Evaluation of Casting Fatigue Life Based on Numerical Model and Fatigue Tests

Autorzy
Treść / Zawartość
Identyfikatory
Warianty tytułu
Języki publikacji
EN
Abstrakty
EN
The article presents the results of experimental and numerical analysis carried out on a variable in time state of stress and strain using the proposed algorithm. Calculations were performed on a model of the scraper conveyor lock used in mining transportation equipment; fatigue tests were performed on samples of the cast L20HGSNM steel.
Rocznik
Strony
95--100
Opis fizyczny
Bibliogr. 16 poz., rys., tab., wykr.
Twórcy
autor
  • AGH University of Science and Technology, Faculty of Foundry Engineering, Department of Foundry Process Engineering Reymonta 23, 30-059 Cracow, Poland
autor
  • AGH University of Science and Technology, Faculty of Foundry Engineering, Department of Foundry Process Engineering Reymonta 23, 30-059 Cracow, Poland
Bibliografia
  • [1] Karolczuk A. & Macha E. (2005). A review of critical plane orientations in multiaxial fatigue failure criteria of metallic materials. International Journal of Fracture, Vol. 134, pp. 267-304.
  • [2] Maj M. (2012). Trwałość zmęczeniowa wybranych stopów odlewniczych. Monografia. Wyd. Archives of Foundry Engineering. Katowice-Gliwice.
  • [3] Piekło J., Maj M. & Stachurski W. (1995). Ocena naprężeń eksploatacyjnych w silnie obciążonym elemencie przenośnika zgrzebłowego na podstawie badań elastooptycznych i obliczeń numerycznych. Prace Instytutu Odlewnictwa, Vol. 1-2, pp. 19-30.
  • [4] Maj M. (2005). Zastosowanie zmodyfikowanej niskocyklowej próby zmęczeniowej do wyznaczania właściwości mechanicznych żeliwa ADI w temperaturze podwyższonej i pokojowej. Projekt badawczy 4 T08B 006 25, AGH Kraków.
  • [5] Karolczuk A., Łagoda T. & Ogonowski P. (2006). Weryfikacja kryteriów niskocyklowego zmęczenia metali. Politechnika Opolska, Studia i monografie, Z. 186, Opole.
  • [6] Mrzygłód M. & Zieliński A.P. (2006). Numerical implementation of multiaxial high-cycle fatigue criterion to structural optimization Journal of Theoretical and Applied Mechanics 44, pp. 161-171.
  • [7] Jing Li, Chun-Wang Li, Yan-Jiang Qiao & Zhong-Ping Zhang (2004). Fatigue life prediction for some metallic materials under constant amplitude multiaxial loading. International Journal of Fatigue 68, pp.10-23.
  • [8] Gates N. & Fatemi A. (2004). Notched fatigue behavior and stress analysis under multiaxial states of stress. International Journal of Fatigue 67, pp. 2-14.
  • [9] Piekło J. (1994). A simulation of the phenomenon of crack propagation in an insert of die casting die – part I: Thermal stresses. Prace Instytutu Odlewnictwa, Vol. 3, pp. 139-158.
  • [10] Piekło J. (1995). A simulation of the phenomenon of crack propagation in an insert of die casting die – part II: Initiation and propagation of cracks. Prace Instytutu Odlewnictwa, Vol. 1-2, pp. 1-18.
  • [11] Li B., Reis L. & Freitas M. de (2006). Simulation of cyclic stress/strain evolutions for multiaxial fatigue life prediction. International Journal of Fatigue 28, pp.451-458.
  • [12] Skibicki D. & Dymski S. (2008). Austenite steel transformations under the influence of fatigue loading. Archives of Foundry Engineering Vol. 08 - I3 17.
  • [13] Mroziński S. & Dymski S. (2009). Fatigue damage cumulation in brass under variable loading. Archives of Foundry Engineering Vol. 09 - I3 49.
  • [14] Bernasovský P. (2010). Case studies of steel structure failures. Archives of Foundry Engineering Vol. 10 - SI 1 71.
  • [15] Vechet S., Kohout J. & Hanzlikova K. (2004). Fatigue properties of nodular cast iron in dependence of loading cycle asymmetry. Archives of Foundry AF 04/11 92.
  • [16] Mróz M., Orłowicz W. & Tupaj M. (2010). Evaluation of fractures in MAR-M509 alloy samples after fatigue strength tests. Archives of Foundry Engineering Vol. 10 - I3 22.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-2b1b209a-a52c-49af-b409-65edc61c5d3b
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.