Investigation of the possibility of forming nanofibres with potato starch

• Autorzy: Šukytė J. , Adomavičiūtė E. , Milašius R.

Warianty tytułu

PL

Badanie możliwości wytwarzania nanowłókien z udziałem skrobi ziemniaczanej

• Języki publikacji: EN

Abstrakty

EN

In this paper nanofibres were formed from PVA solution with potato starch and a small amount of ethanol. Due to the previous study, it was determined that with the addition of ethanol (30 wt.%) in the solution, it is possible to form bicomponent PVA/cationic starch (75/25 wt.%) nanofibres. Preparation of a procedure using cationic starch was quite difficult, and therefore a high quantity of ethanol was also not desirable. In this study the influence of simple potato starch (which is used in the food industry) and a low quantity of ethanol on the formation of nanofibres was analysed. The results showed that with a 5 wt.% amount of potato starch it is impossible to form nanofibres by the electrospinning process. However, when a 5 wt.% amount of ethanol is added to the PVA solution, it was possible to form nonwoven material from nanofibres. It was confirmed that even a small amount of ethanol has a significant positive influence on the electrospinning process but not a positive influence on the nanofibres and web structure.

PL

Formowano nanowłókna z roztworu polialkoholu winylowego (PVA) z dodatkiem skrobi ziemniaczanej i małej ilości etanolu. Na podstawie wcześniejszych badań było wiadomo, że po dodaniu etanolu (30 wt.%) do roztworu jest możliwe formowanie nanowłókien dwuskładnikowych PVA/skrobia kationowa (75/25 wt.%). Opracowanie procedury używania skrobi kationowej było dość trudne, stwierdzono również że dla wytworzenia włókien niepożądana jest większa ilość etanolu. W pracy badano wpływ zwykłej skrobi ziemniaczanej, używanej w przemyśle spożywczym, oraz małej ilości etanolu na formowanie nanowłókien. Wyniki pokazują, że przy 5 wt.% skrobi ziemniaczanej formowanie nanowłókien metodą elektroprzędzenia jest niemożliwe. Jednakże jeśli zostanie dodane 5 wt.% etanolu do roztworu PVA staje się możliwe wytworzenie włókniny z tych nanowłókien. Potwierdzono, że nawet niewielka ilość etanolu ma znaczący pozytywny wpływ na proces elektroprzędzenia, ale nie wpływa pozytywnie na nanawłókna i strukturę wyrobu.

Słowa kluczowe

EN

electrospinning; nanofibre; PVA; potato starch

PL

elektroprzędzenie; nanowłókna; roztwór polialkoholu winylowego; PVA; skrobia ziemniaczana

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2010
• Tom: Vol. 18, no. 5 (82)
• Strony: 24--27
• Opis fizyczny: Bibliogr. 17 poz., rys.

Twórcy

autor

Šukytė J.

• Kaunas University of Technology, Department of Textile Technology, Studentu 56, LT-51424, Kaunas, Lithuania

autor

Adomavičiūtė E.

• Kaunas University of Technology, Department of Textile Technology, Studentu 56, LT-51424, Kaunas, Lithuania

autor

Milašius R.

• Kaunas University of Technology, Department of Textile Technology, Studentu 56, LT-51424, Kaunas, Lithuania

Bibliografia

• 1. Ioannis S.; Chronakis. Journal of Materials Processing Technology, Vol. 167 (2005) pp. 283-293.
• 2. Doshi J., Reneker H. D.; Journal of electrostatics, Vol. 35 (1995) pp. 151-160.
• 3. Thandavamoorthy S., Ghat G. S., Tock R. W., Parameswaran S., Ramkumar S. S.; Journal of Applied Polymer Science, Vol. 96 (2005) pp. 557-569.
• 4. Torres-Giner S., Ocio M. J., Lagaron J. M.; Eng. Life Sci. Vol. 3 (2008) pp. 303-314.
• 5. Huang Z. M., Zhang Y. Z., Kotaki M., Ramakrishna S.; Composite Sci. Technol., Vol 63 (2003) pp. 2223-2253.
• 6. Danelevičiūtė-Vainienė A., Katunskis J., Buika G.; Fibre &Textiles in Eastern Europe, Vol 17 No 6 (2009) pp. 40-43.
• 7. Ignatova M., Starbova K., Markova N., Manolova N., Rashkov I.; Carbohydrate Research 341 (2006) pp. 2098-2107.
• 8. Hunley T. M., Long E. T.; Polymer International Vol. 57 (2008) pp. 385-389.
• 9. Lee K-H., Givens S., Chase D. B., Rabolt J. F.; Polymer, Vol. 47 (2006) pp. 8013-8018.
• 10. Adomačiūtė E., Milašius R., Žemaitaitis A., Bendoraitienė J., Leskovšek M., Demšar A.; Fibres & Textiles in Eastern Europe, Vol. 17 No 3(74), 2009, pp. 29-33.
• 11. Koski A., Yim K., Shivkumar S.; Materials Letters, Vol. 58 (2004) pp. 493-497.
• 12. Kenawy E-R., Abdel-Hay F.I., EI-Newehy M. H., Wnek G. E.; Materials Science and Engineering, Vol. 459 (2007) pp. 390-396.
• 13. Tao J., Shivkumar S.; Materials Letters, Vol. 61 (2006) pp. 2325-2328.
• 14. Zhang C., Yuan X., Wu L., Han Y., Sheng J.; European Polymer Journal, Vol. 41 (2005) pp. 423-432.
• 15. Adomavičiūtė E., Milašius R.; Fibre &Textiles in Eastern Europe, Vol. 15 No. 5-6(64-65), 2007, pp. 69-72.
• 16. Supaphol P., Chuangchote S.; Journal of Applied Polymer Science, Vol. 108 (2008) pp. 969-978.
• 17. Adomavčiūtė E., Milašius R., Levinskas R.; Materials Science (Medžiagotyra), Vol 13(2007) No.2 pp. 152-155.