Macroscopic quality evaluation of lacquered steel sheets

• Autorzy: Kuśmierczak S. , Svobodova J.
• Języki publikacji: EN

Abstrakty

EN

This paper deal with the evaluation of quality of lacquered sheets with different pre-treatments after corrosive loading. Samples will be divided into groups according to the type and duration corrosion loadings. After exposure to corrosive salt mist corrosion chamber, the samples will be evaluated macroscopically according to relevant standards. Low degradation after all time corrosion load was on the sample pre-treated with an alkaline degreasing in combination with a yellow chromating and the samples pre-treated with an alkaline degreasing in combination with surface passivation. On these samples showed no loss of adhesion to the base material and the evaluation of delamination due to corrosion during loading had a low degree of degradation. Surfaces after the cross-cut test did not for both sets of samples after corrosion load all times no defects in the adhesion layer.

Słowa kluczowe

EN

macroscopic evaluation; quality; lacquered sheets; pre-treatment

PL

ocena makroskopowa; jakość; arkusz lakierowany; obróbka wstępna

• Wydawca: Oficyna Wydawnicza Stowarzyszenia Menedżerów Jakości i Produkcji
• Czasopismo: Production Engineering Archives
• Rocznik: 2014
• Tom: Vol. 2, No. 1
• Strony: 23--26
• Opis fizyczny: Bibliogr. 6 poz., rys., tab.

Twórcy

autor

Kuśmierczak S.

• Faculty of Production Technology and Management, J.E. University in Ústí nad Labem

autor

Svobodova J.

• Faculty of Production Technology and Management, J.E. University in Ústí nad Labem

Bibliografia

• 1. Bartoníček R. a kol. 1986. Koroze a protikorozní ochrana kovů. Academia, Praha. ISBN 3032-21-037-66.
• 2. Borkowski S., Knop K. 2013. Visual control as a key factor in a production process of a company from automotive branch. Production Engineering Archives. No. 1. ISSN 2353-5156. p.25.
• 3. Holoubek V. 2005. Kataforetické lakování. Avalaible at www http://www.povrchoveupravy.cz/2005-04-clanek01.html
• 4. Kreibich V. 1996. Teorie a technologie povrchových úprav. ČVUT, Praha. ISBN 80-01-01472-X.
• 5. Kraus V. 2000. Povrchy a jejich úpravy. Západočeská univerzita, Plzeň. ISBN 80-7082-668-1.
• 6. Palko M. 2009. Nastupující systém ošetření povrchu před práškovým lakováním. Avalaible at www.povrchovauprava.cz/uploads/assets/casopisy/pu-2009-01.pdf