Comparison of Softened Polylactic Acid and Polyethylene Terephthalate Fabrics Using KES-FB

• Autorzy: Hasani H. , Avinc O. , Khoddami A.

Warianty tytułu

PL

Porównanie zmiękczania tkanin PLA i PET z zastosowaniem systemu KES-FB

• Języki publikacji: EN

Abstrakty

EN

We examined and compared low-stress mechanical properties, such as tensile, shear, bending, compression, and surface properties, measured by the Kawabata Evaluation System for Fabrics (KES-FB), of polyethylene terephthalate (PET) and poly(lactic acid) (PLA) fabrics before and after softening with commercial softeners. The bending and shear properties of both fabrics were influenced by the chemical nature of the softening agents and the emulsion type used in the softener. In contrast, the ionicity and hydrophobicity of the softener appeared to have little or no effect on bending and shear properties of both fabrics. There is no clear trend showing that the LT, RT, MMD, MIU, LC, and RC values of both fabrics were influenced by any of the following properties of the softeners: the chemical nature, emulsion type, ionicity, or hydrophobicity. The best performing softener for both fabrics was a slightly cationic hydrophobic aminofunctional polydimethylsiloxane micro-emulsion softener. Overall, all softened PLA fabrics exhibited lower bending rigidity, tensile linearity, and tensile resilience as well as higher tensile energy, extensibility, geometrical roughness, mean deviation of friction, and compression energy values than all softened PET fabrics, leading to a softer, fuller, and fluffier but rougher fabric handle.

PL

Badano i porównano właściwości mechaniczne przy małych naprężeniach, takie jak: wytrzymałość na zrywanie, ścinanie, zginanie, ściskanie, jak również właściwości powierzchniowe zmierzone za pomocą systemu Kawabata KES-FB. Stwierdzono, że na właściwości zginające i ścinające tkanin wpływa chemiczny skład zmiękczaczy i emulsji. Natomiast właściwości jonowe i hydrofobowe maja minimalny lub zerowy wpływ na właściwości zginania i ścinania obydwu rodzajów tkanin. W pozostałych przypadkach nie stwierdzono występowania wyraźnie określonych zależności pomiędzy parametrami tkanin a rodzajem zmiękczacza. Ogólnie rzecz biorąc, wszystkie zmiękczane tkaniny PLA wykazywały niższą sztywność zginania, liniowość przebiegów wytrzymałościowych na rozciąganie i odprężność, jak również większą energię zrywu, rozciągliwość, średnie odchylenie tarcia i energię ściskania w porównaniu do tkanin PET.

Słowa kluczowe

EN

KES-FB; mechanical properties; surface properties; PLA fabric; PET fabric; softener; softening

PL

KES-FB; właściwości mechaniczne; właściwości powierzchni; PLA; tkaniny PET; zmiękczacze; zmiękczanie

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2013
• Tom: Vol. 21, no. 3 (99)
• Strony: 81--88
• Opis fizyczny: Bibliogr. 23 poz., rys., tab.

Twórcy

autor

Hasani H.

• Department of Textile Engineering, Isfahan University of Technology, Isfahan, Iran

autor

Avinc O.

• Department of Textile Engineering, Faculty of Engineering, Pamukkale University, Denizli, Turkey

autor

Khoddami A.

• Department of Textile Engineering, Isfahan University of Technology, Isfahan, Turkey

Bibliografia

• 1. Heywood D. Textile Finishing. Society of Dyers and Colourists, Bradford, 2003.
• 2. Schindler WD, Hauser PJ. Chemical Finishing of Textiles. Woodhead Publishing in Textiles, 2004.
• 3. Wahle B, Falkowski J. Softeners in textile processing. Part 1: An overview. Review of Progress in Coloration 2002; 32: 118–124.
• 4. Hong J, Jayaraman S. Friction in textiles. Textile Progress 2003; 34 (1/2).
• 5. Dockery A. American Textiles International 1988; 17(12): 40.
• 6. Kawabata S. The Standardization and Analysis of Hand Evaluation. 2nd edition. The Hand Evaluation and Standardization Committee, the Textile Machinery Society of Japan, July 1980.
• 7. Postle R, Kawabata S, Niwa M, Mahar TJ. Textile Machinery: Investing for the Future. Textile Institute, Manchester, 8. 1982.
• 8. Drumright RE, Gruber PR, Henton DE. Polylactic acid technology. Advanced Materials 2000; 12(23): 1841–1846.
• 9. Dugan JS. Novel Properties of PLA Fibers. Research Fiber Innovation Technology, Inc., INTC 2000, Texas, USA, 2000. Available at: http://www.fitfibers.com/ publications.htm.
• 10. Sawyer DJ. PLA technology and applications. Nonwovens World 2001; 10(2): 49–53.
• 11. Jacobsen S, Degée P, Fritz HG. Polylactide (PLA) – a new way of production. Polymer Engineering and Science 1999; 39(7): 1311–1319.
• 12. Blackburn RS. Biodegradable and Sustainable Fibres. Woodhead Publishing Limited, 2005.
• 13. Slade PE. Handbook of Fiber Finish Technology. Marcel Dekker Inc., 1998.
• 14. Avinc O, Wilding M, Gong H, Farrington D. Effects of softeners and laundering on the handle of knitted PLA filament fabrics. Fibers and Polymers 2010; 11(6): 924–931.
• 15. DyStar Plc, IngeoTM Fiber Coloration Pack. DyStar Textilfarben GmbH & Co. Deutschland KG, 2004. Available at: www.natureworksllc.com, accessed November 2010.
• 16. Avinc O, Bone J, Owens H, Phillips D, Wilding M. Preferred alkaline reduction- Received 11.07.2012 Reviewed 03.09.2012 clearing conditions for use with dyed Ingeo poly(lactic acid) fibres. Coloration Technology 2006; 122: 157–161.
• 17. Shore J. Colorants and Auxiliaries, Organic Chemistry and Application Properties. 2nd edition. Volume 2: Auxiliaries. Society of Dyers and Colourists, 2002.
• 18. Bereck A, Riegel D, Matzat A, Habereder P, Lautenschlager H. Silicones on fibrous substrates: Their mode of action. AATCC Review 2001; January: 45–49.
• 19. Kut D, Gunesoglu C, Orhan M. Determining suitable softener type for 100% PET woven fabric. AATCC Review 2005; 5: 16–19.
• 20. Hasani H. Effect of the different processing stages on mechanical and surface properties of cotton-knitted fabrics. Indian Journal of Fiber & Textile Research 2010; 35: 139–144.
• 21. Habereder P, Bereck A. Softeners in textile processing. Part 2: Silicone softeners. Review of Progress in Coloration and Related Topics 2002; 32: 125–137.
• 22. Habereder P. In: 28th Aachen Textile Conference 2001; 2002: 94–104.
• 23. Schindler W, Hauser P. Chemical finishing of textiles: soft-handle finish. ITB International Textile Bulletin 2003; 4: 72–79.