Strukturalne i elektryczne własności wybranych tlenochlorków metali ziem rzadkich
Języki publikacji
Abstrakty
The preparation and sintering conditions of the selected rare-earth oxychlorides REOCl (Re=La, Nd, Sm, Gd) were determined. The purity of materials phase compositions was confirmed by X-ray diffraction method. Further analysis of the data enabled lattice parameters and average grain size determination. The electrical properties of the single phase REOCl materials were investigated by Electrochemical Impedance Spectroscopy in wide temperature range in atmospheric air. The spectra were analyzed by the equivalent circuit fitting. Basing on the values of equivalent circuits parameters the specific conductivities were calculated and presented in the Arrhenius coordinates. Energies of activation were calculated. The determined structural and electrical properties of four different rare-earth oxychlorides were directly compared.
Ustalono warunki syntezy i spiekania wybranych tlenochlorków metali ziem rzadkich, a mianowicie LaOCl, NdOCl, SmOCl oraz GdOCl. Czystość składów fazowych materiałów potwierdzono metodą dyfrakcji promieniowania rentgenowskiego. Analiza uzyskanych danych pozwoliła na wyznaczenie wartości stałych sieciowych oraz średniej wielkości ziaren. Własności elektryczne materiałów wyznaczono metodą elektrochemicznej spektroskopii impedancyjnej w szerokim zakresie temperatur w powietrzu atmosferycznym. Do każdego z widm dopasowano układ zastępczy. Na tej podstawie wyznaczono wartości przewodnictw właściwych i sporządzono wykresy Arrheniusa oraz wyznaczono wartości energii aktywacji. Przeprowadzone badania pozwoliły na bezpośrednie porównanie własności strukturalnych i elektrycznych tlenochlorków czterech różnych metali ziem rzadkich.
Wydawca
Czasopismo
Rocznik
Tom
Strony
1595--1601
Opis fizyczny
Bibliogr. 8 poz., rys., tab., wykr.
Twórcy
autor
- AGH University of Science and Technology, Faculty of Materials Science and Ceramics, al. Mickiewicza 30, 30-059 Krakow, Poland
autor
- AGH University of Science and Technology, Faculty of Materials Science and Ceramics, al. Mickiewicza 30, 30-059 Krakow, Poland
autor
- AGH University of Science and Technology, Faculty of Materials Science and Ceramics, al. Mickiewicza 30, 30-059 Krakow, Poland
autor
- AGH University of Science and Technology, Faculty of Materials Science and Ceramics, al. Mickiewicza 30, 30-059 Krakow, Poland
Bibliografia
- [1] J. Hölsä, R. Lamminmäki, M. Lastusaari, P. Porcher, R. Sáez- Puche, J. Alloy. Compd. 303-304, 498-504 (2000).
- [2] Y. Cho, H. Yang, H. Eun, E. Kim, J. Kim, J. Ind Eng. Chem 11, 707-711 (2005).
- [3] M. Dziubaniuk, P. Pasierb, M. Rękas, Funct. Mater. Lett. 4,171-174 (2011).
- [4] K. Okamoto, N. Imanaka, G. Adachi, Solid State Ionics 154- 155, 577-580 (2002).
- [5] N. Imanaka, K. Okamoto, G. Adachi, Angew. Chem. Int. Ed. Eng. 41, 3890-3892, (2002).
- [6] N. Imanaka, K. Okamoto, G. Adachi, Matter. Lett. 57, 1966- 1969 (2003).
- [7] N. Imanaka, K. Okamoto, G. Adachi, Electrochem. Commmun. 3, 49-51 (2001).
- [8] N. Imanaka, K. Okamoto, G. Adachi, Sens. Actuators B 93, 233-236 (2003).
Uwagi
EN
The financial support of National Science Centre, grant No. 2012/05/N/ST5/01462 is acknowledged
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-2a54b3d9-935c-49d9-af9c-6c65f0424c66