Application of Polyaniline for the Modification of Polylactide Fibres

• Autorzy: Połowiński S. , Szumilewicz J. , Stawski D.

Warianty tytułu

PL

Zastosowanie polianiliny do modyfikacji włókien z PLA

• Języki publikacji: EN

Abstrakty

EN

Polyaniline was deposited on a polylactide nonwoven by the in situ method in the form of emeraldine salt (Green Protonated Emeraldine), i.e. by oxidative polymerisation on the fibre surface. The nonwoven was also padded with a solution of Blue Emeraldine Base. Depending on the type of polyaniline (PANI) deposited, the resulting samples showed different conductance values. Changes in electrical resistance were assessed versus the procedure of final treatment. Thermogravimetric measurements showed an increase in the temperature of decomposition of about 50 °C compared to that of an unmodified sample. The nonwoven with the deposited layer of PANI was overlaid with a layer of complexing polymers by the layer-by-layer method. The effect of such a modification on the electro-conductive (resistance) and sorption properties of nonwovens was examined.

PL

Na włókninę z włókien polilaktydowych nanoszono polianilinę metodą in situ w postaci soli emeraldyny (Green Protonated Emeraldine), tj. przez polimeryzację oksydacyjną na powierzchni włókien, oraz napawano włókninę roztworem zasady emeraldyny (Blue Emeraldine Base). Stwierdzono różnice w przewodnictwie próbek w zależności od typu naniesionej polianiliny. Badano zmiany oporności elektrycznej w zależności od sposobu końcowej obróbki. Wykonano pomiary termograwimetryczne i stwierdzono wzrost temperatury rozkładu o koło 50 °C w porónaniu z prókąniemodyfikowaną Na włóninęz naniesionąwarstwąpolianiliny nakłdano warstwy polimeró kompleksująych metodą warstwa-po-warstwie (Layer-by-Layer). Zbadano wpłw takiej modyfikacji na włśiwośi elektroprzewodzące (oporność) i sorpcyjne.

Słowa kluczowe

EN

polylactide fibres; modification; polyaniline; polylactide nonwoven; layer-by-layer method; electrical resistance

PL

włókna polilaktydowe; modyfikacja; polianilina; polilaktyd włókniny; opór elektryczny; polimeryzacja oksydacyjna; metoda warstwa-po-warstwie (layer-by-layer)

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2011
• Tom: Vol. 19, no. 4 (87)
• Strony: 119--123
• Opis fizyczny: Bibliogr. 18 poz.,rys., wykr., tab.

Twórcy

autor

Połowiński S.

• Poland, Łódź, Technical University of Łódź, Department of Physical Chemistry of Polymers

autor

Szumilewicz J.

• Poland, Łódź, Technical University of Łódź, Department of Physical Chemistry of Polymers

autor

Stawski D.

• Poland, Łódź, Technical University of Łódź, Department of Physical Chemistry of Polymers

Bibliografia

• 1. Guimard N. K., Gomez N., Schmidt C. E.; Progr. Polym. Sci., 32 876 (2007) Conducting polymers in biomedical engineering.
• 2. Barthet Ch., Armes S. P., Lascelles S. F., Luk S. Y., Stanley H. M. E., Langmuir, 14 (8) 2032 (1998).
• 3. Barthet S., Armes P. Chehimi M. M. Bilem C. Omastova M.; Langmuir 14 5032 (1998).
• 4. Stejskal J., Sapurina I., Trchová M.: Progr. Polym. Sci. 35 1420 (2010).
• 5. Zhou J., Tzamalis G., Zaid N. A.,. Komfort N.P., Mpnkman A.P.; J. Appl. Polym. Sci., 79 2503 (2001).
• 6. Chacko A. P., Hardaker S. S., Gregory R. V., Samuels R. J.; Synthetic metals 84 41 (1997).
• 7. Rahman N. A., Gizdavic-Nikolaidis M., Ray S., Easteal A.J., Travas-Sejdic J. Synthetic Metals 160 (2010) 2015-2022.
• 8. Oh K. W., Hong K. W., Kim S. H.; J. Appl. Polym. Sci., 74 2094 (1999).
• 9. Chandran A. S. Narayanankutty S. K. ; Europ. Polym. J., 44 2418 (2008).
• 10. Patenty: US 4975317 (1991); US 5503508 (1991); US. CA 1315494 (1993); CA 1330024 (1994).
• 11. Fryczkowski R., Rom R., Fryczkowska B., Fibres Text. Eastern Europ; 13 141 (2005).
• 12. Stockton W.B., Rubner M.F.; Macromolecules 30 2717 (1997).
• 13. Połowiński S.; Polimery, 52 nr 5, 37-41 (2007).
• 14. Połowiński S., Jantas R., Stawski D.,Szumilewicz J.; FIBRES & TEXTILES inEastern Europe 2010, Vol. 18, No. 4 (81)pp. 87-91.
• 15. Mi-Kyoung Park, Onishi K., Locklin J.,Caruso F., Advincula R. C.; Langmuir 19 8550 (2003).
• 16. Ram M. K., Salerno M., Adami M., Faraci P., Nicolini C.; Langmuir 15 1252 (1999).
• 17. Hong-Quan Xie, Yong-Mei Ma, Jun-Shi Guo; Synthetic Metals 123 (2001) 47-52.
• 18. Kumar P., Adhikari S., Banerji P.; Synthetic Metals 160 (2010) 1507-1512.