The paper presents the effect of deformation temperature on the mechanical stability of retained austenite in a multiphase TRIP steel. Series of static tensile tests were carried out in the temperature range –20 to 140°C in order to simulate the temperatures occurring during stamping process of automotive steel sheets and conditions of their exploitation. Samples deformed at 20°C and 60°C showed the best combination of strength and ductility. It was related to the gradual transformation of retained austenite into martensite. Obtained results revealed that the intensity of TRIP effect is significantly related to the deformation temperature. The amount of retained austenite, which transformed into martensite during plastic deformation decreases as the deformation temperature increases. It was also found that the stability of retained austenite depends on its morphology. The obtained results showed the relationship between deformation temperature and the stability of retained austenite. The chemical composition and microstructure of multiphase steels dedicated to the automotive industry should be designed for providing the maximum TRIP effect at the specific deformation temperatures.
Wydawca
Czasopismo
Rocznik
Tom
Strony
941--949
Opis fizyczny
Bibliogr. 38 poz., fot., rys., tab.
Twórcy
autor
- Silesian University of Technology, Department of Engineering Materials and Biomaterials, 18A Konarskiego Str., 44-100 Gliwice, Poland
autor
- Silesian University of Technology, Department of Engineering Materials and Biomaterials, 18A Konarskiego Str., 44-100 Gliwice, Poland
autor
- Silesian University of Technology, Department of Engineering Materials and Biomaterials, 18A Konarskiego Str., 44-100 Gliwice, Poland
autor
- Silesian University of Technology, Department of Engineering Materials and Biomaterials, 18A Konarskiego Str., 44-100 Gliwice, Poland
Bibliografia
- [1] A. Grajcar, S. Lesz, Mater. Sci. Forum 706-709, 2124-2129 (2012).
- [2] B. C. De Cooman, Curr. Opin. Solid. St. 8, 285-303 (2004).
- [3] R. Kuziak, R. Kawalla, S. Waengler, Arch. Civ. Mech. Eng. 8, 2, 103-117 (2008).
- [4] Z. Gronostajski, A. Niechajowicz, S. Polak, Arch. Metall. Mater. 55, 1, 221-230 (2010).
- [5] S. Keeler, M. Kimchi, Peter J. Mooney, Advanced high-strength steels application guidelines version 6.0, WorldAutoSteel 2017.
- [6] K. Kowalczyk, M. Jabłońska, S. Rusz, G. Junak, Arch. Metall. Mater. 63, 4, 1957-1961 (2018).
- [7] M. Hojny, M. Glowacki, P. Bała, W. Bednarczyk, W. Zalecki, Arch. Metall. Mater. 64, 1, 401-412 (2019).
- [8] E. Hadasik, R. Kuziak, R. Kawalla, M. Adamczyk, M. Pietrzyk, Steel Res. Int. 77, 927-933 (2006).
- [9] E. V. Pereloma, A. A. Gazder, I. Timokhina, Retained austenite: Transformation-Induced Plasticity, Encyclopedia of Iron, Steel, and Their Alloys. Taylor and Francis, New York 2016.
- [10] A. Grajcar, M. Kciuk, S. Topolska, A. Płachcińska, J. Mater. Eng. Perform. 25, 6, 2245-2254 (2016).
- [11] M. Adamczyk, D. Kuc, E. Hadasik, Arch. Civ. Mech. Eng. 8, 3, 5-13 (2008).
- [12] J. Jung, S. J. Lee, S. Kim, B. C. De Cooman, Steel Res. Int. 82, 857-865 (2011).
- [13] A. Grajcar, Mater. Tehnol. 49, 5, 715-720 (2015).
- [14] A. Grajcar, W. Kwaśny, W. Zalecki, Mater. Sci. Tech. 31, 7, 781-794 (2015).
