Badanie składu fazowego oraz chemicznego proszków Bi1-xNdxFeO3 spiekanych swobodnie
Konferencja
Composites and Ceramic Materials - Technology, Application and Testing (13 ; 13-15.05.2013 ; Białowieża, Poland)
Języki publikacji
Abstrakty
In the present paper studies on Bi1-xNdxFeO3 for x =0.1-0.4 are reported. The mixed oxide method followed with pressureless sintering was employed for ceramics fabrication. Thermal behavior of stoichiometric mixtures of simple oxide powders, viz. Bi2O3, Nd2O3 and Fe2O3 was studied by simultaneous thermal analysis. It was found that with an increase in neodymium content the weight loss increased from 0.75% to 3.16% for x =0.1 and x =0.4, respectively. It was found that weight loss took place mainly within two temperature ranges, namely ΔT1 ≈(300-400)0C and ΔT2 ≈(600-800)°C. Bi1-xNdxFeO3 ceramics was studied in terms of its phase composition (X-ray phase analysis) and chemical composition (EDS method) at room temperature. It was found that Bi1-xNdxFeO3 suffered structural phase transition from rhombohedral to orthorhombic symmetry with an increase in neodymium concentration x within the range x =(0.2-0.3).
W niniejszej pracy zaprezentowano wyniki badań ceramiki Bi1-xNdxFeO3 dla x =0,1-0,4. Do wytworzenia ceramiki zastosowano metodę reakcji w fazie stałej z mieszaniny tlenków wyjściowych Bi2O3, Nd2O3 i Fe2O3 spiekanej swobodnie w atmosferze powietrza. Analiza termiczna stechiometrycznej mieszaniny proszków wykazała wzrost ubytku masy proszku przy wzroście zawartości (x) neodymu w mieszaninie (od 0,75% do 3,16% dla x =0,1 i x =0,4 odpowiednio). Stwierdzono, że ubytek masy zachodzi głównie w dwóch zakresach temperatury, a mianowicie ΔT1 ≈ (300-400)°C i ΔT2 ≈ (600-800)°C. Ceramika Bi1-xNdxFeO3 została poddana charakterystyce składu fazowego (rentgenowska analiza fazowa) oraz składu chemicznego (metoda EDS) w temperaturze pokojowej. Stwierdzono, że Bi1-xNdxFeO3 przejawia strukturalną przemianę fazową z fazy romboedrycznej do rombowej przy wzroście koncentracji neodymu w zakresie x =(0.2-0.3).
Wydawca
Czasopismo
Rocznik
Tom
Strony
1371--1376
Opis fizyczny
Bibliogr. 19 poz., rys., tab
Twórcy
autor
- University of Silesia, Department of Materials Science, 2 Śnieżna St., 41-200 Sosnowiec, Poland
autor
- University of Silesia, Department of Materials Science, 2 Śnieżna St., 41-200 Sosnowiec, Poland
autor
- University of Silesia, Department of Materials Science, 2 Śnieżna St., 41-200 Sosnowiec, Poland
autor
- University of Silesia, Department of Materials Science, 2 Śnieżna St., 41-200 Sosnowiec, Poland
Bibliografia
- [1] J. Wang, J. B. Neaton, H. Zheng, V. Nagarajan, S. B. Ogale, B. Liu, D. Viehland, V. Vaithyanathan, D. G. Schlom, U. V. Waghmare, N. A. Spaldin, K. M. Rabe, M. Wuttig, R. Ramesh, Epitaxial BiFeO3 multiferroic thin film heterostructures, Science 299, 1719 (2003).
- [2] A. Johari, Synthesis and characterization of bismuth ferrite Nnanoparticles, AKGEC Journal of Technology July-December 2, 2, 0975-9514 (2011).
- [3] A. Lisińska-Czekaj, Ł. Madej, J. Plewa, D. Czekaj, Otrzymanie i właściwości magnetyczne ceramiki multiferroicznej BiFeO3, Prace Komisji Nauk Ceramicznych - Polski Biuletyn Ceramiczny Ceramika/Ceramics 101, 223-228 (2008).
