Physical Modelling of the Plastic Working Processes of Zirconium Alloy Bars and Tubes in Thermomechanical Conditions

• Autorzy: Kawałek A. , Dyja H. , Gałkin A. M. , Ozhmegov K.V. , Sawicki S.

Identyfikatory

DOI

10.2478/amm-2014-0157

Warianty tytułu

PL

Modelowanie fizyczne procesów przeróbki plastycznej prętów i rur ze stopu cyrkonu w warunkach termomechanicznych

• Języki publikacji: EN

Abstrakty

EN

The article presents results of physical modelling of processes of plastic working of the modified Zr-1%Nb zirconium alloy, obtained using different methods of the plastometric testing. The „Gleeble 3800”‚ metallurgical process simulator, a DIL805 A/D dilatometer with a plastometric attachment, and a „Setaram‚ plastometer were used for testing. Based on the obtained testing results, the values of the yield stress and limiting plasticity of the tested alloy were determined for wide ranges of temperature variation (T=20÷950°C) and strain rate variation (ε=0.1÷15.0 s^-1) under continuous loading conditions. It was found that by using different testing methods, different alloy properties, characteristic for a given plastic working process, could be obtained.

PL

W artykule przedstawiono wyniki modelowania fizycznego procesów przeróbki plastycznej modyfikowanego stopu cyrkonu Zr-1%Nb, otrzymane za pomocą różnych metod badań plastometrycznych. Do badań zastosowano symulator procesów metalurgicznych „Gleeble 3800”‚ dylatometr DIL805 A/D z przystawką plastometryczną i plastometr „Setaram‚. Na podstawie otrzymanych wyników badań określono wartość naprężenia uplastyczniającego i plastyczności granicznej stopu dla szerokiego zakresu zmian temperatury (T=20÷950°C) i prędkości odkształcenia (ε=0.1÷15.0 s^-1), w warunkach obciążania ciągłego. Stwierdzono, że stosując różne metody badawcze można uzyskać inne własności stopu, charakterystyczne dla danego procesu przeróbki plastycznej.

Słowa kluczowe

EN

Zr-1%Nb; tube; physical modeling; hot; cold deformation

PL

pręty; rury; modelowanie fizyczne; odkształcenie na zimno

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2014
• Tom: Vol. 59, iss. 3
• Strony: 935--940
• Opis fizyczny: Bibliogr. 15 poz., rys.

Twórcy

autor

Kawałek A.

• Częstochowa University of Technology, 19 Armii Krajowej Str., 42-200 Częstochowa, Poland

autor

Dyja H.

• Częstochowa University of Technology, 19 Armii Krajowej Str., 42-200 Częstochowa, Poland

autor

Gałkin A. M.

• Moscow State Institute of Steel And Alloys, Russia

autor

Ozhmegov K.V.

• Moscow State Institute of Steel And Alloys, Russia

autor

Sawicki S.

• Częstochowa University of Technology, 19 Armii Krajowej Str., 42-200 Częstochowa, Poland

Bibliografia

• [1] B. Balance, The Hot Deformation of Austenite AIME, 631, New York: 1977.
• [2] P. I. Polukhin, G. Ja. Gun, A. M. Gałkin, Soprotivlene plasticheskoy deformatsi metallovy splavov, M.: Metallurgia, 351 (1983).
• [3] G. Ju. Kalin, S. Ju. Mushnikova, O. V. Fomina, Fizicheskoe modelirovane processov termodeformatsionnoy obrabotki vysokoprochnoy azotosoderzhashey austenitnoy stalyy issledovana ikh vlyanya na mikrostruktiruy svoystva, Metalli 2, 40-47 (2011).
• [4] S. Mróz, Modification of the roll pass design to the bar rolling process with longitudinal band separation, Archives of Metallurgy and Materials 54, 597-605 (2009).
• [5] D. Gloaguen, M. Francois, R. Guillen, Evolution of internal stresses in rolled Zr702a, Acta Materialia 50, 871-880 (2005).
• [6] Z. Skuza, R. Prusak, R. Budzik, Contemporary elements of system of quality management in metallurgical enterprises, Metallurgy 50, 2, 13140, April/June 2011.
• [7] H. Dyja, A. Gałkin, M. Knapiński, K. Ozhmegov, The plastometric test of a zirconium alloy of the Zr-Nb system, Hutnik Wiadomości Hutnicze, 5, 207-209 (2010).
• [8] L. M. Kachanov, Osnovi teorii plastichnosti, M.: Nauka, 420 (1969).
• [9] P. Szota, S. Mróz, A. Stefanik, H. Dyja, Numerical modelling of the working rolls wear during rods rolling process, Archives of Metallurgy and Materials 56, 2, 495-501 (2011). ]
• [10] V. M. Azhazha, O. V. Ivasishin, I. N. Butenko, Vli-janie rezhimov termomechanicheskoj obrabotki na strukturu, kristallograficheskuju teksturui machanicheskie svojstva spla-va Zr-1%Nb, Voprosi atomnoj naukii techniki, 6, 194-201 (2009).
• [11] M. L. Bernshtein, S. V. Dobatkin, L. M. Kaputkina, S. D. Prokoshkin, Diagrammi gorachey deformatsi, strukturay svoystva staley, M.: Metullurgia, 544 (1989).
• [12] A. Stefanik, H. Dyja, P. Szota, S. Mróz, Determination of the critical value of normalized Cockroft-Latham criterion during multi slit rolling based on tensile test, Archives of Metallurgy and Materials 56, 2, 543-549 (2011).
• [13] S. Sawicki, H. Dyja, Theoretical and experimental analysis of the bimetallic ribbed bars steel – steel resistant to corrosion rolling process, Archives of Metallurgy and Materials 57, 1, 61-69 (2012).
• [14] H. Dyja, A. Gałkin, M. Knapiński, Reologia metali odkształcanych plastycznie, (The rheology of plastically deformed metals) Częstochowa, 371 (2010).
• [15] A. S. Zaymovsky, A. V. Nikulina, N. G. Reshetnikov, Tsirkonevye splavyv atomnoy energetike, M.: Ener-goizdat, 232 (1981).

Uwagi

Artykuł dostępny również w Vol. 59, iss. 4 (2014) str. 1345--1350.