Microstructure and electromagnetic properties of microwave sintered CoCuZn ferrites

• Autorzy: Patankar K. K.
• Języki publikacji: EN

Abstrakty

EN

Co-Cu-Zn ferrite material has been extensively used in multilayer chip inductors because of their good electromagnetic properties at higher frequencies and low sintering temperatures. In this research work, a comparative study on Co-Cu-Zn ferrite prepared from two different routes is reported. The two different routes are conventional ceramic sintering method (CS) and is microwave sintered (MS) method. The former route is most commonly used while the latter one is now gaining popularity in sintering processes. The work highlights that the sintering temperature and time were significantly reduced from 4 h and 1250 °C for the CS process to 20 min and 900 °C for MS process. Moreover, microwave sintering also improves the physical and electromagnetic properties of ferrite.

Słowa kluczowe

EN

ferrite; microwave sintering; microstructure; electromagnetic; inductors

• Wydawca: Przedsiębiorstwo Wydawnictw Naukowych "DARWIN"
• Czasopismo: International Letters of Chemistry, Physics and Astronomy
• Rocznik: 2014
• Tom: Vol. 1
• Strony: 1--8
• Opis fizyczny: Bibliogr. 17 poz., rys., wykr.

Twórcy

autor

Patankar K. K.

• Department of Physics, Rajaram College, Kolhapur - 416 004, India

Bibliografia

• [1] T. Nakamura, J. Magn. Magn. Mater. 168 (1997) 285.
• [2] J. Y. Hsu, W. S. Ko, H. D. Shen, C. J. Chen, IEEE Trans. Magn. 30 (1994) 4875.
• [3] M. Fujimoto, J. Am. Ceram. Soc. 77 (11) (1994) 2873.
• [4] A. Goldstein, N. Travitzky, A. Singurindi, M. Kravchik, J. Eur. Ceram. Soc. 19 (1999) 2067.
• [5] C. Siligardi, C. Leonelli, F. Bondioli, A. Corradi, G. C. PellakaCo, J. Eur. Ceram. Soc. 20 (2000) 177.
• [6] A.C.F.M. Costa, E. Tortella, M.R. Morelli, R.H.G.A. Kiminami, J. Magn. Magn. Mater. 256 (2003) 174.
• [7] V. Tsakaloudi, E. Papazoglou, V. T. Zaspalis, Mater. Sci. Eng. B 106 (2004) 289.
• [8] M. Sorescua, L. Diamandescua, R. Peelamedu, R. Roy, P. Yadoji, J. Magn. Magn. Mater. 279 (2004) 195.
• [9] N. A. Travitzky, A. Goldstein, O. Avsian, A. Singurindi, Mater. Sci. Eng. A 2 (2000) 225.
• [10] J. Majling, P. Znasik, J. Cheng, D. Agrawal, R. Roy, J. Mater. Res. 10 (1995) 2411.
• [11] A. R. PhaCo, S. Santucci, J. Non-Cryst. Solids. 352 (2006) 4093.
• [12] W. Madhuri, M. Penchal Reddy, N. Ramamanohar Reddy, K. V. Siva Kumar, V. R. K. Murty, J. Phys. D: Appl. Phys. 42 (2009) 165007.
• [13] W. Madhuri, Ph.D Thesis, Srikrishnadevaraya UCoversity, Anatapur (2008) India.
• [14] Q. H. Yang, H. W. Zhang, Y. L. Liu, Q. Y. Wen, Mater Lett. 62 (2008) 2647.
• [15] A. Verma, D. C. Dube. J Am Ceram Soc 88 (2005) 519.
• [16] M. L. S. Teo, L. B. Kong, Z. W. Li, G.Q. Lin, Y. B. Gan. J Alloys Compd. 459 (2008) 567.
• [17] C. Y. Tsay, K. S. Liu, I. N. Lin, J. Europ. Ceram. Soc. 24 (2004) 1057.