Impact of the type of quench aging after hyperquenching on the mechanical strength properties of AW-7020 alloy

• Autorzy: Hajdukiewicz G.

Identyfikatory

DOI

10.5604/01.3001.0012.2791

• Języki publikacji: EN

Abstrakty

EN

The article attempts to determine the influence of selected types of the heat treatment on the strength properties of the AW-7020 alloy used in the shipbuilding industry. The text presents information on the applied types of heat treatment. There are presented the results of the static tensile test of the material after its earlier hyperquenching and aging (natural and artificial) as well as comparison to the test results of the alloy without heat treatment. To illustrate the nature of the supersaturation and aging process, a test was carried out for a series of samples in a transitional state. During the tests for all the samples were determined: elongation at rupture and reduction of area at fracture, strength limit Rm and proof stress Re0.2. The results of the tests showed that the choice of the type of aging after saturation has significant importance for the strength properties of the AW-7020 alloy. It has been shown that it is possible to significantly accelerate the achievement of higher strength properties of the tested alloy, replacing the natural aging of the material with artificial aging.

Słowa kluczowe

EN

AW-7020 alloy; age hardening; natural aging; artificial aging; hyperquenching strength limit; rupture elongation; fracture area reduction; intermediate state; age process hardening

• Wydawca: Łukasiewicz Research Network - Institute of Aviation ; European Science Society of Powertrain and Transport KONES Poland ; Wydawnictwo Instytutu Technicznego Wojsk Lotniczych
• Czasopismo: Journal of KONES
• Rocznik: 2018
• Tom: Vol. 25, No. 2
• Strony: 141--148
• Opis fizyczny: Bibliogr. 7 poz., rys.

Twórcy

autor

Hajdukiewicz G.

• Maritime University of Gdynia Department of Mechanical Engineering Morska Street 81-87, 81-225 Gdynia, Poland tel.: [phone], fax: [phone]

Bibliografia

• [1] Jurczak, W., Właściwości mechaniczne i korozyjne stopu AlZn5Mg1 po modyfikacji pierwiastkami stopowymi, Zeszyty Naukowe Akademii Marynarki Wojennej, Nr 3, p. 21, 2006.
• [2] Sabirov, I., Estrin, Y., Barnett, M. R., Timokhina, I., Hodgson, P. D., Enhaced tensile ductility of an ultra-fine-grained aluminium alloy, Scripta Materilia, Vol. 58, Iss. 3, pp. 163-166, 2008.
• [3] Dobrzański, L. A., Podstawy nauki o materiałach i metaloznawstwo, Wydawnictwa Naukowo-Techniczne, Gliwice 2002.
• [4] Kaufman, J. G., Rooy, E. L., Aluminium Alloy Castings: Properties, Processes and Applications, Ch. 3, pp. 21-37, 2004
• [5] Szklarz, Z., Wpływ odkształcenia plastycznego na korozję mikrostrukturalną stopów aluminium typu AlCu4Mg1 i AlMg2, Rozprawa doktorska, AGH, 2013.
• [6] Davis, J. R., Aluminium and Aluminium Alloys, Ohio 2004.
• [7] PN-ENISO 6892-1:2010, Metale, Próba rozciągania, Część 1, Metoda badania w temperaturze pokojowej, Polski Komitet Normalizacji, Warszawa 2010.

Uwagi

Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).