Comparison of low and high frequency fatigue tests

• Autorzy: Vasko A. , Belan J. , Kucharikova L.

Identyfikatory

DOI

10.30657/pea.2017.17.03

• Języki publikacji: EN

Abstrakty

EN

The paper presents the results of low and high frequency fatigue tests carried out on nodular cast iron. The specimens of synthetic nodular cast irons from three different melts were studied in the high cycle fatigue region (from 10⁵ to 10⁸ cycles) using fatigue experimental equipments for low and high frequency cyclic loading. Low frequency fatigue tests were carried out at frequency f ≈ 120 Hz using the fatigue experimental machine Zwick/Roell Amsler 150HFP 5100; high frequency fatigue tests were carried out at frequency f ≈ 20 kHz using the ultrasonic fatigue testing device KAUP-ZU. Both fatigue tests were realised at sinusoidal cyclic push-pull loading (stress ratio R = –1) at ambient temperature (T = 20 ± 5 °C).

Słowa kluczowe

EN

fatigue test; low frequency cyclic loading; high frequency cyclic loading; nodular cast iron

PL

test zmęczeniowy; cykliczne obciążenie niskoczęstotliwościowe; cykliczne obciążenie o wysokiej częstotliwości; żeliwo sferoidalne

• Wydawca: Oficyna Wydawnicza Stowarzyszenia Menedżerów Jakości i Produkcji
• Czasopismo: Production Engineering Archives
• Rocznik: 2017
• Tom: Vol. 17
• Strony: 15--18
• Opis fizyczny: Bibliogr. 12 poz., rys., tab.

Twórcy

autor

Vasko A.

• University of Žilina, Faculty of Mechanical Engineering, Department of Materials Engineering, Univerzitná 8215/1, 010 26 Žilina, Slovakia

autor

Belan J.

• University of Žilina, Faculty of Mechanical Engineering, Department of Materials Engineering, Univerzitná 8215/1, 010 26 Žilina, Slovakia

autor

Kucharikova L.

• University of Žilina, Faculty of Mechanical Engineering, Department of Materials Engineering, Univerzitná 8215/1, 010 26 Žilina, Slovakia

Bibliografia

• 1. BORKOWSKI S., ULEWICZ R. 2009. Laboratorium z materiałoznastwa dla inżynierów. CWA Regina Poloniae, Częstochowa.
• 2. BOKŮVKA O., NICOLETTO G., KUNZ L., PALČEK P., CHALUPOVÁ M. 2002. Low & high frequency fatigue testing. EDIS, Žilina.
• 3. BOKŮVKA O., NICOLETTO G., GUAGLIANO M., KUNZ L., PALČEK P., NOVÝ F., CHALUPOVÁ M. 2014. Fatigue of materials at low and high fre-quency loading. EDIS, Žilina.
• 4. COPI K. W., LERNER Y. S., LAUKHIN N. S. 2003. SiC vs. 75% FeSi: Comparing pre-inoculation effects. Modern Casting 93, 29-31.
• 5. KONEČNÁ R., FINTOVÁ S. 2014. Metódy štúdia štruktúry. EDIS, Žilina.
• 6. SKOČOVSKÝ P., VAŠKO A. 2007. Kvantitatívne hodnotenie štruktúry liatin. EDIS, Žilina.
• 7. TRŠKO L., BOKŮVKA O., NOVÝ F., GUAGLIANO M. 2014. Effect of severe shot peening on ultra-high-cycle fatigue of a low-alloy steel. Materials and design 57, 103-113.
• 8. ULEWICZ R., TOMSKI P. 2017. The effect of high-frequencies loading on the fatigue cracking of nodular cast iron. Metalurgija 56, 33-36.
• 9. VAŠKO A., SKOČOVSKÝ P. 2014. Vlastnosti a použitie kovových materiálov. EDIS, Žilina.
• 10. VAŠKO A., VAŠKO M. 2016. Correlation between shape factor and mechanical properties of graphitic cast irons, Production Engineering Archives 11, 11-14.
• 11. VĚCHET S., KOHOUT J., BOKŮVKA O. 2001. Únavové vlastnosti tvárné litiny. EDIS, Žilina.
• 12. ZHANG W. H., DING J., NIE F. R. 2009. SiC inoculation pretreatment of cast iron. Foundry (Zhuzao) 58, 279-281.

Uwagi

Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).