Autoklawizowany beton komórkowy niezawierający cementu i siarczanów

Autorzy
Identyfikatory
Warianty tytułu
EN
Cement and sulphate free autoclaved aerated concrete
Języki publikacji
PL
Abstrakty
EN
New laws are likely which will make putting autoclaved aerated concrete (ACC) into landfills more difficult in the future. Consequently, a project was launched at Xella to reduce the sulphate content in AAC to almost zero. Positive side effects are no risk of thaumasite, agglomeration residue of lime and grey stains. The biggest source of sulphate besides cement is the pure calcium sulphate, which is added either as gypsum or anhydrite to the mixture. Additional calcium sulphate has been used in AAC to improve its material properties for many years. The reduction of calcium sulphate in ordinary cementitious AAC recipes leads to highs shrinkage and less compressive strength of the material. Sulphate free AAC with a low bulk density is not yet being made in mass production. Due to the lag of the hydraulic binder cement, completely sulphate free recipes could not be handled in technologies like Durox, Hebel or Ytong yet. Cement and sulphate free ACC cakes tend to collapse either in the demoulding or autoclaving process, and especially low densities are difficult to process. Technological solutions and recipes were found to produce cement and sulphate free AAC with low bulk densities in moulds with the size of 5,4 m 3 . The material meets the requirements for the German bulk density class PP2/0,35 with λ 0,09 W/(mK). The shrinkage tests show values under 0,20 mm/m according to to DIN EN 680. Finally, it was shown that cement free recipes lead to fewer transportation damages due to less brittle surfaces. Further research is currently in progress.
Rocznik
Tom
Strony
102--103
Opis fizyczny
Bibliogr. 3 poz., il., wykr.
Twórcy
autor
  • Xella Technologie- und Forschungsgesellschaft mbH, Niemcy
Bibliografia
  • [1] Clementi F., 1967. Verfahren zur Herstellung von darnpfgehärtetem Gasbeton, German patent, Aktenzeichen DE 16 46 580.8-45 (H 62442), Bundesrepublik Deutschland, Deutsches Patentamt.
  • [2] Straube B., Langer P., Stumm A., 2008. Durability of Autoclaved Aerated Concrete, 11DBMC International Conference on Durability of Building Materials and Components, Istanbul Turkey, May 11-14th.
  • [3] Züurn S. G., 1997. Einfluss der Sandminerale auf die Bildung von Calciumsilikathydraten (C-S-H-Phasen), das Gefüge und die mechanischen Eigenschaften von Porenbetonprodukten, Logos Verlag Berlin.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-15950f3a-0a7d-4bfe-ae2d-ea2712804e88
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.