Research on tribological properties of dental composite materials

• Autorzy: Dziedzic K. , Zubrzycka-Wróbel J. , Józwik J. , Barszcz M. , Siwak P. , Chałas R.

Identyfikatory

DOI

10.12913/22998624/65123

• Języki publikacji: EN

Abstrakty

EN

Dental practice today used a lot of different materials. This paper evaluates tribological and mechanical properties of two dental materials CeramX and I-Light. Tribological analysisad of samples was conducted at temperature 37°C and in the environment of artificial saliva. The wear rate was evaluated with a ball-on-disc tribotester, in accordance to ASTM G-133 norm. The counterbodies were 6-mm-in-diameter Al2 O3 steel balls. The load of 2, 10 and 20 N was applied. The tests were conducted at 0.15 m/s sliding velocity over a sliding stroke of 1000 m. The changes in the value of the following parameters were measured during the trials: friction coefficient, friction force, temperature and wear depth. After completing the tribological tests the surface of samples was carried out.

Słowa kluczowe

EN

dental materials; biotribology; friction coefficient; wear

• Wydawca: Lublin University of Technology ; Polish Society of Ecological Engineering (PTIE), Branch of PTIE in Lublin
• Czasopismo: Advances in Science and Technology. Research Journal
• Rocznik: 2016
• Tom: Vol. 10, nr 32
• Strony: 144--149
• Opis fizyczny: Bibliogr. 11 poz., fig.

Twórcy

autor

Dziedzic K.

• Department of Fundamental of Technology, Fundamentals of Technology Faculty, Lublin University of Technology, ul. Nadbystrzycka 38, 20-618 Lublin

autor

Zubrzycka-Wróbel J.

• Department of Conservative Dentistry and Endodontics, Medical University of Lublin, ul. Karmelica 7, 20-081 Lublin, Poland

autor

Józwik J.

• Department of Production Engineering, Mechanical Engineering Faculty, Lublin University of Technology, ul. Nadbystrzycka 38, 20-618 Lublin, Poland

autor

Barszcz M.

• Department of Fundamental of Technology, Fundamentals of Technology Faculty, Lublin University of Technology, ul. Nadbystrzycka 38, 20-618 Lublin

autor

Siwak P.

• Faculty of Mechanical Engineering and Management, Institute of Mechanical Technology, Poznań University of Technology, ul. Piotrowo 3, 60-965 Poznań, Poland

autor

Chałas R.

• Department of Conservative Dentistry and Endodontics, Medical University of Lublin, ul. Karmelica 7, 20-081 Lublin, Poland

Bibliografia

• 1. Mystkowska J., Dąbrowski J.R., Tribological characteristics of the kinematics couple: tooth – composite material for permanent dental fillings, Maintenance and reliability, Nr 3, 2010, 4–9.
• 2. Klaczewska J., Bieliński D.M., Friction and wear of resin-based dental materials, Archives of civil and mechanical engineering, Vol. 7, 2007, 87–96.
• 3. Ozwoniarek J., Wiśniewska-Weinert H., Leshchynsky V., Kędzia Ł. and Gierzyńska-Dolna M. Nowe rozwiązania w zakresie biotribologii i biomateriałów. Obróbka Plastyczna Metali, 17(3), 2006, 29–36.
• 4. Szafran M., Bobryk E., Szczęsna B. and Jałbrzykowski M. Wpływ dodatku nanowypełniacza na właściwości mechaniczne i tribologiczne kompozytów ceramiczno-polimerowych do zastosowań stomatologicznych. Kompozyty (Composites), 6, 2006, 83–87.
• 5. Walczak M. Wpływ wybranych zabiegów technologicznych na trwałość użytkową układów metalceramika stosowanych w protetyce stomatologicznej. Wydawnictwo Politechniki Lubelskiej, Lublin, 2014.
• 6. Jodkowska E. Materiały kompozycyjne: budowa, klasyfikacja i niektóre właściwości fizyko-chemiczne. Mag. Stom, 1, 1991, 4–7.
• 7. Grądzka-Dahlke M., Tokajuk G., Wilczko M., Pawińska M. and Stokowska W. Właściwości mechaniczne wybranych kompozytów stomatologicznych stosowanych do stabilizacji zębów, Kompozyty (Composites), 4, 2004, 326–330.
• 8. Andrzejczuk M., Lewandowska M. and Kurzydłowski K.J. Właściwości mechaniczne światłoutwardzalnych kompozytów zbrojonych mikro- i nanocząstkami. Kompozyty (Composites), 5, 2005, 75–79.
• 9. Hahnel S., Schultz S., Trempler C., Ach B., Handel G., Rosentritt M., Two-body wear of dental restorative materials, Journal of the mechanical behavior of biomedical materials, Vol. 4, 2011, 237–244.
• 10. Sajewicz E., Kulesza Z., A new tribometer for friction and wear studies of dental materials and hard tooth tissues, Tribology International, Vol. 40, 2007, 885–895.
• 11. Sajewicz E., On evaluation of wear resistance of tooth enamel and dental materials, Wear, Vol. 260, 2006, 1256–1261.

Uwagi

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.