Wear resistance of nodular cast iron with carbides

• Autorzy: Gumienny G.
• Języki publikacji: EN

Abstrakty

EN

In this paper results of abrasive and adhesive wear resistance of selected grades of nodular cast iron with carbides are presented. It was demonstrated, that the maximum wear resistance has got nodular cast iron with the microstructure of upper bainite, lower bainite and carbides. This cast iron with hardened steel and sulfonitrided steel is the most advantageous friction pair during adhesive wear testing. It was found, that the least advantageous friction pair is pearlitic nodular cast iron with carbides and normalized steel.

Słowa kluczowe

EN

innovative foundry technology; innovative foundry material; nodular cast iron; carbides; abrasive wear resistance; adhesive wear resistance

PL

innowacyjna technologia odlewnicza; innowacyjny materiał odlewniczy; żeliwo sferoidalne; węgliki; odporność na ścieranie

• Wydawca: Komisja Odlewnictwa Polskiej Akademii Nauk Oddział w Katowicach
• Czasopismo: Archives of Foundry Engineering
• Rocznik: 2011
• Tom: Vol. 11, iss. 3 spec.
• Strony: 81--88
• Opis fizyczny: Bibliogr. 8 poz., rys., tab., wykr.

Twórcy

autor

Gumienny G.

• Department of Materials Engineering and Production Systems, Technical University of Łódź, Stefanowskiego 1/15 Street, 90-924 Łódź, Poland

Bibliografia

• [1] Pietrowski S., Gumienny G., Crystallization of nodular cast iron with carbides, Archives of Foundry Engineering. 2008, Vol. 8, Issue 4/2008, p. 236-240.
• [2] Pietrowski S., Gumienny G., Nodular cast iron with carbides, Archives of Foundry Engineering, No 19, 2006, p. 233-238 (in Polish).
• [3] Pietrowski S., Gumienny G., Bainite obtaining in cast iron with carbides castings, Archives of Foundry Engineering, 2010 Vol. 10, Issue 1, p. 109-114.
• [4] Pietrowski S., Gumienny G., Crystallization of nodular cast iron with additions of Mo, Cr, Cu and Ni, Archives of Foundry Engineering, No 22, 2006, p. 406-413 (in Polish).
• [5] Pietrowski S., Gumienny G., Bainite obtaining in cast iron with carbides castings, Archives of Foundry Engineering, 2010, Vol. 10, Issue 1, p. 109-114.
• [6] Gumienny G., Bainitic-martensitic nodular cast iron with carbides, Archives of Foundry Engineering, 2010, Vol. 10, iss. 2, p. 63-68.
• [7] Gumienny G., Chromium and copper influence on the nodular cast iron with carbides microstructure, Archives of Foundry Engineering, 2010 Vol. 10, iss. 4, p. 47-54.
• [8] Gumienny G., Wear resistance of cast iron, Archives of Foundry Engineering, 2008 Vol. 8, iss. 3, p. 173-180.