Skutki wadliwego doboru mieszanki w mostowych łożyskach elastomerowych

• Autorzy: Niemierko A. , Piaskiewicz M.

Warianty tytułu

EN

Effects of improper compound selection of elastomeric bridge bearings

• Konferencja: Współczesne metody budowy, wzmacniania i przebudowy mostów : XXIV seminarium (3-4.06.2014; Poznań, Polska)
• Języki publikacji: PL

Abstrakty

EN

Properly selected compound for elastomeric bridge bearing is a key factor of their reliability and durability. Independently from the compound which will be chosen based on natural or synthetic caoutchouc it should be always resistant on ozone, sunlight, ultraviolet radiation and temperature as well as on oxidation. Over 80-years use of elastomeric bearings in bridge construction confirms their utility as material supporting bridge superstructures. But it is registered from time to time that failed technology or wrong rubber compound are the reason of defects occurred in practice. One such a case was discussed in the paper. Improper of natural rubber compound was a main cause of superficial deep cracks on the whole depth of elastomeric blocks. Material tests carried out on sample cut out from bearing pad revealed low elastomer resistance on ozone and higher temperature action. It was decided that all defected bearings should be replaced.

Słowa kluczowe

PL

łożyska elastomerowe; łożyska mostowe; elastomery; estakada

• Wydawca: Wydawnictwo Politechniki Poznańskiej
• Czasopismo: Archiwum Instytutu Inżynierii Lądowej
• Rocznik: 2014
• Tom: Nr 18
• Strony: 93--106
• Opis fizyczny: Bibliogr. 13 poz., rys., tab.

Twórcy

autor

Niemierko A.

• Instytut Badawczy Dróg i Mostów

autor

Piaskiewicz M.

• Instytut Inżynierii Materiałów Polimerowych i Barwników Oddział Elastomerów i Technologii Gumy w Piastowie

Bibliografia

• [1] Block T., Eggert H., Kauschke W., Lager im Bauwesen. 3. Auflage, Wilhelm Ernst & Sohn, 2013.
• [2] Brandt A., O zastosowaniu łożysk kauczukowych w mostownictwie, Inż.i Bud., 3, s. 104-109, 1962.
• [3] Chabert A., Dauvilliers M., Durabilité des appareils d'appui en élastomère fretté, Bull.de liaison des lab.des ponts et chauss., No 129, s. 57-69, 1984.
• [4] Itoh Y., Gu H.S., Prediction of Aging Characteristics in Natural Rubber Bearings Used in Bridges, Journal of Bridge Engineering ASCE, March/April 2009, s. 122-128.
• [5] Lee D.J., Bridge Bearings and Expansion Joints, E & FN SPON 1994, s. 111-112.
• [6] Nakauchi H., Tanaka K., Yokoyama C., Miyazaki M., Yamazaki N., Characterization of a 100-year-old rubber bearing by microanalytical methods, J. Appl. Polym. Symp., 50, 1992, 360-375.
• [7] Niemierko A., Germaniuk K., Wpływ sztucznego starzenia i zamrażania na odkształcalność gumowych łożysk mostowych dużych nośności, Prace IBDiM, 1, s. 49-80, 1978.
• [8] Niemierko A., Bridge Bearings Durability and Reliability Factors, International Bridge Conference Warsaw’94, Road and Bridge Research Institute, s. 97-106, 1994.
• [9] Niemierko A., Rubber Bridge Bearings Test Results After 30 Years in Service, Fourth World Congress on Joint Sealants and Bearing Systems for Concrete Structures, ed. Barrie Atkinson, vol.2, ACI, SP 164-60, Sacramento, Ca (USA), 1996, s. 1199-1218.
• [10] Price A.R., Fenn M.A., Removal and testing of elastomeric bridge bearings, TRRL Report 812,Crowthome, 1983.
• [11] Topaloff B., Gummilager für Brücken - Berechnung und Anwendung, Der Bauingenieur, 39, 2, s. 50-64, 1964.
• [12] Watanabe Y., Kato A., Yoneda G., Hirotani T., Aging effects of forty years old laminated rubber bearings, Proc. 1st Aseismic and Resist Colloquium, JSCE, s. 439-446, Tokyo, 1996.
• [13] PN-EN 1337-3 Łożyska konstrukcyjne, Część 3: Łożyska elastomerowe.