in Russian).
• [8] A. A. Zhukov, V. P. Polovinchuk, V. S. Churkin, Copper influence on heat conductivity, wear resistance and machinability of grey cast iron // Mi TOM 4, 25-27 (1989) (in Russian).
• [9] Economic alloying of liner cast iron with copper / R. E. Trubitskij, A. G. Slutskij [and oth.] // Lityei Metallurgiya 4, 72-76 (2010) (in Russian).
• [10] Friction and wear resistance testing machines / L. M. Geller, V. S. Golubkov, B. L. Smushkovich [and oth.], 56 (1974) (in Russian).
• [11] L. P. Gorushkina, Structure and properties of magnesium cast iron. - Kharkov: Vysha shkola, 160 (1980) (in Russian).