Influence of Lubricants on Wear Resistance of Aluminum Alloy Strips Series 2XXX

• Autorzy: Żaba K. , Kita P. , Nowosielski M. , Kwiatkowski M. , Madej M.

Identyfikatory

DOI

10.1515/amm-2015-0313

Warianty tytułu

PL

Wpływ środków smarnych na odporność na zużycie blach ze stopu aluminium serii 2XXX

• Języki publikacji: EN

Abstrakty

EN

The article presents a properly planned and designed tests of the abrasive wear resistance 2024 aluminum alloy strips under friction conditions involving various lubricants. Test were focused on the selection of the best lubricant for use in industrial environment, especially for sheet metal forming. Three lubricants of the Orlen Oil Company and one used in the sheet metal forming industry, were selected for tests. Tests without the use of lubricant were performed for a comparison. The tester T-05 was used for testing resistance to wear. As the counter samples were used tool steel - NC6 and steel for hot working - WCL, which are typical materials used for tools for pressing. The results are presented in the form of the force friction, abrasion depth, weight loss and coefficient of friction depending on the lubricant used and the type of counter samples. The results allowed for predicting set lubricant-material for tools which can be applied to sheet metal made of aluminum alloy 2024.

PL

W artykule przedstawiono wyniki badań odporności na zużycie blach ze stopu aluminium serii 2024 w różnych warunkach smarowania. Badania były ukierunkowane na wybór najlepszego środka smarnego do zastosowania w warunkach przemysłowych, przede wszystkim do tłoczenia blach. Do badań wytypowano trzy środki smarne firmy Orlen Oil oraz jeden środek smarny stosowany w przemyśle do tłoczenia blach. Dla porównania wykonano również badania bez użycia środka smarnego. Do badań odporności na zużycie wykorzystano tester T-05. Jako materiały przeciwpróbek zastosowano stal narzędziową NC6 oraz stal do pracy na gorąco WCL, będące typowymi materiałami wykorzystywanymi na narzędzia do tłoczenia. Wyniki badań przedstawiono w postaci zależności siły tarcia, głębokości wytarcia, ubytku masy i współczynnika tarcia od zastosowanego środka smarnego i rodzaju przeciwpróbki. Wyniki badań pozwoliły na wytypowanie najlepszego, spośród badanych, zestawu środek smarny-materiał na narzędzia, do tłoczenia blach ze stopu aluminium z gatunku 2024.

Słowa kluczowe

EN

lubricants; wear resistance; aluminum alloy strips series 2XXX

PL

smary; odporność na zużycie; blachy ze stopu aluminium serii 2XXX

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2015
• Tom: Vol. 60, iss. 3A
• Strony: 1833--1837
• Opis fizyczny: Bibliogr. 14 poz., rys., tab., wykr.

Twórcy

autor

Żaba K.

• AGH University of Science and Technology, Faculty of Non-Ferrous Metals, Al. A. Mickiewicza 30, 30-059 Krakow, Poland

autor

Kita P.

• AGH University of Science and Technology, Faculty of Non-Ferrous Metals, Al. A. Mickiewicza 30, 30-059 Krakow, Poland

autor

Nowosielski M.

• AGH University of Science and Technology, Faculty of Non-Ferrous Metals, Al. A. Mickiewicza 30, 30-059 Krakow, Poland

autor

Kwiatkowski M.

• AGH University of Science and Technology, Faculty of Non-Ferrous Metals, Al. A. Mickiewicza 30, 30-059 Krakow, Poland

autor

Madej M.

• AGH University of Science and Technology, Faculty of Metals Engineering and Industrial Computer Science, Al. A. Mickiewicza 30, 30-059 Krakow, Poland

Bibliografia

• [1] S. Kumar, A. P. Harsha, H. S. Goyal, A. A. Hussain, S. B. Wesley, Part J: Journal of Engineering Tribology 227, 328-338 (2012).
• [2] S. M. R. Mousavi Abarghouie, S. M. Seyed Reihani, Journal of Alloys and Compounds 501, 326-332 (2010).
• [3] M. Muratoğlu, M. Aksoy, Journal of Materials Processing Technology 174, 272–276 (2006).
• [4] S. M. R. Mousavi Abarghouie, S. M. Seyed Reihani, Materials & Design 31 (5), 2368–2374 (2010).
• [5] K. Żaba, Archives of Metallurgy and Materials 56 (4), 871-882 (2011).
• [6] K. Żaba, M. Madej, Archives of Metallurgy and Materials 56 (4), 860–869 (2011).
• [7] K. Żaba, M. Nowosielski, P. Kita, M. Madej, Influence of lubricant on the wear resistance of aluminized steel strip, COMAT 2012, conference proceedings.
• [8] ASTM B209 – 10, Standard specification for aluminum and aluminum-alloy sheet and plate.
• [9] EN 573-3:2009, Aluminum and aluminum-alloy. Chemical composition and form of wrought product. Chemical composition and form of product.
• [10] ASTM D 2714, Standard Test Method for Calibration and Operation of the Falex Block-on-Ring Friction and Wear Testing Machine.
• [11] ASTM D 3704, Standard Test Method for Wear Preventive Properties of Lubricating Greases Using the (Falex) Block on Ring Test Machine in Oscillating Motion.
• [12] ASTM D 2981, Block-on-Ring Test for Solid Lubricants.
• [13] ASTM G 77, Standard Test Method for Ranking Resistance of Materials to Sliding Wear Using Block-on-Ring Wear.
• [14] M. Babić, B. Stojanović, S. Mitrović, I. Bobić, N. Miloradović, M. Pantić, Tribological Journal Bultrib 3, 148-164 (2013).