Influence of Technological Parameters of Furane Mixtures on Shrinkage Creation in Ductile Cast Iron Castings

• Autorzy: Vasková I. , Hrubovčáková M. , Eperješi Š. , Malik J.

Identyfikatory

DOI

10.2478/amm-2014-0174

Warianty tytułu

PL

Wpływ właściwości masy furanowej na wielkość skurczu odlewów z żeliwa sferoidalnego

• Języki publikacji: EN

Abstrakty

EN

Ductile cast iron (GS) has noticed great development in last decades and its boom has no analogue in history humankind. Ductile iron has broaden the use of castings from cast iron into areas, which where exclusively domains for steel castings. Mainly by castings, which weight is very high, is the propensity to shrinkage creation even higher. Shrinkage creation influences mainly material, construction of casting, gating system and mould. Therefore, the main realized experiment was to ascertain the influence of technological parameters of furane mixture on shrinkage creation in castings from ductile iron. Together was poured 12 testing items in 3 moulds forto determine and compare the impact of various technological parameters forms the propensity for shrinkage in the casting of LGG.

PL

W ostatnich latach obserwuje sie intensywny wzrost produkcji odlewów z żeliwa sferoidalnego. Dotyczy to także zastępowania tym tworzywem odlewów staliwnych. W przypadku masywnych odlewów szczególnie duże znaczenie odgrywa przebieg skurczu tworzywa. Powstawanie skurczu wiąże się z materiałem odlewu, jego konstrukcja, układem wlewowym oraz materiałem formy. Celem badan zaprezentowanych w artykule jest ocena wpływu właściwości technologicznych formy na podstawie skurczu. Odlano 12 kształtek w 3 formach, aby ocenić wpływ jakości formy na skurcz odlewów z żeliwa sferoidalnego.

Słowa kluczowe

EN

graphitization; shrinkage; metallurgical quality; furan molding sand

PL

grafityzacja; skurcz odlewniczy; jakość metalurgiczna; furanowe masy formierskie

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2014
• Tom: Vol. 59, iss. 3
• Strony: 1037--1040
• Opis fizyczny: Bibliogr. 11 poz., rys., tab.

Twórcy

autor

Vasková I.

• Department of Ferrous Metallurgy and Foundry, Faculty of Metallurgy, Technical University in Košice, Slovakia

autor

Hrubovčáková M.

• Department of Ferrous Metallurgy and Foundry, Faculty of Metallurgy, Technical University in Košice, Slovakia

autor

Eperješi Š.

• Department of Ferrous Metallurgy and Foundry, Faculty of Metallurgy, Technical University in Košice, Slovakia

autor

Malik J.

• Department of Ferrous Metallurgy and Foundry, Faculty of Metallurgy, Technical University in Košice, Slovakia

Bibliografia

• [1] Z. Gedeonova, I. Jelč, Metallurgy of Cast Irons. Technical university at Kosice, Faculty of Metallurgy 2000.
• [2] J. Vilcko, S. Slovak. Foundry Technologies. ALFA, Bratislava, 1987.
• [3] Ductile Iron and its using, p. 2, Slevarenstvi, 8/199.
• [4] T Smekal, Effect of technological parameters on the formation of furan mold shrinkage in LGG casts. PhD thesis Kosice, 2009.
• [5] Z. Gedeonova, H. Pacyna, Metallurgical and technological influences to impacts onthe need fora poweredmetaldur-ing solidificationof spheroidal graphitecast iron, Slevarenstvi, 2003.
• [6] J. Rous, Shrinkage in castings. P.273 Slevarenstvi 7/1997.
• [7] Z. Gedeonova, Theory of foundry processes. Technical university at Kosice, 1990.
• [8] I. Fürbacher, K. Macek, J. Steidl, Lexicon of technical materials. VerlagDashofer.CES EduPack 2006, Granta Design Ltd., Cambridge, UK.
• [9] R. Hummer, Giesserei-Praxis, Nr.17/18, 241-245 (1985).
• [10] S. Karsay, QIT comp: DUCTILE IRON III.
• [11] L. Bechny, P. Masarik, Cast Iron Modern .1, 49 (1989).