2006 | 36 | 3 | 536-547
Tytuł artykułu

Corrosion inhibitors for chlorides induced corrosion in reinforced concrete structures

Treść / Zawartość
Warianty tytułu
Języki publikacji
Reinforcements corrosion is the most important cause of premature failure on reinforced concrete structures. Phenomena promoting corrosion are the ingress of chlorides and the reaction of atmospheric CO 2 with cement paste. Aim of this paper is the investigation on the effectiveness of three organic commercial inhibitors in preventing carbon steel chlorides induced corrosion in concrete, since there is not yet a clear knowledge on the real effectiveness of these products. Inhibitors were added to the concrete mixture in dosage suggested by the manufacturers. Chlorides were added in the concrete mixture or penetrated from outside by “ponding” cycles with a 3.5% sodium chloride solution. The effectiveness of the inhibitors has been evaluated by long-term rebar corrosion monitoring in reinforced concrete and by rebar visual inspection after three years tests. Also solution tests were performed in order to verify the effectiveness of inhibition. Results give information about corrosion prevention ability of analysed commercial inhibitors.
Słowa kluczowe
Opis fizyczny
  • Dipartimento di Chimica, Materiali e Ingegneria Chimica “G. Natta” Politecnico di Milano, Via Mancinelli, 7-20131 Milano, Italy ,
  • CESI S.p.A., Via Rubattino, 20100 Milano, Italy
  • Dipartimento di Chimica, Materiali e Ingegneria Chimica “G. Natta” Politecnico di Milano, Via Mancinelli, 7-20131 Milano, Italy
  • Dipartimento di Progettazione e Tecnologie, Università di Bergamo, Viale Marconi 5, 24044 Dalmine (BG), Italy
  • 1. Bertolini, L.& Elsener, B.& Pedeferri, P.& Polder, R., "Corrosion of Steel in Concrete: Prevention, Diagnosis, Repair", 2004
  • 2. Page, C.L., "Nature and Properties of Concrete in Relation to Reinforcement Corrosion, Corrosion of Steel in Concrete, Aachen", 1992
  • 3. Elsener, B., Corrosion Inhibitors for Steel in Concrete — State of the Art Report, EFC Publications, vol. vol. 35, 2001
  • 4. Berke, N.S., Mater. Perform., vol. 28, 10, 1989, p.41-45
  • 5. Berke, N.S.& Weil, T.G., World-wide Review of Corrosion Inhibitors in Concrete; Advances in Concrete Technology, 1992, p.899-924
  • 6. Cigna, R.& Familiari, G.& Gianetti, F.& Proverbio, E., International Conference on Corrosion and Corrosion Protection of Steel in Concrete, Sheffield, 1994, p.878
  • 7. Callander, I.A.& Gianetti, F., "A rewiew on the use of C.N. corrosion inhibitor to improve the durability of reinforced concrete", The 2nd Annual Middle East Protection and Rehabilitation of Reinforced Concrete Conference, Dubai, 1996, p.1-12
  • 8. Berke, N.S.& Hicks, M.C., "Predicting long-term durability of steel reinforced concrete with calcium nitrite corrosion inhibitor", Cem. Concr. Compos., vol. 26, 2004, p.191-198
  • 9. Andrade, C.& Alonso, C.& Acha, M.& Malric, B., "Na2PO4F as inhibitor of corroding reinforcement in carbonated concrete", Cem. Concr. Res., vol. 26, 1996, p.405-415
  • 10. Ngala, V.T.& Page, C.L.& Page, M.M., "Corrosion inhibitor system for remedial treatment of reinforced concrete: Part 2. Sodium monofluoroposphate", Corros. Sci., vol. 45, 2003, p.1523-1537
  • 11. Raharinaivo, A.& Malric, B., "Performance of MFP for inhibiting corrosion of steel in reinforced concrete structures", International Conference on Corrosion and Rehabilitation of Reinforced Concrete Structures, 1998
  • 12. Mäder, U., "A new class of corrosion inhibitors for reinforced concrete", Concrete, vol. 9, 1999, p.215
  • 13. Gaidis, J.M., Cem. Concr. Compos., vol. 26, 2004, p.181-189
  • 14. Bjegovic, D.& Miksic, B., "Migrating corrosion inhibitor protection of concrete", Mater. Perform., vol. 11, 1999, p.52-56
