Effect of thermal annealing in air on scintillation properties of LuAG and LuAG:Pr

Treść / Zawartość
Warianty tytułu
Języki publikacji
EN
Abstrakty
EN
Pure and Pr-activated Lu3Al5O12 (LuAG) crystals have been grown by the Czochralski method. In order to improve the scintillation properties, several samples have been annealed in air. Various annealing temperatures and periods of time have been tested to determine optimal conditions in the way of scintillation yield and energy resolution enhancement. The largest increase of yield of LuAG:Pr (17%), accompanied by a distinct decrease of resolution, has been observed after annealing at 1100°C for 48 h. On the contrary, in case of undoped LuAG no significant changes following thermal annealing have been noticed.
Wydawca

Czasopismo
Rocznik
Tom
11
Numer
1
Strony
138-142
Opis fizyczny
Daty
wydano
2013-01-01
online
2013-01-15
Twórcy
autor
  • Division of Optoelectronics, Institute of Physics, Nicolaus Copernicus University, Grudziadzka 5, 87-100, Torun, Poland, brykam@fizyka.umk.pl
  • Division of Optoelectronics, Institute of Physics, Nicolaus Copernicus University, Grudziadzka 5, 87-100, Torun, Poland
  • Division of Optoelectronics, Institute of Physics, Nicolaus Copernicus University, Grudziadzka 5, 87-100, Torun, Poland
autor
  • Institute of Multidisciplinary Research for Advanced Materials, Tokohu University, 2-1-1 Katahira, Aoba-ku, Sendai, Miyagi, 980-8577, Japan
  • Institute of Multidisciplinary Research for Advanced Materials, Tokohu University, 2-1-1 Katahira, Aoba-ku, Sendai, Miyagi, 980-8577, Japan
Bibliografia
  • [1] M. Nikl, H. Ogino, A. Krasnikov, A. Beitlerova, A. Yoshikawa, T. Fukuda, Phys. Status Solidi A 202, R4 (2005) http://dx.doi.org/10.1002/pssa.200409079[Crossref]
  • [2] J.A. Mares et al., Phys. Status Solidi C 4, 996 (2007) http://dx.doi.org/10.1002/pssc.200673858[Crossref]
  • [3] W. Drozdowski et al., IEEE T. Nucl. Sci. 55, 2420 (2008) http://dx.doi.org/10.1109/TNS.2008.2000845[Crossref]
  • [4] L. Swiderski et al., IEEE T. Nucl. Sci. 56, 934 (2009) http://dx.doi.org/10.1109/TNS.2009.2015590[Crossref]
  • [5] W. Drozdowski et al., IEEE T. Nucl. Sci. 56, 320 (2009) http://dx.doi.org/10.1109/TNS.2008.2011269[Crossref]
  • [6] H. Ogino, A. Yoshikawa, M. Nikl, K. Kamada, T. Fukuda, J. Cryst. Growth 292, 239 (2006) http://dx.doi.org/10.1016/j.jcrysgro.2006.04.021[Crossref]
  • [7] W. Drozdowski, K. Brylew, A. Chruscinska, K. Kamada, T. Yanagida, A. Yoshikawa, Opt. Mater. 34, 1975 (2012) http://dx.doi.org/10.1016/j.optmat.2011.11.024[Crossref]
  • [8] J.P. Zhong, H.B. Liang, Q. Su, J.Y. Zhou, J.Y. Wang, Trans. Nonferrous Met. Soc. China 19, 1628 (2009) http://dx.doi.org/10.1016/S1003-6326(09)60080-7[Crossref]
  • [9] J.P. Zhong, H.B. Liang, Q. Su, G.B. Zhang, P. Dorenbos, M.D. Birowosuto, J. Rare Earth. 25, 568 (2007) http://dx.doi.org/10.1016/S1002-0721(07)60564-X[Crossref]
  • [10] H. Feng et al., J. Appl. Phys. 103, 083109 (2008) http://dx.doi.org/10.1063/1.2906348[Crossref]
Typ dokumentu
Bibliografia
Identyfikatory
Identyfikator YADDA
bwmeta1.element.-psjd-doi-10_2478_s11534-012-0153-5
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.