- [15] C. Garcia-Mateo, F. G. Caballero, ISIJ Int. 45, 1736-1740 (2005)
- [16] K. Radwański, R. Kuziak, R. Rozmus, Arch. Civ. Mech. Eng. 19, 2, 453-468 (2019).
- [17] H. Nasr El-Din, E. A. Showaib, N. Zaafarani, IJMME. 12, 3-12 (2017).
- [18] A. Grajcar, P. Skrzypczyk, D. Woźniak, Arch. Metall. Mater. 59, 4, 1691-1697 (2014).
- [19] A. Kokosza, J. Pacyna, Mater. Sci. Technol. 31, 7, 802-807 (2015).
- [20] L. Kucerova, H. Jirkova, A. Jandova, Acta Metall. Mater. 23, 3, 244-252 (2017).
- [21] A. Kurc-Lisiecka, A. Lisiecki, Mater. Perform. Charact. 8, 6, 1-11 (2019).
- [22] J. Gorka, S. Stano, Metals 8, 2, 132-147, doi: 10.3390/met8020132 (2018).
- [23] A. Grajcar, K. Radwański, Mater. Tehnol. 48, 5, 679-683 (2014).
- [24] S. Chen, Z. Cao, C. Wang, C. Huang, D. Ponge, W. Cao, J. Iron Steel Res. Inst. 26, 1209-1218 (2019).
- [25] A. Kokosza, J. Pacyna, Arch. Metall. Mater. 55, 1001-1006 (2010).
- [26] M. N. Yoozbashi, T. Hajilou, E. Akbarzadeh Chiniforush, S. Yazdani, ISSI Int. 14, 2, 27-32 (2017).
- [27] F. G. Caballero, C. Garcia-Mateo, J. Chao, M. J. Santofimia, C. Capdevila, C. G. de Andres, ISIJ Int. 48, 1256-1262 (2008).
- [28] C. Garcia-Mateo, F. G. Caballero, J. Chao, C. Capdevila, C. Garcia de Andres, J. Mater. Sci. 44, 17, 4617-4624 (2009).
- [29] S. Zaefferer, J. Ohlert, W. Bleck, Acta Mater. 52, 9, 2765-2778 (2004).
- [30] D. X. Zhu, S. H. Li, J. He, Mater. Sci. Eng. A 680, 54-63 (2017).
- [31] H. S. Park, J. C. Han, N. S. Lim, J. B. Seol, C. G. Park, Mater. Sci. Eng. A 627, 262-269 (2015).
- [32] I. Timokhina, P. Hodgson, E. V. Pereloma, Metall. Mater. Trans. A 35, 2331-2341 (2004).
- [33] A. Das, M. Ghosh, S. Tarafder, S. Sivaprasad, D. Chakrabarti, Mater. Sci. Eng. A 680, 249-258 (2017).
- [34] A. Grajcar, A. Kozłowska, K. Radwański, A. Skowronek, Metals, 9, doi: 10.3390/met9121304 (2019).
- [35] K. Sugimoto, M. Misu, M. Kobayashi, H. Shirasawa, ISIJ Int. 33, 775-782 (1993).
- [36] L. Luo, W. Li, L. Wang, S. Zhou, X. Jin, Mater. Sci. Eng. A 682, 698-703 (2017).
- [37] R. Tian, L. Li, B. C. De Cooman, X. C. Wei, P. Sun, J. Iron Steel Res. Inst. 13, 51-56 (2006).
- [38] A. Kozłowska, A. Janik, K. Radwański, A. Grajcar, Materials, 12, doi: 10.3390/ma12183042 (2019)
Uwagi
EN
1. A. Kozłowska acknowledges the support from statutory funds of the Faculty of Mechanical Engineering of Silesian University of Technology in 2019.
PL
2. Opracowanie rekordu ze środków MNiSW, umowa Nr 461252 w ramach programu "Społeczna odpowiedzialność nauki" - moduł: Popularyzacja nauki i promocja sportu (2020).
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-1e2b7271-90eb-458e-8d6d-9e0b129b6052