Carbidic bainitic and ausferritic ductile cast iron

• Autorzy: Gumienny G.

Identyfikatory

DOI

10.2478/amm-2013-0125

Warianty tytułu

PL

Żeliwo sferoidalne bainityczne i ausferrytyczne z węglikami

• Języki publikacji: EN

Abstrakty

EN

This article presents new kinds of carbidic ductile cast iron with different microstructures of the metal matrix. This cast iron was obtained using the Inmold method nodularisation which guarantees strong refining of graphite and the metal matrix components. A different microstructure of the metal matrix of the cast iron was obtained without any thermal treatment (unwrought) by a suitable composition of alloy additives. It was shown that by adding molybdenum, chromium, nickel and copper it is possible to obtain in the cast iron metal matrix consisting of upper bainite, its mixture with lower bainite or ausferrite in the casts with the wall thickness of 3/25 mm. The process of cast iron crystallization is presented and described with the help of the thermal and derivative analysis (TDA) curves. It also shows the thermal effects from transformation of austenite in solid state.

PL

W arty kule przedstawiono nowe rodzaje żeliwa sferoidalnego z węglikami o różnej mikrostrukturze osnowy metalowej. Żeliwo to otrzymano stosując sferoidyzację metodą Inmold. zapewniającą dużą liczbę kulek grafitu i rozdrobnienie składników osnowy metalowej. Różną mikrostrukturę osnowy metalowej żeliwa otrzymywano bez stosowania obróbki cieplnej (w stanie surowym) poprzez odpowiednią kombinację ilościową dodatków stopowych. Wykazano, że dodatek molibdenu, chromu, niklu i miedzi w żeliwie sferoidalnym pozwala uzyskać osnowę metalową złożoną z bainitu górnego, jego mieszaniny z dolnym lub ausferrytu w odlewach o grubości ściany 3-25 mm. Proces krystalizacji żeliwa przedstawiono i opisano za pomocą krzywych analizy termicznej i derywacyjnej (ATD). Pokazano efekty cieplne od przemiany austenitu w stanie stałym.

Słowa kluczowe

EN

carbidic ductile cast iron; bainite; ausferrite; thermal and derivative analysis (TDA)

PL

węglik żeliwa sferoidalnego; bainit; ausferryt; analiza termiczno-derywacyjna (ATD)

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2013
• Tom: Vol. 58, iss. 4
• Strony: 1053--1058
• Opis fizyczny: Bibliogr. 8 poz., rys.

Twórcy

autor

Gumienny G.

• Department of Materials Engineering and Production Systems, Technical University of Łódź, 1/15 Stefanowskiego Str., 90-924 Łódź, Poland

Bibliografia

• [1] 44th Census of World Casting Production, Modern Casting, 16-19, December 2010.
• [2] E. Guzik, The processes of cast iron enrichment - selected problems, Archives of Foundry Engineering, 2001, Monograph No 1M [in Polish].
• [3] S. Pietrowski, Ductile iron with the structure of bainite with austenite or bainitic ferrite, Archives of Materials Science 4, 18, 253-273 (1997), [in Polish].
• [4] S. Pietrowski, G. Gumienny, Bainite obtaining in cast iron with carbides castings, Archives of Foundry Engineering 10, 1, 109-114 (2010).
• [5] G. Gumienny, Chromium and copper influence on the nodular cast iron with carbides microstructure, Archives of Foundry Engineering 10, 4, 47-54 (2010).
• [6] S. Pietrowski, G. Gumienny, Wear resistance of cast iron, Archives of Foundry Engineering 8, 3, 173-180 (2008).
• [7] S. Pietrowski, Influence of reaction chamber shape on the cast-iron spheroidization process in-mold, Archives of Foundry Engineering 10, 1, 115-122 (2010).
• [8] S. Pietrowski, G. Gumienny, B. Pisarek, T. Szymczak, R. Władysiak, The analysis of the correctness of the estimation of crystallization of the chosen alloys by the TDAmethod, High Quality Casting Technologies, Materials and Casts, collective work under the editorship of Stanisław Pietrowski, pp. 111-132, Katowice - Gliwice 2011, [in Polish].