Influence of Temperature on The Rate of Copper Recovery From the Slag of The Flash Direct-To-Blister Process by AaSolid Carbon Reducer

• Autorzy: Madej P. , Kucharski M.

Identyfikatory

DOI

10.1515/amm-2015-0289

Warianty tytułu

PL

Wpływ temperatury na szybkość odmiedziowania żużla z procesu zawiesinowego za pomocą reduktora węglowego

• Języki publikacji: EN

Abstrakty

EN

The aim of the work was to investigate the influence of temperature on the rate of copper removal from the obtained slag from the flash direct-to-blister process by means of a carbon reducer. The slag used in this work was taken from the direct-to-blister Outokumpu flash furnace at the smelter in Głogów, and graphite penetrators were used as the slag reducers. The experiment was carried out at 1573 K, 1623 K and 1673 K. It was found that the rate of the de-coppering process of the “Głogów” slag increased with the increase of temperature.

PL

Celem pracy było określenie wpływu temperatury na kinetykę procesu odmiedziowania żużli z procesu zawiesinowego za pomocą reduktora węglowego. Do badań użyto żużel pobrany z procesu zawiesinowego realizowanego w HM „Głogów”, przy czym reduktorem były penetratory grafitowe zanurzane w badanym żużlu. Badania przeprowadzono w temperaturach 1573 K, 1623 K i 1673K. Uzyskane wyniki wskazują, że szybkość procesu zwiększała się ze wzrostem temperatury ale tyko w pierwszym okresie.

Słowa kluczowe

EN

influence of temperature; copper recovery; flesh direct-toblister process; solid carbon reducer

PL

wpływ temperatury; odmiedziowanie żużla; proces zawiesinowy; reduktor węglowy

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2015
• Tom: Vol. 60, iss. 3A
• Strony: 1663--1671
• Opis fizyczny: Bibliogr. 24 poz., rys., tab., wykr., wzory

Twórcy

autor

Madej P.

• AGH University of Science and Technology, Department of Metallurgy of Non-Ferrous Metals, Al.Mickiewicza 30, 30-019 Kraków, Poland

autor

Kucharski M.

• AGH University of Science and Technology, Department of Metallurgy of Non-Ferrous Metals, Al.Mickiewicza 30, 30-019 Kraków, Poland

Bibliografia

• [1] M. Kucharski, Solubility of copper in Outokumpu slag, Metals Technology, 354-356, September 1979
• [2] M. Kucharski, Copper Reduction from Commercial Slag by Solid Iron, Arch. Hutn. 26, 3-10 (1981).
• [3] B. Szafirska, M. Król, A. Warczok, The role of electrokinetic phenomena in copper recovery from flash-smelter slag, Arch. Hutn. 28, 11-25 (1983).
• [4] M. Kucharski, Solubility of Copper in SiO2-CaO-Al2O3 Slags, Arch. Metall. 32, 1, 27-32 (1987).
• [5] J. Czernecki, Z. Śmieszek, J. Botor, R. Wojciechowski, Decopperizing of slag from flash smelting of sulphide concentrates, “Pyrometallurgy ‘87” Symposium organized by The Institution of Mining and Metallurgy in association with The Institute of Metals, London 21-23 September, 1987, pp. 265-283.
• [6] J. Czernecki, Z. Śmieszek, S. Gizicki, J. Dobrzański, M. Warmuz, Problems with Elimination of the Main Impurities in the KGHM Polska Miedź S.A. Copper Concentrates from the Copper Production Cycle (Shaft Furnace Process, Direct Blister Smelting in a Flash Furnace) Sulfide Smelting ’98: Current and Future Practices Edited by J.A. Asteljoki and R.L. Stephens, The Minerals, Metals & Materials Society, 1998, pp. 315-343.
• [7] G. W. Toop, C. S. Samis, Trans. TMS-AIME 224, 878-887 (1962).
• [8] C. R. Masson, Proc. Roy. Soc. A287, 201-221 (1965).
• [9] D. R. Gaskell, Met. Trans. 4, 185-192 (1973).
• [10] M. Kucharski, Metals Technology, 354-356 (1979).
• [11] V. V. Kondakov, D. I. Ryzhonkov, D. M. Golenko: Izv. VUZ Chern. Met. 4, 23-28 (1960).
• [12] P. Grieveson, E. T. Turkdogan, AIME Trans. 230, 1609-1614 (1964).
• [13] H. Krainer, H. P. Beer, H. Brandl, Techn. Mitt. Krupp Forsch.-Ber 24 (3), 139-146 (1966).
• [14] Fay Fun, Metall. Trans.1, 2537-41 (1970).
• [15] M. P. Shalimov, V. N. Boronenkov, S. A. Lyamkin, Metally 6, 32-6 (1980).
• [16] A. Sato, G. Aragane, K. Kamihira, S. Yoshimatsu, Transactions of ISIJ 27, 789-96 (1987).
• [17] D. J. Min, R. J. Fruchan, Metall. Trans. B 23B, 29-37 (1992).
• [18] T. Utigard, G. Sunchez, J. Manriquez, A. Lurashi, C. Diaz, D. Cordero, E. Almendras, Metall. Trans.B 28B, 821-26 (1997).
• [19] A. Warczok, T. A. Utigard, Can. Metall. Q. 37 (1), 27-38 (1998).
• [20] K. P. El-Rassi, T. U. Utigard, Metall. Mater. Trans. B. 31B, 1187-1194 (2000).
• [21] J. Mróz, Metall. Mater. Trans.B.32B (5), 821-30 (2001).
• [22] M. Barati, K. Coley, Metall. Mater. Trans.B 36B, 169-178 (2005).
• [23] K. Rogóż, M. Kucharski, The rate of metal oxides reduction from the slag of the direct-to-blister flash smelting process, Arch. Metall. Materials 55, 317-323 (2010).
• [24] M. Kucharski, T. Sak, P. Madej, M. Wędrychowicz, W. Mróz, A study on the copper recovery from the slag of the Outokumpu direct-to-copper process, Metall. Mater. Trans. B 45B, 590-602 (2014).

Uwagi

EN

We would like to thank the Polish National Center Research and Development (NCBiR) for the financial support – grant Nr 07-0022-10