Research on Extruded Products of MgAlZn Alloys – Microstructure and Mechanical Properties

• Autorzy: Płonka B. , Remsak K. , Korczak P. , Lech-Grega M. , Rajda M.

Identyfikatory

DOI

10.1515/amm-2015-0475

Warianty tytułu

PL

Badania wyrobów wyciskanych ze stopów MgAlZn – mikrostruktura i właściwości mechaniczne

• Języki publikacji: EN

Abstrakty

EN

The aim of the study was to test and assess products extruded from the magnesium alloys type MgAlZn: AZ31, AZ61 and AZ80A alloys in the form of Ø35mm round bars and 80x15mm flat bars. The test material was extruded in a direct system with the ram feed speed of 1 mm/s and the extrusion ratio λ = 7 ÷ 9. The extruded bars were examined in as-extruded state and after heat treatment to the T5 temper and T6 temper. The strength properties were tested and microstructure was examined with calculation of the average grain size.

PL

Praca miała na celu zbadanie wyrobów uzyskanych w procesie wyciskania stopów magnezu typu MgAlZn: AZ 31, AZ 61 oraz AZ 80A w postaci prętów Ø35mm oraz płaskowników 80x15mm. Materiał do badań został wyciśnięty w systemie współbieżnym z prędkością posuwu tłoka 1 mm/s, przy współczynniku wydłużenia λ=7÷9. Wyciśnięte pręty analizowano w stanie wyciskanym oraz po obróbce cieplnej do stanu T5 i T6. Zbadano ich właściwości wytrzymałościowe jak również poddano analizie mikrostruktury z określeniem średniej wielkości ziarna.

Słowa kluczowe

EN

magnesium alloy; extrusion; mechanical properties; structure

PL

stop magnezu; wyciskanie; właściwości mechaniczne; struktura

• Wydawca: Institute of Metallurgy and Materials Science of Polish Academy of Sciences ; Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences
• Czasopismo: Archives of Metallurgy and Materials
• Rocznik: 2015
• Tom: Vol. 60, iss. 4
• Strony: 2977--2980
• Opis fizyczny: Bibliogr. 10 poz., rys.

Twórcy

autor

Płonka B.

• Institute of Non-Ferrous Metals, Light Metals Division, 19 Piłsudskiego Str., 32-050 Skawina, Poland

autor

Remsak K.

• Institute of Non-Ferrous Metals, Light Metals Division, 19 Piłsudskiego Str., 32-050 Skawina, Poland

autor

Korczak P.

• Institute of Non-Ferrous Metals, Light Metals Division, 19 Piłsudskiego Str., 32-050 Skawina, Poland

autor

Lech-Grega M.

• Institute of Non-Ferrous Metals, Light Metals Division, 19 Piłsudskiego Str., 32-050 Skawina, Poland

autor

Rajda M.

• Institute of Non-Ferrous Metals, Light Metals Division, 19 Piłsudskiego Str., 32-050 Skawina, Poland

Bibliografia

• [1] Metals Handbook Ninth Edition, Metals Park, Ohio, Properties and Selection Nonferrous Alloys and Pure Metals 2,707-832 (1979).
• [2] S. Kleiner a, O. Beffort a, P.J. Uggowitzer, Microstructure evolution during reheating of an extruded Mg-Al-Zn alloy into the semisolid state, Scripta Materialia 51, 405-410 (2004).
• [3] E. F Volkova, Met. Sci. Heat. Treat. 48, 508-512 (2006).
• [4] T. Rzychoń, J. Szala, A. Kiełbus, Microstructure, castability, microstructural stability and mechanical properties of ZRE1 magnesium alloy, Archives of Metallurgy and Materials 57, 254-252 (2012).
• [5] R. Ye. Lapovok, M.R. Bernett, C.H.J. Davies, J.. Mater. Process. Tech. 146, 408-414 (2004).
• [6] T. Rzychoń, A. Kiełbus, L. Lityńska-Dobrzyńska, Microstructure, microstructural stability and mechanical properties of sand-cast Mg-4Al-4RE alloy, Materials Characterization 83, 21-34 (2013), doi: 10.1016/j. matchar.2013.06.001 (2013).
• [7] ASM Speciality Handbook, Magnesium and Magnesium Alloys, ASM International Materials Park, OH, 2004.
• [8] B. Płonka, K. Remsak, M. Nowak, M. Lech-Grega, P. Korczak, A. Najder, Arch. Metall. Mater. 59, 377-383 (2014).
• [9] B. Płonka, J. Kut, P. Korczak, M. Lech-Grega, M. Rajda, Arch. Metall. Mater. 57, 619-626 (2012).
• [10] B. Płonka, M. Lech-Grega, K. Remsak, P. Korczak, A. Kłyszewski, Arch. Metall. Mater. 58, 127-132 (2013).

Uwagi

PL

Opracowanie ze środków MNiSW w ramach umowy 812/P-DUN/2016 na działalność upowszechniającą naukę.