Influence of long-term heating on the fatigue properties of low-alloyed cast steel STN 42 2707

• Autorzy: Bokuvka O. , Jambor M. , Novy F. , Trsko L. , Lago J
• Języki publikacji: EN

Abstrakty

EN

In this paper the authors publish own experimental results of examination of low-alloyed cast steel STN 42 2707 fatigue properties (near- threshold regime of fatigue crack propagation for rates from da/dN =5.6x10^-9m.cycle^-1 to da/dN =10^-12 m.cycle-1 and K_ath at da/dN =10^-12 m.cycle^-1) initial state and after long-term heating (T = 400 °C, t = 4000 hours ≈ 167 days) obtained at high-frequency loading (f ≈ 20 kHz, T= 20 ± 5 °C, R = -1). The long-term heating of material caused decrease of Kath and increase of fatigue crack growth rate in the near-threshold regime; then worse of low-alloyed cast steel STN 42 2707 fatigue properties.

Słowa kluczowe

EN

cast steel STN 42 2707; long-term heating; fatigue properties; Kath; da/dN = f(Ka)

PL

staliwa; własności zmęczeniowe; pęknięcie zmęczeniowe

• Wydawca: Oficyna Wydawnicza Stowarzyszenia Menedżerów Jakości i Produkcji
• Czasopismo: Production Engineering Archives
• Rocznik: 2016
• Tom: Vol. 12, No. 3
• Strony: 30--33
• Opis fizyczny: Bibliogr. 15 poz., rys.,tab.

Twórcy

autor

Bokuvka O.

• University of Žilina, Department of Materials Engineering, SK, phone: [phone]

autor

Jambor M.

• University of Žilina, Department of Materials Engineering, SK, phone: [phone]

autor

Novy F.

• University of Žilina, Department of Materials Engineering and Research Centre of University of Žilina, SK, phone: [phone]

autor

Trsko L.

• Research Centre of the University of Žilina, SK, phone: [phone]

autor

Lago J

• University of Žilina, Department of Materials Engineering, SK, phone: [phone]

Bibliografia

• 1. Bokůvka O. et al. 2002. Low and High Frequency Fatigue Testing. EDIS ŽU v Žiline.
• 2. Ulewicz R., Mazur M. 2013. Production Engineering Archives, No. 1, 32.
• 3. Trško L. et al. 2013. Dynamics Strength and Fatigue Lifetime. EDIS ŽU v Žiline.
• 4. Skočovský P. et al. 2015. Náuka o materiáli. EDIS ŽU v Žiline (in Slovak).
• 5. Kunz L. 2003. Experimentální stanoveníú na vových charakteristik materiálů. EDIS ŽU v Žiline (in Czech).
• 6. Ritchie R.O. 1981. Application of Fracture Mechanics to Fatigue Crack Propagation. University of California.
• 7. Letko I. et al. 2002. Priemyselné technológie II. EDIS ŽU v Žiline (in Slovak).
• 8. Skočovský, P. et al. 2000. Konštrukčné materiály. EDIS ŽU v Žiline (in Slovak).
• 9. Klesnil M., Lukáš P. 1975. Únavakovových material ůpři mechanickémnamáhání. ACADEMIA Praha (in Czech).
• 10. Hurtalová L. et al. 2013. Key Eng. Materials, Vol. 592-593, 433.
• 11. Bokůvka O. et al. 2015. Fatigue of Materials at Low and High-frequency Loading. EDIS ŽU v Žiline.
• 12. Puškár A. et al. 1987. Strojírenství, 2, 507 (in Slovak).
• 13. Trško L. et al. 2016. Production Engineering Archives, Vol. 10 (1).
• 14. Růžičková M. et al. 1999. Materiálové inžinierstvo, 6, 19 (in Slovak).
• 15. Píšek F. et al. 1975. Nauka o materiálu I., 4. svazek. ČAV Praha (in Czech).

Uwagi

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.