- [4] J. Dzik, H. Bernard, K. Osińska, A. Lisińska-Czekaj, D. Czekaj, Synthesis, structure and dielectric properties of Bi1-x Ndx Fe O3, Archives of Metallurgy and Materials 56, 4, 1119-1125 (2011).
- [5] Z. Dai, Y. Akishige, Electrical properties of multiferroic BiFeO3 ceramics synthesized by spark plasma sintering, Journal of Physics D: Applied Physics 43, 445403-445407 (2010).
- [6] S. M. Selbach, T. Tybell, M. A. Einarsrud, T. Grande, Size-dependent properties of multiferroic BiFeO3 nanoparticles, Chemistry of Materials. 19, 26, 6478-84 (2007).
- [7] Q. Jiang, C. Nan, Y. Wang, Y. Liu, Z. Shen, Synthesis and properties of multiferroic Bi Fe O3 ceramics, Journal of Electroceramics 21, 690-693 (2008).
- [8] R. Pandu, K. L. Yadav, A. Kumar, P. R. Reddy, A. Gupta, Effect of sintering temperature on structural and electrical properties Bi Fe O3 multiferroics, Indian Journal of Engeneering & Materials Sciences 17, 481-485 (2010).
- [9] S. H. Han, K. S. Kim, H. G. Kim, H. G. Lee, H. W. Kang, J. S. Kim, Ch. I. Cheon, Synthesis and characterization of multiferroic BiFeO3 powders fabricated by hydrothermal method, Ceramics International 36, 1365-1372 (2010).
- [10] J. K. Kim, S. S. Kim, W.-J. Kim, Solgel synthesis and properties of multiferroic BiFeO3, Materials Letters 59, 4006-4009 (2005).
- [11] M. S. Bernardo, T. Jardiel, M. Peiteado, A. C. Caballero, M. Villegas, Reaction pathways in the solid state synthesis of multiferroic BiFeO3, Journal of the European Ceramic Society 31, 3047-3053 (2011).
- [12] B. Wodecka-Duś, J. Dzik, H. Bernard, K. Osińska, A. Lisińska-Czekaj, D. Czekaj, Application of impedance spectroscopy for Bi1-x Ndx Fe O3 ceramics characterization, Materials Science Forum 730-732, 71-75 (2013).
- [13] G. L. Yuan, O. D. Siu-wing, L. Helen, W. Chan, Raman scattering spectra and ferroelectric properties of Bi1-x Ndx Fe O3 (x=0-0.2) multiferroic ceramics, Journal of Applied Physics 101, 064101 (2007).
- [14] MATCH! Version 2.x, CRYSTAL IMPACT, Postfach 1251, 53002 Bonn, Germany. (URL.: http://www.crystalimpact.com.matcg)
- [15] J. Rodriguez-Carvajal, Physica B. 192, 55 (1993); http://www.ill.eu/sites/fullprof.
- [16] W. Kraus, G. Nolze, Powder cell -aprogram for the representation and manipulation of crystal structures and calculation of the resulting X-ray powder patterns, Journal of Applied Crystallography 29, 301-303 (1996).
- [17] A. Lisińska-Czekaj, D. Czekaj, Synthesis of Bi5Ti Nb WO15ceramics, Archives of Metallurgy and Materials 54, 4, 869-874 (2009).
- [18] R. T. Downs, M. Hall-Wallace, The American Mineralogist Crystal Structure Database, American Mineralogist 88 (2003) 247-250; N. Niizek i, M. Wach i, The crystal structures of Bi2Mn4O10, Bi2Al4O9 and Bi2Fe4O9, Zeitschrift fur Kristallographie 127, 173-187 (1968).
- [19] C. R. Hubbard, E. H. Evans, D. K. Smith, The reference intensity ratio method for computer simulated powder patterns, J. Appl. Crystallogr. 169, 9, 169-174 (1976).
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-11084ff5-21e1-4383-81fa-37f9833ddd55