Microstructure and hardness of Co-based alloy/tungsten carbide padding welds produced by TIG method

• Autorzy: Piasecki A. , Popławski M. , Młynarczyk A.

Warianty tytułu

PL

Mikrostruktura i twardość napoin na bazie kobaltu iwęglika wolframu wytworzonych metodą TIG

• Języki publikacji: EN

Abstrakty

EN

In this study, surface layers were produced by the surfacing of powders on S355 steel with the tungsten inert gas process (TIG). The powders consisted of a cobalt based alloy and 20% tungsten carbide. Padding welds were obtained at two different current intensity values, namely 90 and 120 A. The microstructure, chemical and phase composition, as well as hardness of the padding welds were studied. On the basis of the conducted research it was found that the padding welds Were characterized by a multiphase structure and are connected with the substrate by diffusion. The produced padding welds consisted of dendrites and eutectics. The padding welds produced at the lower current intensity were characterized by higher hardness.

PL

W pracy wytworzono napoiny w wyniku napawania metodą TIG proszków na bazie kobaltu i 20% WC na stali konstrukcyjnej S355. Napoiny wytworzono przy dwóch różnych natężeniach prądu 90 i 120 A. Zbadano mikrostrukturę, skład chemiczny i fazowy oraz twardość napoin. Na podstawie przeprowadzonych badań stwierdzono, że napoiny charakteryzują się wielofazową budową oraz dyfuzyjnym związaniem z podłożem. Wytworzone napoiny były zbudowane z dendrytów i eutektyki. Większą twardością charakteryzowały się napoiny wytworzone przy mniejszym natężeniu prądu.

Słowa kluczowe

EN

laser alloying; laser raster-scanning; nodular iron

PL

stopowanie laserowe; raster; żeliwo sferoidalne

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2013
• Tom: Vol. 34, nr 2
• Strony: 121--124
• Opis fizyczny: Bibliogr. 6 poz., rys., tab.

Twórcy

autor

Piasecki A.

• Instytut Inżynierii Materiałowej, Politechnika Poznańska

autor

Popławski M.

• Instytut Inżynierii Materiałowej, Politechnika Poznańska

autor

Młynarczyk A.

• Instytut Inżynierii Materiałowej, Politechnika Poznańska

Bibliografia

• [1] Azimmi G., Shamanian M.: Microstructure and wear properties of Fe-Cr-C and Fe-Cr-Si-C clads on carbon steel by TIG surfacing process. Advanced Materials Research 83-86 (2010) 1035÷1042.
• [2] Bober M., Senkara J.: Napawanie plazmowo-proszkowe warstw stopu Fe- Cr-W-Mo z węglikiem wanadu. Spajanie Metali i Tworzyw w Praktyce 1 (16) (2007) 16÷21.
• [3] Klimpel A.: Napawanie i natryskiwanie cieplne. Technologie. WNT, Warszawa (2000).
• [4] Madadi F., Shamanian M., Ashrafizadeh F.: Effect of pulse current on microstructure and wear resistance of Stellite 6/tungsten carbide claddings produced by tungsten inert gas process. Surface and Coatings Technology 205 (17-18) (2011) 4320÷4328.
• [5] Zhang C., Qi L., Hu F., Zhang S., Wang M.: Study of WC particles dissolved by plasma surfacing. Advanced Materials Research 299-300 (2011) 193÷196.
• [6] Zhong M., Liu W., Yao K., Goussain J. C., Mayer C., Becker A.: Microstructural evolution in high power laser cladding of Stellite 6 + WC layers. Surface and Coatings Technology 157 (2-3) (2002) 128÷137.