Dependence of defect concentration, optical and photocatalytic properties of β-Ni(OH)2/ZnO and NiO/ZnO composite powders on phase transformation

Identyfikatory
Warianty tytułu
Języki publikacji
EN
Abstrakty
EN
β-Ni(OH)2/ZnO composite powders were successfully synthesized by hydrothermal method at 180 °C for 15 h whereas NiO/ZnO composite powders formed after the as-prepared powders were calcined at 800 °C for 1 h in air. The X-ray diffractometer (XRD), scanning electron microscope (SEM), UV-Vis spectrophotometer were used to characterize the phase, particle shape as well as size and optical properties, respectively. In this system, it was found that ZnO is a major phase while β-Ni(OH)2 and NiO are a minor phases. The altered particle shape of ZnO was influenced by addition of Ni(CH3COO)2ˑ6H2O whereas the particle shape of the minor phase was changed due to the calcination process. The optical band gap decreased when the amount of minor phase increased. For photocatalytic study, it was found that 6 mol% β-Ni(OH)2/ZnO composite powders exhibited the best decolorization of methylene blue aqueous solution.
Słowa kluczowe
Wydawca
Rocznik
Strony
219--227
Opis fizyczny
Bibliogr. 29 poz., tab., rys.
Twórcy
  • Department of Materials Science and Technology, Faculty of Science, Prince of Songkla University, Hat Yai, Songkhla 90110, Thailand
  • Center of Excellence in Nanotechnology for Energy (CENE), Prince of Songkla University, Hat Yai, Songkhla 90110, Thailand
  • Department of Materials Science and Technology, Faculty of Science, Prince of Songkla University, Hat Yai, Songkhla 90110, Thailand
  • Department of Materials Science and Technology, Faculty of Science, Prince of Songkla University, Hat Yai, Songkhla 90110, Thailand
  • Department of Chemistry and Center of Excellence for Innovation in Chemistry, Faculty of Science, Prince of Songkla University, Hat Yai, Songkhla 90110, Thailand
  • Center of Excellence in Nanotechnology for Energy (CENE), Prince of Songkla University, Hat Yai, Songkhla 90110, Thailand
Bibliografia
  • [1] KANT R., Nat. Sci., 4 (2012), 22.
  • [2] KLUBNUAN S., SUWANBOON S., AMORNPITOKSUK P., Opt. Mater., 53 (2016), 134.
  • [3] JIN Z., YANG D.L., ZHANG S.H., JIAN X.G., ChineseChem. Lett., 18 (2007), 1543.
  • [4] HAFIDI M., AMIR S., REVEL J.C., Proc. Biochem., 40 (2005), 2615.
  • [5] CHONG M.N., JIN B., CHOW C.W.K., SAINT C., Water Res., 44 (2010), 2997.
  • [6] SALAZAR-VILLANNUEVA M., CRUZ-LÓPEZ A., ZALDÍVAR-CADENA A.A., TOVAR-CORONA A., GUEVARA-ROMERO M.L., VAZQUEZ-CUCHILLO O., Mater. Sci. Semicond. Proc., 58 (2017), 8.
  • [7] YU C., WU Z., LIU R., HE H., FAN W., XUE S., J. Phys. Chem. Solids, 93 (2016), 7.
  • [8] DUO S., LI Y., LIU Z., ZHONG R., LIU T., Mater. Sci. Semicond. Proc., 56 (2016), 196.
  • [9] SCUDERI V., AMIARD G., BONINELLI S., SCALESE S., MIRITELLO M., SBEMA P.M., IMPELLIZZERI G., PRIVITERA V., Mater. Sci. Semicond. Proc., 42 (2016), 89.
  • [10] LU Y., SHANG H., SHI F., CHAO C., ZHANG X., ZHANG B., J. Phys. Chem. Solids, 85 (2015), 44.
  • [11] BARZEGAR M., HABIBI-YANGJEH A., BEHBOUDNIA M., J. Phys. Chem. Solids, 70 (2009), 1353.
  • [12] GOUTHAM S., KAUR S., SADASIVUNI K.K., BAL J.K., JAYARAMBABU N., KUMAR D.S., RAO K.V., Mater. Sci. Semicond. Proc., 57 (2017), 110.
  • [13] WANG M., XING C., CAO K., MENG L., LIU J., J. Phys. Chem. Solids, 75 (2014), 808.
  • [14] MARIN O., TIRADO M., BUDINI N., MOSQUERA E., FIGUEROA C., COMEDI D., Mater. Sci. Semicond. Proc., 56 (2016), 59.
  • [15] AHSANULHAQ Q., KIM S.H., HAHN Y.B., J. Phys. Chem. Solids, 70 (2009), 627.
  • [16] XU K., LIU C., CHEN R., FANG X., WU X., LIU J., Physica B, 502 (2016), 155.
  • [17] ZHANG X.L., DAI H.T., ZHAO J.L., WANG S.G., SUN X.W., Cryst. Res. Technol., 49 (2014), 220.
  • [18] HALL D.S., LOCKWOOD D.J., BOCK C., MACDOUGALL B.R., Proc. R. Soc. A., 471 (2016), 20140792.
  • [19] QIAO H., WEI Z., YANG H., ZHU L., YAN X., J. Nanomater., 2 (2009), 1.
  • [20] KOAO L.F., DEJENE F.B., TSEGA M., SWART H.C., Physica B, 480 (2016), 53.
  • [21] LUPAN O., CHOW L., CHAI G., ROLDAN B., NAITABDI A., SCHULTE A., HEINRICH H., Mater. Sci. Eng. B, 145 (2007), 57.
  • [22] ZAMIRI R., LEMOS A.F., REBLO A., AHANGAR H.A., FERREIRA J.M.F., Ceram. Int., 40 (2014), 523.
  • [23] TAKARKHEDE M.V., BAND S.A., NEMADE K.R., FADANAVIS S.A., Ceram. Int., 42 (2016), 1021.
  • [24] MALASHCHONAK M.V., STRELTSOV E.A., MAZANIK A.V., KULAK A.I., POZNYAK S.K., STROYUK O.L., KUCHMIY S.Y., GAIDUK P.I., Thin Solid Films, 589 (2015), 145.
  • [25] JULKAPLI N.M., BAGHERI S., HAMID S.B.A., Sci. World J., 24 (2014), 692307.
  • [26] CAI X., CAI Y., LIU Y., DENG S., WANG Y., WANG Y., DJERDJ I., Ceram. Int., 40 (2014), 57.
  • [27] KLUBNUAN S., AMORNPITOKSUK P., SUWANBOON S., Mater. Sci. Semicond. Proc., 39 (2015), 515.
  • [28] DAI P., YAN T.T., YU X.X., BAI Z.M., WU M.Z., Nanoscale Res. Lett., 11 (2016), 226.
  • [29] TKALYCH A.J., YU K., CARTER E.A., J. Phys. Chem. C, 119 (2015), 24315.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-0faf392d-0f66-43df-8004-c241549703ac
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.