Tytuł artykułu

Blended Rotor - Spun Yarns with a High Proportion of Flax

Wybrane pełne teksty z tego czasopisma
Warianty tytułu
PL
Bezwrzecionowe przędze mieszankowe z wysokim udziałem lnu
Języki publikacji
EN
Abstrakty
EN
We present the results of tests on rotor-spun blended yarns, made with a high proportion of flax, and rotor-spun all-cotton yarns. Of special concern was the method of preparing the fibres and sliver. The flax/cotton sliver was made up of medium-long cotton, and the flax fibre was shortened and reduced in diameter by mechanical cottonising. The basic composition of the flax/cotton sliver was 30% cotton and 70% mechanically cottonised flax. The optimum linear density of the yarns was 40 tex. The experiments enabled the optimum values of twist and linear density to be found, at which the quality parameters of the yarns produced were acceptable. In addition, a comparative analysis of the produced cotton yarn and flax/cotton yarn was made. The flax/cotton yarn with a high proportion of flax is suitable for both weaving and knitting.
PL
Przedstawiono wyniki badań przędz mieszankowych z wysokim udziałem lnu i czysto bawełnianych otrzymanych w procesie przędzenia bezwrzecionowego. Zwrócono szczególną uwagę na sposób przygotowania włókien i taśm. Taśmy lniano-bawełniane przygotowano z bawełny średniowłóknistej i włókien lnianych skróconych i pocienionych w procesie mechanicznej kotonizacji. Taśmy lniano-bawełniane posiadały podstawowy skład: 30% włókien wełny i 70% włókien lnianych po mechanicznej kotonizacji. Optymalna masa liniowa przędz wynosi minimum 40 tex. Przeprowadzone badania doprowadziły do ustalenia optymalnych wartości skrętu i mas liniowych, dla których otrzymano dobre parametry jakościowe przędz. Dokonano także analizy porównawczej przędz bawełnianych z przędzami mieszankowymi len-bawełna. Przędze bezwrzecionowe mieszankowe z wysokim udziałem lnu mogą być wykorzystane zarówno w procesach tkackich, jak i dziewiarskich.
Wydawca

Rocznik
Tom
Strony
80--83
Opis fizyczny
Bibliogr. 10 poz., rys., tab.
Twórcy
  • Institute of Natural Fibres, ul. Wojska Polskiego 71 b, 60-680 Poznań, Poland
  • Institute of Natural Fibres, ul. Wojska Polskiego 71 b, 60-680 Poznań, Poland
  • Institute of Natural Fibres, ul. Wojska Polskiego 71 b, 60-680 Poznań, Poland
  • Institute of Natural Fibres, ul. Wojska Polskiego 71 b, 60-680 Poznań, Poland
autor
  • Zamatex Sp. z o.o., ul. Rembielińskiego 16/18, 93-575 Łódź, Poland
autor
  • Zamatex Sp. z o.o., ul. Rembielińskiego 16/18, 93-575 Łódź, Poland
Bibliografia
  • 1. W. Cierpucha, J. Mańkowski, J. Waśko, T. Mańkowski, S. Zaręba, J. Szporek: ‘Application of mechanically cottonised flax and hemp to rotor spinning.’ Fibres & Textiles in Eastern Europe, No2, 2002, p. 32.
  • 2. W. Cierpucha, R. Kozłowski, J. Mańkowski, J. Waśko, T. Mańkowski: ‘Suitability of flax and hemp for the production of cotton-type fibre and blended yarns.’ Fibres & Textiles in Eastern Europe, No3, 2004, p. 13.
  • 3. W. Cierpucha, S. Zaręba, J. Mańkowski, J. Szporek: ‘Utilitarian values of products made from cotton/flax and cotton/hemp blends’ (in Polish). Przegląd Włókienniczy – November 2001, p. 15.
  • 4. J. Mańkowski, W. Cierpucha, J. Kołodziej: ‘Modification of flax and hemp to spinning in blend with other fibres’ (in Polish). Spektrum Tekstylno-Włókiennicze 3/2005, p. 23.
  • 5. W. Ankudowicz, J. Wróblewski: ‘Preparation of flax fibres and spinning with cotton’, Research Reports of the Textile Research Institute, vol. XXX, Łódź, Poland.
  • 6. T. Jackowski, J. Czekalski, B. Chylewska, D. Cyniak: ‘Yarn blends hemp-cotton’ (in Polish), Proceedings of the Textile Faculty Conference, Technical University of Łódź, March, 2000.
  • 7. J. Czekalski, K. Patejuk: ‘The Effect of Flax Fibre Modification on the Quality of Linen/Cotton-Blended Yarn’, Przegląd Włókienniczy, No. 10/1999, pp.11.
  • 8. T. Jackowski, B. Chylewska, D. Cyniak, J. Czekalski: ‘Tensile Strength of Untwisted Blended Cotton/Flax Fibre Streams’, Fibres & Textiles in Eastern Europe, vol. 11, No. 3(42)2003.
  • 9. T. Jackowski, B. Chylewska, D. Cyniak, J. Czekalski, L. Jackowska-Strumiłło: ‘Modelling of the Relationship Between Feeding Sliver Structures and Parameters of Cotton/Linen Blended Yarns’, Fibres & Textiles in Eastern Europe, vol. 11, No. 2(41)2003.
  • 10. J. Czekalski, T. Jackowski, I. Krucińska: ‘Analysis of the Manufacturing Process of Blended Fine Yarns with the Content of Flax Fibres’, Fibres & Textiles in Eastern Europe, vol. 8, No. 2(29)2000.
Typ dokumentu
Bibliografia
Identyfikatory
Identyfikator YADDA
bwmeta1.element.baztech-d59c4b4b-4a46-4d90-8e50-473bd3b7da8e
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.