2012 | Vol. 48, iss. 1 | 103-112
Tytuł artykułu

Adsorption of c.i. basic blue 9 onto TiO2-SiO2 inorganic support

Wybrane pełne teksty z tego czasopisma
Warianty tytułu
Języki publikacji
Adsorption of C.I. Basic Blue 9 (Methylene Blue Hydrate) on the surface of TiO2-SiO2 oxide composite unmodified or functionalized with N-2-(aminoethyl)-3-amino propyltrimethoxsysilane was investigated. The organic dye was supported on inorganic TiO2-SiO2 oxide composite precipitated in the emulsion system. The process of adsorption was performed for the dye concentrations from 100 to 3000 mg/dm3. Specific surface area of support was determined prior to and after modification with aminosilane. The pigments obtained were subjected to characterization of their physicochemical properties, including particle size distributions and surface morphology as well as colorimetric analysis. Elemental analysis allowed evaluation of the degree of support coverage with the dye. The data obtained permitted assessment of the pigments quality and the effectiveness of support surface modification.

Opis fizyczny
Bibliogr. 24 poz.
  • 1. ANDRZEJEWSKA A., KRYSZTAFKIEWICZ A., JESIONOWSKI T., 2007, Treatment of textile dye wastewater using modified silica, Dyes Pigments, 75, 116–124.
  • 2. ANDRZEJEWSKA A., KRYSZTAFKIEWICZ A., JESIONOWSKI T., 2004, Adsorption of organic dyes on the aminosilane modified TiO2 surface, Dyes Pigments, 62, 121–130.
  • 3. BERENDSEN G.E., de GOLAN L., 1978, Preparation and chromatographic properties of some chemically bonded phases for reversed-phase liquid chromatotography, J. Liq. Chromatogr., 1, 561–586.
  • 4. BINKOWSKI S., JESIONOWSKI T., KRYSZTAFKIEWICZ A., 2000, Preparation of pigments on modified precipitated silica, Dyes Pigments, 47, 247–257.
  • 5. CHO K., CHANG H., PARK J.H., KIM B.G., JANG H.D., 2008, Effect of molar ratio of TiO2/SiO2 on the properties of particles synthesized by flame spray pyrolysis, J. Ind. Eng. Chem., 14, 860–863.
  • 6. CIESIELCZYK F., JESIONOWSKI T., 2011, Characterization of highly dispersed magnesium silicates prepared from silica sols and selected magnesium salts, Physicochem. Probl. Miner. Process. 46, 279–288.
  • 7. DUTOIT D.C.M., SCHNEIDER M., BAIKER A., 1995, Titania-silica mixed oxides: I. Influence of sol-gel and drying conditions on structural properties, J. Catal., 153, 165–176.
  • 8. HARRIS R.G., WELLS J.D., JOHNSON B.B., 2001, Selective adsorption of dyes and other organic molecules to kaolinte and oxide surfaces, Colloids Surf. A, 180, 131–140.
  • 9. JESIONOWSKI T., KRYSZTAFKIEWICZ A., 2000, Comparison of the techniques used to modify amorphous hydrated silicas, J Non-Cryst. Solids, 277, 45–57.
  • 10. JESIONOWSKI T., 2002, Synthesis of organic-inorganic hybrids via adsorption of dye on the aminosilane-functionalised silica surface, Dyes Pigments, 55, 133–141.
  • 11. JESIONOWSKI T., POKORA M., TYLUS W., DEC A., KRYSZTAFKIEWICZ A., 2003, Effect of N-2-(aminoethyl)-3-aminopropyltrimethoxysilane surface modification and C.I. Acid Red 18 dye adsorption on physicochemical properties of silicas precipitated in an emulsion route, used as a pigment and filler in acrylic paints, Dyes Pigments, 57, 29–41
  • 12. JESIONOWSKI T., ANDRZEJEWSKA A., KRYSZTAFKIEWICZ A., 2008, Adsorption of basic dyes from model aqueous solutions onto novel spherical silica support, Color. Technol., 124, 165–172.
  • 13. JESIONOWSKI T., KRYSZTAFKIEWICZ A., ŻURAWSKA J., BULA K., 2009, Novel precipitated silicas – an active filler of synthetic rubber, J. Mater Sci., 44, 759–769.
  • 14. JESIONOWSKI T., 2009, Preparation of spherical silica in emulsion systems using the co-precipitation technique, Mater. Chem. Phys., 113, 839–849.
  • 15. JESIONOWSKI T., PRZYBYLSKA A., KURC B., CIESIELCZYK F., 2011, The preparation of pigment composites by adsorption of C.I. Mordant Red 11 and 9-aminoacridine on both unmodified and aminosilane-grafted silica supports, Dyes Pigments, 88, 116–124.
  • 16. LIU Y., GE Ch., REN M., YIN H., WANG A., ZHANG D., LIU Ch., CHEN J., FENG H., YAO H., JIANG T., 2008, Effects of coating parameters on the morphology of SiO2-coated TiO2 and the pigmentary properties, Appl. Surf. Sci., 254, 2809–2819.
  • 17. MALIK D.J., STRELKO Jr. V., STREAT M., PUZIY A.M., 2002, Characterisation of novel modified active carbons and marine algal biomass for the selective adsorption of lead, Water Res., 36, 1527–1538.
  • 18. MESSINA V.P., SCHULTZ C.P., 2006, Adsorption of reactive dyes on titania-silica mesoporous materials, J. Colloid Interface Sci., 299, 305–320.
  • 19. PARK J.-K., KIM J.-K., KIM H.-K., 2007, TiO2–SiO2 composite filler for thin paper, J. Mater. Process. Tech., 186, 367–369.
  • 20. PILARSKA A., JESIONOWSKI T., 2011, Synthesis of MgO in magnesium hydroxide carbonatization process, Physicochem. Probl. Miner. Process. 46, 83–94.
  • 21. SIWINSKA-STEFANSKA K., KRYSZTAFKIEWICZ A., CIESIELCZYK F., PAUKSZTA D., SOJKA-LEDAKOWICZ J., JESIONOWSKI T., 2010, Physicochemical and structural properties of TiO2 precipitated in an emulsion system, Physicochem. Probl. Miner. Process. 44, 231–244.
  • 22. SIWINSKA-STEFANSKA K., PRZYBYLSKA A., JESIONOWSKI T., SOJKA-LEDAKOWICZ J., OLCZYK J., WALAWSKA A, 2010, Wpływ kompozytu tlenkowego TiO2-SiO2 na właściwości barierowe wyrobów włókienniczych, Przem. Chem., 89, 1661–1666.
  • 23. VALVARDE-AGUILAR G., GARCIA-MACEDO J.A., RENTERIA-TAPIA V., 2011, Photoconductivity studies of gold nanoparticles supported on amorphous and crystalline TiO2 matrix prepared by sol-gel method, Rev. Mex. Fis. 57, 13–18.
  • 24. WU F.-C., TSENG R.-L., 2006, Preparation of highly porous carbon from fir wood by KOH etching and CO2 gasification for adsorption of dyes and phenols from water, J. Colloid Interface Sci., 294, 21–30.
Typ dokumentu
Identyfikator YADDA
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.