Microstructural aspects of repairing unalloyed cast steel with around 0.3% carbon content using welding technology

• Autorzy: Lachowicz Maciej B. , Lachowicz Marzena M.

Identyfikatory

DOI

10.17402/408

• Języki publikacji: EN

Abstrakty

EN

In this work, the results of tests on castings made from unalloyed cast steel, which was repaired using surface padding, have been presented. The purpose of the work was to present the impact of the application of welding technology on the microstructure of cast steels and the dangers related to it. The appearance of a very adverse microstructure was found in the area where the padding occurred. In the light of the presented research, it seems that it is necessary to apply normalizing annealing after the padding of a cast, which will result in a more uniform and fine microstructure of the material being obtained. As a consequence, this will prevent possible operating damage from occurring in the finished products.

Słowa kluczowe

EN

metallography; casting defects; repairing castings; padding; welding methods; microstructure

• Wydawca: Wydawnictwo Naukowe Akademii Morskiej w Szczecinie
• Czasopismo: Zeszyty Naukowe Akademii Morskiej w Szczecinie
• Rocznik: 2020
• Tom: nr 61 (133)
• Strony: 130--135
• Opis fizyczny: Bibliogr. 9 poz., rys., tab.

Twórcy

autor

Lachowicz Maciej B.

• Wrocław University of Science and Technology 27 Wybrzeże Wyspiańskiego, 50-370 Wrocław, Poland
• Machinefish Materials & Technologies Ltd. Limited Partnership 13 Duńska St., 54-427 Wrocław, Poland

autor

Lachowicz Marzena M.

• Wrocław University of Science and Technology 27 Wybrzeże Wyspiańskiego, 50-370 Wrocław, Poland

Bibliografia

• 1. Bęczkowski, R. (2017) Repair Welding of the Massive Cast. Archives of Foundry Engineering 17 (2), pp. 5–8.
• 2. Bęczkowski, R. & Gucwa, M. (2015) Selected aspects of the repair of cast bodies of power equipment. Przegląd Spawalnictwa, Welding Technology Review 87 (5), pp. 106–109.
• 3. Grigorenko, G.M. & Kostin, W.A. (2013) Weldability of steels and criterion of its estimation. Przegląd Spawalnictwa, Welding Technology Review 85 (7), pp. 11–17.
• 4. Kozioł, P. & Organek, P. (2015) Ocena spawalności stali konstrukcyjnych. Przegląd Budowlany 2015 (1), pp. 22–26.
• 5. Mičian, M., Koňár, R., Hlavaty, I., Winczek, J. & Gucwa, M. (2018) The repair of foundry defects in steel castings using welding technology. Archives of Foundry Engineering 18 (2), pp. 177–180.
• 6. Piwowarczyk, T., Winnicki, M., Małachowska, A. & Ambroziak, A. (2014) Casting defects filling by Low Pressure Cold Spraying Method. Archives of Foundry Engineering 14 (1), pp. 109–114.
• 7. PN-85/H-83105 (1985) Odlewy. Podział i terminologia wad.
• 8. Wojciechowski, W. & Kowalski, J.S. (2013) Techniki spawalnicze w odlewnictwie. Napawanie. Archives of Foundry Engineering 13 (1), pp. 87–90.
• 9. Zawadzka, K. & Łybacki, W. (2008) Wspomaganie diagnostyki wad odlewów narzędziami zarządzania jakością. Archiwum Technologii Maszyn i Automatyzacji 28 (1), pp. 89–101.

Uwagi

Opracowanie rekordu ze środków MNiSW, umowa Nr 461252 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2020).