Structure and Mechanical Properties of AlMg4.5 and AlMg4.5Mn Wires Extruded by Kobo Method

• Autorzy: Jaskowski M. , Pieła K. , Błaż L.

Identyfikatory

DOI

10.2478/amm-2014-0078

Warianty tytułu

PL

Struktura i własności mechaniczne drutów AlMg4.5 i AlMg4.5Mn otrzymanych metodą KoBo

• Języki publikacji: EN

Abstrakty

EN

The influence of the number of extrusion steps in KoBo method (at the same total extrusion ratio of λ = 100) on structure, mechanical properties and work hardening characteristics of AlMg4.5 and AlMg4.5Mn (AA5083) alloys was investigated. It was found that one-step extrusion leads to the formation of recrystallised structure of the material, while the use of two-step extrusion yields a fibrous structure of a “mixed” type, i.e. containing areas where the intensive recovery effects are associated with partially recrystallised structure. As a consequence, the strength properties of the latter extrudate are much higher in both as extruded state and after the subsequent cold rolling. In all cases, the tensile stress-strain curves of the extrudates show the flow stress serrations that are typical for the Portevin - LeChatelier (P-L) effect. In a few tensile tests, the P-L effect was preceded by the plastic flow instability being typical for the occurrence of Lüders bands. Both AlMg4.5 and AlMg4.5Mn extruded wires show a monotonic increase of the work hardening that results from the following cold deformation in the groove rolling.

PL

W pracy badano wpływ liczby operacji wyciskania metodą KoBo (z identycznym sumarycznym stopniem przerobu λ = 100) na strukturę, własności mechaniczne i charakterystyki umocnieniowe drutów ze stopów AlMg4.5 i AlMg4.5Mn (AA5083). Stwierdzono, że wyciskanie jednooperacyjne prowadzi w przypadku obu stopów do formowania struktury typowej dla materia- łów zrekrystalizowanych. podczas gdy zastosowanie dwuoperacyjnego wyciskania skutkuje utworzeniem struktury włóknistej o charakterze „mieszanym”, tzn. zawierającej zarówno obszary, w których dominowały procesy intensywnego zdrowienia, jak i rekrystalizacji. W konsekwencji własności wytrzymałościowe tych ostatnich są zdecydowanie wyższe zarówno po wyciskaniu, jak i po późniejszym walcowaniu na zimno. We wszystkich przypadkach na krzywych rozciągania drutów obserwowano sko- kowe oscylacje naprężenia, charakterystyczne dla efektu Portevin - LeChatelier (P-L). W nielicznych próbach rozciągania efekt P-L poprzedzała niestateczność płynięcia plastycznego typowa dla występowania pasma LUdersa. Charakterystyki umocnienia wywołane procesem walcowania wykazywały przebieg monotonicznie rosnący.

Słowa kluczowe

EN

aluminium alloys; extrusion; KoBo method; structure; mechanical properties; work hardening

PL

stopy glinu; wytłaczanie; metoda KOBO; struktura; właściwości mechaniczne; hartowanie

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2014
• Tom: Vol. 59, iss. 2
• Strony: 473--479
• Opis fizyczny: Bibliogr. 17 poz., rys., tab.

Twórcy

autor

Jaskowski M.

• AGH University of Science and Technology, Department of Materials Science and Non- Ferrous Metals Engineering, Al. A. Mickiewicza 30, 30-059 Krakow, Poland

autor

Pieła K.

• AGH University of Science and Technology, Department of Materials Science and Non- Ferrous Metals Engineering, Al. A. Mickiewicza 30, 30-059 Krakow, Poland

autor

Błaż L.

• AGH University of Science and Technology, Department of Materials Science and Non- Ferrous Metals Engineering, Al. A. Mickiewicza 30, 30-059 Krakow, Poland

Bibliografia

• [1] A. Korbel, W. Bochniak, Method of plastic forming of materials. U.S.(1998). Patent No 5, 737, 959. Europen Patent No 737, 959.
• [2] A. Korbel, W. Bochniak, Scripta Mater. 51, 755 (2004).
• [3] K. Pieła, L. Błaż, M. Jaskowski, Arch. Metall. Mater. 58, 683 (2013).
• [4] A. Walocha, A. Korbel, W. Bochniak, P. Ostachowski, Rudyi Metale 54, 773 (2009).
• [5] L. Błaż, Dynamic structural processes in metals and alloys. Wyd. AGH, Kraków, 1998 (in Polish).
• [6] H. J. Mc Queen, S. Spigarelli, M. E. Kossener, E. Evangelista, Hot deformation and processing of aluminum alloys. CRC Press, Taylor & Francis Group LLC, USA, 2011.
• [7] M. Jaskowski, K. Pieła, L. Błaż, Rudyi Metale 59, 103 (2014).
• [8] W. Bochniak, K. Pieła, Method of manufacture of metal products with high mechanical properties. Patent Nr P-390 785 (2010).
• [9] B. Ren, W. A. Cassada, Deformation and recrystallization behaviors during hot rolling of 5182 alloy. 4th Int. Conf. Recrystallization and Related Phenomena. Japan, 1999.
• [10] Y. Miura, T. Shioyama, D. Hara, Mater. Sci. Forum 217-222, 505 (1996).
• [11] K. J. Gardner, R. Grimes, Met. Sci. 13, 216 (1979).
• [12] W. Blum, Q. Zhu, R. Merkel, H. J. McQueen, Z. Metallkde, 87, 14 (1996).
• [13] H. Dybiec, High temperature deformation of Al Mg4.5 alloy. Metallurgy and Foundry, vol. 136, Kraków, 1991 (in Polish).
• [14] F. C. Liu, Z. Y. Ma, Mater. Sci. Eng. A530, 548 (2011).
• [15] S. W. Lee, J. W. Ye h, Mater. Sci. Eng. A460-461, 409 (2007).
• [16] G. E. Totten, D. S. Mac Kenzie, Physical Metallurgy and Processes, Handbook of Aluminum, vol. 1, New York, Basel, Marcel Dekker Inc., 2003.
• [17] A. W. Brzostowicz, M. Jaskowski, W. Bochniak, K. Pieła, A. Brzostowicz, in press.