Twisting Characteristics of Rotor - Spun Composite Yarns

• Autorzy: Zhang X. , Xue Y. , Wang S.

Warianty tytułu

PL

Wpływ skrętu na charakter rotorowych przędz kompozytowych

• Języki publikacji: EN

Abstrakty

EN

At two filament over-feed ratios, different kinds of rotor-spun composite yarns were produced by combining staple fibres with filament yarns under varying twisting factors. The yarn tensions were measured, and the effects of twist factors on the characteristics of composite yarns were investigated. The polyester filament in the composite yarn is twisted with the cotton strand and follows a helical path. When the filament tension increases with increasing yarn twist factors and filament over-feed ratio, the filament yarn tends to lie near the inner layer of the composite yarn, and the properties of composite yarns will change accordingly. Compared with the normal rotor-spun yarn, the appearance of composite yarns is clearer, the structure is much tighter, and the properties are improved.

PL

Różnego rodzaju rotorowe przędze kompozytowe wyprodukowano poprzez łączenie włókien odcinkowych z włóknami ciągłymi, przy dwóch współczynnikach naddatku włókna ciągłego i przy różnych współczynnikach skrętu. Mierzono naprężenie przędzy, oraz badano wpływ współczynnika skrętu na właściwości przędz kompozytowych. Włókno ciągłe poliestrowe, jako jeden ze składników przędzy kompozytowej, jest skręcane z nitką bawełnianą i układa się według linii śrubowej. Kiedy wzrasta naprężenie włókna ciągłego ze wzrostem współczynnika skrętu i współczynnika naddatku włókna ciągłego, to ostatnie ma tendencję układania się w pobliżu wewnętrznych warstw włókna kompozytowego, którego właściwości odpowiednio się zmieniają. Porównując z konwencjonalną przędzą rotorową, jego wygląd jest bardziej wyrównany, struktura znacznie bardziej zwarta a właściwości polepszone.

Słowa kluczowe

EN

twisting characteristic; rotor-spun composite yarn; twist factor; filament over-feed ratio; tension

PL

charakterystyka skrętu; rotorowe przędze kompozytowe; współczynnik skrętu; współczynnik naddatku; napięcie

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2006
• Tom: Vol. 14, no. 2 (56)
• Strony: 17--19
• Opis fizyczny: Bibliogr. 13 poz., rys.

Twórcy

autor

Zhang X.

• College of Textiles, Donghua University, Shanghai 200051, P. R. China
• Department of Textiles, Henan Textiles College, Zhengzhou 450007, P. R. China

autor

Xue Y.

• College of Clothing and Art Design, Jiaxing University, Jiaxing 314001, P. R. China

autor

Wang S.

• College of Textiles, Donghua University, Shanghai 200051, P. R. China

Bibliografia

• 1. Wu X. Y., Wang F. M., Wang, S. Y., Textile Res. J., 73(4), p. 305-309, 2003.
• 2. Sawhney A. P. S., Robert K. Q., Ruppenicker G.F., Kimmel L.B., Textile Res. J., 62, p. 21-25, 1992.
• 3. Sawhney A. P. S., Ruppenicker G. F., Kimmel L. B., Robert K. Q., Textile Res. J., 62(2), p. 67-73, 1992.
• 4. Basu A., J. Textile Inst., 91(1), p. 179-182, 2000.
• 5. Huh Y., Kim Y. R., Oxenham W., Textile Res. J., 72(2), p. 156-163, 2002.
• 6. Koc E., Lawrence C. A., Iype C., Fibres &Textiles in Eastern Europe, 13(2), p. 8-15, 2005.
• 7. Nield R., Ali A. R. A., J. Textile Inst., 68(7), p. 223-229, 1977.
• 8. Cheng K. B., Murray R., Textile Res. J., 70(8), p. 690-695, 2000.
• 9. Pouresfandiari F., Fushimi S., Sakaguchi A., Saito H., Toriumi K., Nishimatsu T., Shimizu Y., Shirai H., Matsumoto Y., Gong H., Textile Res. J., 72(1), p. 61-70, 2002.
• 10. Matsumoto Y., Fushimi S., Saito H., Sakaguchi A., Toriumi K., Nishimatsu T., Shimizu Y., Shirai H., Morooka H., Gong H., Textile Res. J., 72(8), p. 735-740, 2002.
• 11. Hearle J. W. S., Gupta B. S., Merchant V.B., Textile Res. J., 35(4), p. 329-334, 1965.
• 12. Lord P. R., Grady P. L., Textile Res. J., 46(2), p. 123-129, 1976.
• 13. Salhotra K. R., Dutta B., Scott S. K., Textile Res. J., 51, p. 360-363, 1981.