  • 15. Wombacher, F.& Maeder, U.& Marazzani, B., "Aminoalcohol based mixed corrosion inhibitors", Cem. Concr. Compos., vol. 26, 2004, p.209-216
  • 16. Nmai, C.K.& Faci, P.E., "A critical review of corrosion inhibitors and their use in improving concrete durability in the middle east", 7th International Conference on Concrete in Hot and Aggressive Environment, Bahrain, 2003, Paper 14
  • 17. Elsener, B.& Büchler, M.& Stalder, F.& Böhni, H., "Migrating corrosion inhibitor blend for reinforced concrete: Part 1. Prevention of corrosion", Corrosion, vol. 55, 12, 1999, p.1155-1163
  • 18. Elsener, B.& Büchler, M.& Stalder, F.& Böhni, H., "Migrating corrosion inhibitor blend for reinforced concrete: Part 2. Inhibitor as repair strategy", Corrosion, vol. 56, 7, 2000, p.727-732
  • 19. Nmai, C.K.& Farrington, S.A.& Bobrowsky, G.S., "Organic based corrosion inhibiting admixtures for reinforced concrete", Concr. Int., vol. 14, 4, 1992, p.45-51
  • 20. Phanasgaonkar, A.& Cherry, B.& Forsyth, M., "Corrosion inhibition properties of organic amines in simulated concrete environment: mechanism", International Conference on Understanding Corrosion Mechanism in Concrete; a Key to Improve Infrastructure Durability, Cambridge, 1997
  • 21. Nmai, C.K., "Multi-functional organic corrosion inhibitor", Cem. Concr. Compos., vol. 26, 2004, p.199-207
  • 22. Cigna, R.& Mercalli, A.& Peroni, G.& Grisoni, L.& Mäder, U., "Influence of corrosion inhibitors containing aminoalcohols on the prolongation of service life of reinforced concrete", International Conference on Corrosion and Rehabilitation of Reinforced Concrete Structures, 1998
  • 23. de Rincon, O.T.& Perez, O.& Paredes, E.& Caldera, Y.& Urdaneta, C.& Sandoval, I., "Long-term performance of ZnO as a rebar corrosion inhibitor", Cem. Concr. Compos., vol. 24, 2002, p.79-87
  • 24. Sagoe-Crentsil, K.K.& Yilmaz, V.T.& Glasser, F.P., "Properties of inorganic corrosion inhibitors admixtures in steel-containing OPC mortars: chemical and electrochemical properties", Adv. Cem. Res., vol. 4, 1996, p.91-102
  • 25. Gonzales, J.A.& Ramirez, E.& Bautista, A., "Protection of steel embedded in chloride-containing concrete by means of inhibitor", Cem. Concr. Res., vol. 28, 1998, p.577-589
  • 26. Sagoe-Crentsil, K.K.& Glasser, F.P.& Yilmaz, V.T., "Corrosion inhibitors for mild steel; stannous tin in ordinary portland cement", Cem. Concr. Res., vol. 24, 1994, p.313-318
  • 27. Sagoe-Crentsil, K.K.& Yilmaz, V.T.& Glasser, F.P., "Corrosion inhibition of steel in concrete by carboxylic acids", Cem. Concr. Res., vol. 23, 1993, p.1380-1388
  • 28. Monticelli, C.& Frignani, A.& Trabanelli, G., "A study on corrosion inhibitors for concrete application", Cem. Concr. Res., vol. 30, 2000, p.635-642
  • 29. Saraswathy, V.& Muralidharan, S.& Kalyanasundaram, R.M.& Thangavel, K.& Srinivasan, S., "Evaluation of a composite corrosion-inhibiting admixture and its performance in concrete under macrocell corrosion conditions", Cem. Concr. Res., vol. 31, 2001, p.789-794
  • 30. Bolzoni, F.& Fumagalli, G.& Lazzari, L.& Ormellese, M.& Pedeferri, M.P.& Fontana, F., "Inhibition Effect of Organic Molecules on Carbon Steel Corrosion in Alkaline Solution with Chlorides, European Corrosion Congress Eurocorr, Riva del Garda, Italy", 2001
  • 31. Collepardi, M.& Fratesi, R.& Moriconi, G.& Corradetti, C.& Coppola, L., "Use of nitrite salt as corrosion inhibitor admixtures in reinforced concrete structures immersed in sea-water", Vazquez (Eds.), Proceeding of the International RILEM Symposium on Admixtures for concrete—Improvement of Properties, Barcellona, 1990, p.279-288
  • 32. R. Fratesi, G. Moriconi, S. Simoncini, Corrosione delle armature di acciaio nel calcestruzzo fessurato immerso in acqua di mare, Giornate nazionali sulla corrosione e protezione, 2° Edition, AIM, Milan (1994) 39–148 (in Italian).
