Tytuł artykułu

Reduction of formaldehyde emission from plywood bonded with modified UF adhesive

Warianty tytułu
PL
Redukcja emisji formaldehydu ze sklejki klejonej modyfikowaną żywicą mocznikową
Języki publikacji
EN
Abstrakty
EN
Chemical stability of UF adhesives is an important hygienic property. This paper deals with chemical stability of UF adhesives modified with glutaraldehyde (GA) and collagen. GA was added to the adhesive to increase the structural stability of the adhesive. Collagen was added in the form of acid hydrolysate; the hydrolysate is chrome tanned leather waste. Formaldehyde content in plywood was measured through FESYP method; and formaldehyde emission from cured UF adhesive film was measured through “chamber method” according to the STN 49 0030 and STN EN 717-1 standards. The results showed that simultaneous presence of collagen and GA in the UF adhesive mixture reduced the amount of formaldehyde in plywood, and reduced the formaldehyde emission from cured UF adhesive film, as well.
PL
Redukcja emisji formaldehydu ze sklejki klejonej modyfikowaną żywicą mocznikową. Stabilność chemiczna żywicy mocznikowej stanowi jej istotną własność higieniczną. Praca dotyczy stabilności chemicznej kleju mocznikowego modyfikowanego aldehydem glutarowym oraz kolagenem. Aldehyd glutarowy został dodany do kleju w celu zwiększenia stabilności strukturalnej. Kolagen został dodany w formie hydrolizatu kwasowego, pochodzącego z odpadów po garbowaniu skór. Zawartość formaldehydu zmierzono zgodnie z normami STN 49 0030 oraz STN EN 717-1. Wykazano, że równoczesna obecność kolagenu oraz GA w żywicy mocznikowej zmniejsza ilość formaldehydu oraz redukuje jego emisję z utwardzonej żywicy.
Słowa kluczowe
Wydawca
-
Rocznik
Tom
76
Opis fizyczny
p.44-48,fig.,ref.
Twórcy
  • Technical University, T.G. Masaryka, 24, 960 53 Zvolen, Slovakia
autor
  • Technical University, T.G. Masaryka, 24, 960 53 Zvolen, Slovakia
  • VIPO a.s., ul. Gen Svobodu 1069/4, 958 01 Partizanske, Slovakia
autor
  • VIPO a.s., ul. Gen Svobodu 1069/4, 958 01 Partizanske, Slovakia
Bibliografia
  • 1. LANGMAIER, F. et al. 2004. Curing of urea-formaldehyde adhesives with collagen type hydrolysates under acid condition. In Journal of Thermal Analysis and Calorimetry. 2004, 76, p. 1015-1023.
  • 2. LANGMAIER, F. et al. 2005. Curing urea-formaldehyde adhesives with hydrolysates of chrome-tanned leather waste from leather production. In International Journal of Adhesion and Adhesives. 2005, 25, p. 101-108.
  • 3. MAMINSKI, M.L., PAWLICKI, J., PARZUCHOWSKI, P. 2006. Improved water resistance and adhesive performance of a commercial UF resin blended with glutaraldehyde. In The Journal of Adhesion. ISSN 0021-8464, 2006, 82, p.629-641.
  • 4. PARK, B.D., LEE, S.M., ROH J.K. 2009. Effects of formaldehyde/urea mole ratio and melamine content on the hydrolytic stability of cured urea-melamine-formaldehyde resin. In Eur. J. Wood. Prod. 2009, 67, p. 121–123.
  • 5. RINGENA, O. et al. 2006. Estimating the hydrolytic durability of cured wood adhesives by measuring formaldehyde liberation and structural stability. In Holz als Roh- und Werkstoff. 2006, 64, p. 321–326.
  • 6. STN EN 120: 1995: Drevné materiály. Zisťovanie obsahu formaldehydu. Extrakčný postup zvaný „perforátorová metóda“.
  • 7. STN EN 322: 1995: Dosky z dreva. Zisťovanie vlhkosti.
  • 8. STN EN 717-1: 2005: Dosky na báze dreva. Zisťovanie uvoľnenia formaldehydu. Časť 1: Emisia formaldehydu zisťovaná komorovou metódou.
  • 9. TOHMURA, S., INOUE, A., SAHARI, S.H. 2001. Influence of the melamine content in melamine-urea-formaldehyde resins on formaldehyde emission and cured resin structure. In J. Wood Sci. 2001, 47, p. 451- 457.
  • 10. ZHANG, S.F. et al. 2010. Study on properties of modified low molecular ratio urea-formaldehyde resins (I). In Advanced Material Research. 2010, 113-116, p. 2016-2010.
Typ dokumentu
Bibliografia
Identyfikatory
Identyfikator YADDA
bwmeta1.element.agro-170695d7-5ed3-449d-82a7-3ce72afec3dc
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.