Effect of Chemical Composition and Temperature on Viscosity and Structure of Molten CaO-Al2O3-SiO2 System

• Autorzy: Řeháčková L. , Rosypalová S. , Dudek R. , Ritz M. , Matýsek D. , Smetana B. , Dobrovská J. , Zlá S. , Kawuloková M.

Identyfikatory

DOI

10.1515/amm-2015-0459

Warianty tytułu

PL

Wpływ składu chemicznego i temperatury na lepkość i strukturę ciekłego układu CaO-Al2O3-SiO2

• Języki publikacji: EN

Abstrakty

EN

The effects of the change of chemical composition and temperature on the viscosity of CaO-Al2O3-SiO2 oxide system with basicity from 0.78 to 1.63 were investigated in this paper. Experimental measurements of viscosity were performed with use of the high-temperature viscometer Anton Paar FRS 1600. Viscosity was measured in a rotational mode during heating at the rate of 2.2 K/min in the temperature interval from 1673 to 1873 K. Viscosity is often sensitive to the structural changes in molten oxide systems, which implies that the analysis of viscosity is an effective way to understand the structure of molten oxide systems. Exact clarification of the change of structure of the oxide system caused by increased content of CaO was performed by Fourier transform infrared spectroscopy (FTIR), Raman spectroscopy and X-ray diffraction (XRD).

PL

W artykule badano wpływ zmian składu chemicznego i temperatury na lepkość układu tlenków CaO-Al2O3- SiO2 o zasadowości od 0.78 do 1.63. Pomiary doświadczalne lepkości przeprowadzono z użyciem wiskozymetru wysokotemperaturowego Anton Paar FRS 1600. Lepkość mierzono w układzie obrotowym w czasie ogrzewania z szybkością 2.2 K/min w zakresie temperatur 1673-1873 K. Lepkość jest często wrażliwa na zmiany strukturalne w ciekłych układach tlenkowych, co oznacza, że analiza lepkości jest skutecznym sposobem, aby zrozumieć strukturę układu ciekłych tlenków. Przeprowadzono dokładne wyjaśnienie zmiany struktury systemu tlenków spowodowane zwiększeniem zawartości CaO przy użyciu metody FTI R (Fourier transform infrared spectroscopy), spektroskopii Ramana i XRD (X-ray diffraction).

Słowa kluczowe

EN

CaO-Al2O3-SiO2 system; viscosity; basicity; structure of slag

PL

układ CaO-Al2O3-SiO2; lepkość; zasadowość; struktura żużlu

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2015
• Tom: Vol. 60, iss. 4
• Strony: 2873--2878
• Opis fizyczny: Bibliogr. 13 poz., rys.

Twórcy

autor

Řeháčková L.

• VŠB-Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, 17. listopadu 15/2172, Ostrava-Poruba, Czech Republic

autor

Rosypalová S.

• VŠB-Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, 17. listopadu 15/2172, Ostrava-Poruba, Czech Republic

autor

Dudek R.

• VŠB-Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, 17. listopadu 15/2172, Ostrava-Poruba, Czech Republic

autor

Ritz M.

• VŠB-Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, 17. listopadu 15/2172, Ostrava-Poruba, Czech Republic

autor

Matýsek D.

• VŠB-Technical University of Ostrava, Faculty of Mining and Geology, 17. listopadu 15/2172, Ostrava-Poruba, Czech Republic

autor

Smetana B.

• VŠB-Technical University of Ostrava, Faculty of Mining and Geology, 17. listopadu 15/2172, Ostrava-Poruba, Czech Republic

autor

Dobrovská J.

• VŠB-Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, 17. listopadu 15/2172, Ostrava-Poruba, Czech Republic

autor

Zlá S.

• VŠB-Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, 17. listopadu 15/2172, Ostrava-Poruba, Czech Republic

autor

Kawuloková M.

• VŠB-Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, 17. listopadu 15/2172, Ostrava-Poruba, Czech Republic

Bibliografia

• [1] J. H. Park, Structure - Property Relationship of CaO-MgOSiO2 Slag: Quantitative Analysis of Raman Spectra, Metall. Mater. Trans. B 44, 938 -947 (2013).
• [2] K. C. Mills, The Influence of Structure on the Physico-chemical Properties of Slags, ISIJ Int. 33, 148 - 155 (1993).
• [3] B. O. Mysen, The Structure of Silicate Melts, Annual Review of Earth and Planetary Sciences 11, 75-97 (1983).
• [4] L. Zhang, S. Jahanshahi, Review and Modeling of Viscosity of Silicate Melts: Part I. Viscosity of Binary and Ternary Silicates Containing CaO, MgO and MnO, Metall. Mater. Trans. B 29, 177 -186 (1998).
• [5] S. Rosypalová, L. Řeháčková, R. Dudek, J. Dobrovsá, B. Smetana, L. Dobrovský, M. Žaludová, Influence of Temperature and SiO2 Concentration on Viscosity of Molten Oxide Systems, Hutnické listy 65, 15 - 19 (2012).
• [6] F. A. Cotton, G. Wilkinson, Advanced Inorganic Chemistry (5th Edn), New York: Wiley 1988.
• [7] E. T. Turgdogan, Physicochemical Properties of Molten Slags and Glasses, London: The Metals Society 1983.
• [8] L. Řeháčková, S. Rosypalová, R. Dudek, J. Dobrovská, Influence of CaO content on viscosity of molten CaO-Al2O3- SiO2 system, Archives of Materials Science and Engineering 59, 61 - 68 (2013).
• [9] H. Kim, H. Matsuura, F. Tsukihashi, W. Wang, D.J. Min, I. Sohn, Effect of Al2O3 and CaO/SiO2 on the Viscosity of Calcium-Silicate-Based Slags Containing 10 Mass Pct MgO, Metall. Mater. Trans. B 44, 5-12 (2013).
• [10] Y. M. Gao, S. B. Wang, Ch. Hong, X. J. Ma, F. Yang, Effects of basicity and MgO content on the viscosity of the SiO2- CaO-MgO-9wt%Al2O3 slag system, International Journal of Minerals, Metallurgy and Materials 21, 353 - 362 (2014).
• [11] I. Sohn, D. J. Min, A Review of the Relationship between Viscosity and the Structure of Calcium-Silicate-Based Slags in Ironmaking, Steel Research Int. 83, 611 - 630 (2012).
• [12] J. H. Park, D. J. Min, H. S. Song, Amphoteric Behavior of Alumina in Viscous Flow and Structure of CaO-SiO2(- MgO)-Al2O3 Slags, Metall. Mater. Trans. B 35, 269-275 (2004).
• [13] J. Liao, Y. Zhang, S. Sridhar, X. Wang, Z. Zhang, Effect of Al2O3/SiO2 Ratio on the Viscosity and Structure of Slags, ISIJ Int. 52, 753-758 (2012).

Uwagi

PL

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.