  • 33. Hansson, C.M.& Mammoliti, L.& Hope, B.B., "Corrosion inhibitors in concrete: Part II. Effect of chloride threshold values for corrosion of steel in synthetic pore solution", Cem. Concr. Res., vol. 29, 1999, p.1583
  • 34. Trepanier, S.M.& Hope, B.B.& Hansson, C.M., "Corrosion inhibitors in concrete: Part III. Effect on time to chloride-induced corrosion initiation and subsequent corrosion rates of steel in mortar", Cem. Concr. Res., vol. 31, 2001, p.713-718
  • 35. Pazini, E.& Leao, S.& Estefani, G., "Corrosion inhibitors. Behaviour of NaNO2 and amine-based products in the prevention and control of corrosion in reinforced concrete", NACE International Corrosion Conference, Latin–American Congress, Cancun, 1998, p.134-143
  • 36. Mammoliti, L.& Brown, L.& Hansson, C.M.& Hope, B.B., "The influence of surface finish of reinforcing steel and pH of the test solution on the chloride threshold concentration for corrosion initiation in synthetic pore solution", Cem. Concr. Res., vol. 26, 1996, p.545-550
  • 37. CEN ENV 197/1 Standard, Cement: Part 1. Composition, specifications and conformity criteria for common cements, 2000.
  • 38. ASTM C 876-91, Standard test method for half-cell potential of reinforcing steel in concrete, Annual Book of ASTM Standards, ASTM International, West Conshohocken, PA 19428-2959, USA, 1991, reapproved 1999.
  • 39. Stern, M.& Geary, A.L., "Electrochemical polarisation I: a theoretical analysis of the slope of polarisation curves", J. Electrochem. Soc., vol. 104, 1957, p.56-63
  • 40. Andrade, C.& Gonzalez, J.A., "Quantitative measurements of corrosion rate of reinforcing steels embedded in concrete using polarization resistance measurements", Werkst. Korros., vol. 29, 1978, p.519
  • 41. González, J.A.& Molina, A.& Escudero, M.L.& Andrade, C., "Errors in the electrochemical evaluation of very small corrosion rates: I. Polarization resistance method applied to corrosion of steel in concrete", Corros. Sci., vol. 25, 1985, p.917
  • 42. Andrade, C., "Determination of chloride threshold in concrete", COST 521 Workshop, Luxembourg, 2002, p.108
  • 43. UNI 9944 (Italian Standard), Corrosione e protezione dell'armatura nel calcestruzzo. Determinazione della profondità di carbonatazione e del profilo di penetrazione degli ioni cloruro nel calcestruzzo, 1992.
  • 44. Hetek, "Chloride penetration into concrete", State of the art report, Report n. 53, The Road Directorate, Copenaghen, 1996
  • 45. Gonzalez, J.A.& Feliu, S.& Rodriguez, P.& Ramirez, E.& Alonso, C.& Andrade, C., "Some questions on the corrosion of steel in concrete: when, how and how much steel corrodes", Mat. Struct., vol. 29, 1996, p.40-46
Typ dokumentu
Identyfikator YADDA
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.