Effect of Laser Hardening of Steel on the Wear Process in an Abrasive Soil Mass

• Autorzy: Napiórkowski J. , Konat Ł. , Pietruszewska M.

Warianty tytułu

PL

Wpływ hartowania laserowego stali na proces zużywania w glebowej masie ściernej

• Języki publikacji: EN

Abstrakty

EN

This paper presents the results of tests for the effects of laser hardening on the course and intensity of wear of 38GSA (38MnSi4) and Hardox 600 steels in an abrasive soil mass. The tests were carried out under laboratory conditions, using a “rotating bowl” type machine. Two types of soil, i.e. light and medium, were used as the abrasive mass. Based on the obtained test results, it was found that hardness decreased (in relation to asdelivered condition). The performed laser surface hardening process significantly increased the abrasive wear resistance only for 38GSA (38MnSi4) steel. As regards to Hardox steel, the hardening treatment reduced the abrasive wear resistance index compared to the as-delivered condition of the steel.

PL

W pracy przedstawiono wyniki badań wpływu hartowania laserowego na przebieg i intensywność zużywania stali 38GSA (38MnSi4) i Hardox 600 w glebowej masie ściernej. Badania przeprowadzono w warunkach laboratoryjnych, wykorzystując maszynę typu „wirująca misa”. Masę ścierną stanowiły dwa rodzaje gleby: lekka i średnia. Na podstawie uzyskanych wyników badań stwierdzono, że twardość uległa zmniejszeniu (w stosunku do stanu dostarczenia). Przeprowadzenie procesu hartowania powierzchniowego laserem spowodowało wyraźne podwyższenie odporności na zużywanie ścierne jedynie stali 38GSA (38MnSi4). W odniesieniu do stali Hardox zabieg hartowania spowodował zmniejszenie wskaźnika odporności na zużywanie ścierne w stosunku do stanu dostarczenia tej stali.

Słowa kluczowe

EN

laser hardening; wear intensity; soil mass

PL

hartowanie laserowe; intensywność zużycia; masa glebowa

• Wydawca: Stowarzyszenie Inżynierów i Techników Mechaników Polskich
• Czasopismo: Tribologia
• Rocznik: 2018
• Tom: nr 4
• Strony: 63--69
• Opis fizyczny: Bibliogr. 9 poz., rys., tab., wykr.

Twórcy

autor

Napiórkowski J.

• University of Warmia and Mazury in Olsztyn, ul. Michała Oczapowskiego 2, 10-719 Olsztyn, Poland

autor

Konat Ł.

• Wrocław University of Technology, Wybrzeże Wyspiańskiego 27, 50-370 Wrocław, Poland

autor

Pietruszewska M.

• University of Warmia and Mazury in Olsztyn, ul. Michała Oczapowskiego 2, 10-719 Olsztyn, Poland

Bibliografia

• 1. Białobrzeska B., Kostencki P.: Abrasive wear characteristics of selected low-alloy boron steels as measured in both field experiments and laboratory tests, Wear 328–329 (2015), 149–159.
• 2. Napiórkowski J., Konat Ł., Kołakowski K.: Resistance to wear as a function of the microstructure and selected mechanical properties of microalloyed steel with boron. Tribologia 4/2016, 101–114.
• 3. Napiórkowski J., Konat Ł., Ligier K.: The structural properties and resistance to abrasive wear in soil of Creusabro steel. Tribologia 5/2016, 105–119.
• 4. Lemecha M., Napiórkowski J., Konat Ł.: Analysis of wear and tear of working elements with a replaceable cutting edge in an abrasive sill mass, Tribologia 302017, 101–109.
• 5. Pertek-Owsiana A., Kapcińska-Popowska D., Bartkowska A.: Obróbka cieplna objętościowa i powierzchniowa stali z mikrododatkiem boru, Inżynieria Materiałowa nr 5/2014, 401–404.
• 6. https://www.ssab.pl/produkty/marki/hardox/products/hardox600?accordion=downloads
• 7. Jędrusik A., Kupiec B., Koronievskyi M.: Sprawność cieplna procesu spawania przy użyciu lasera cienkich blach ze stopu Inconel 718. Conference materials, International Scientific Conference: „Klaster – Odlewnictwo – Przyszłość”, 09–12.09.2014.
• 8. BN-85/0642-48.
• 9. Konat Ł., Białobrzeska B., Białek P.: Effect of welding process on microstructural and mechanical characteristics of Hardox 600 steel. Metals, vol. 7, No 9, pp. 1–18, 2017.

Uwagi

Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2019).