Comparison and analysis of rotor-spun composite yarn and sirofil yarn

• Autorzy: Yang R.-H. , Xue Y. , Wang S.

Warianty tytułu

PL

Analiza i porównanie kompozytowych przędz rotorowych i przędz typu sirofil

• Języki publikacji: EN

Abstrakty

EN

As a result of various spinning types, different kinds of yarns have different structures and performances. In this research we developed a composite yarn spinning system that produces different kinds of composite yarns containing filament on a modified rotor spinning frame. Rotor-spun composite yarn and sirofil were produced by a modified rotor spinning machine and a modified ring spinning machine, respectively. Their longitudinal views, abrasion resistance, hairiness and breaking strength were tested and analyzed. The conclusion obtained was that, compared with sirofil, rotor-spun composite yarn has a smoother surface, less hairiness, higher abrasion resistance, lower breaking strength and better evenness.

PL

W wyniku stosowania różnych metod przędzenia otrzymuje się przędze zróżnicowane pod względem struktury, parametrów technicznych i jakości. W wyniku badań opracowano system przędzenia przędz kompozytowych na zmodernizowanej przędzarce, na której wyprodukowano rotorowe przędze kompozytowe i przędze typu sirofil. Testowano i analizowano następujące parametry wytworzonych przędz, zewnętrzny wygląd przędz, włochatość, wytrzymałość na ścieranie i wytrzymałość na zrywanie. W wyniku badań stwierdzono, że kompozytowe przędze rotorowe w porównaniu do przędz sirofil charakteryzują się gładszą powierzchnią, mniejszą włochatością, większą wytrzymałością na ścieranie, mniejszą wytrzymałością na zrywanie i lepszą równomiernością.

Słowa kluczowe

EN

sirofil; longitudinal view; abrasion resistance; hairiness; breaking strength; rotor-spun composite yarn

PL

sirofil; odporność na ścieranie; włochatość przędzy; wytrzymałość na zerwanie; rotorowe przędze kompozytowe

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2010
• Tom: Vol. 18, no. 1 (78)
• Strony: 28--30
• Opis fizyczny: Bibliogr. 15 poz., fig., tab.

Twórcy

autor

Yang R.-H.

• College of Textile, Donghua University, Shanghai, 201620, China
• Key Laboratory of Eco-Textiles (Jiangnan University), Ministry of Education, Wuxi, 214122, China

autor

Xue Y.

• College of Clothing and Art Design, Jiaxing University, Jiaxing, Zhejiang, 314001, China

autor

Wang S.

• College of Textile, Donghua University, Shanghai, 201620, China

Bibliografia

• 1. Wu X.Y., Wang F.M., Wang, S.Y., Textile Res. J., 73(4), 2003, pp. 305-309.
• 2. Sawhney A.P.S., Ruppenicker G.F., Kimmel L.B., Robert K.Q., Textile Res. J., 62(2), 1992, pp. 67-73.
• 3. Basu A., J. Textile Inst., 91(1), 2000, pp. 179-182.
• 4. Huh Y., Kim Y.R., Oxenham W., Textile Res. J., 72(2), 2002, pp. 156-163.
• 5. Koc E., Lawrence C.A., Iype C., Fibres &Textiles in Eastern Europe, 13(2), 2005, pp. 8-15.
• 6. Pouresfandiari F., Fushimi S., Sakaguchi A., Saito H., Toriumi K., Nishimatsu T., Shimizu Y., Shirai H., Matsumoto Y., Gong H., Textile Res. J., 72(1), 2002, pp. 61.
• 7. Matsumoto Y., Fushimi S., Saito H., Sakaguchi A., Toriumi K., Nishimatsu T., Shimizu Y., Shirai H., Morooka H., Gong H., Textile Res. J., 72(8), 2002, pp. 735.
• 8. Chou S.S., Jou G.T., Textile Asia, 1995(1), pp. 51-55.
• 9. Lord P.R., Grady P.L., Textile Res. J., 46(2), 1976, pp. 123.
• 10. Hearle J.W.S., Lord P.R., Senturk N., J. Textile Inst, 63(1972), pp. 605.
• 11. Lord P.R., Textile Res. J., 41(9), 1971, pp. 778.
• 12. Salhotra K.R, Dutta B & Scott S.K., Textile Res. J., 51(1981), pp. 360.
• 13. Yao Mu, Study of Textile Material, Chinese Publishing Company of Textile, Beijing, 2000, P56.
• 14. Shanyuan Wang, Xiuye Yu, New Textile Yarns. Publishing Company of Donghua University, 2007, P111.
• 15. China, Patent No.CN02136019.7, 2003.